Formaldehyde content in and VOC release from particleboards made of fibrous chips

Kowaluk G., Komorowicz M., Witczak M., Fuczek D.

Drewno : prace naukowe, doniesienia, komunikaty

2011

vol. 54, nr 185

81-88

The aim of this research was to investigate formaldehyde content in and volatile organic compounds release from particleboards produced from fibrous chips. The object of the tests were panels produced from fibrous chips of black locust Robinia Pseudoacacia L. and willow Salix Viminalis L., as well as from typical industrial particles. The results show that formaldehyde content in the panels produced from willow fibrous chips is similar to the content in the panels made of industrial particles. The concentration of total volatile organic compounds measured after 4 weeks of storage is significantly lower than the required by the existing regulations.

Celem badań było określenie zawartości formaldehydu w płytach wiórowych wytworzonych z wiórów włóknistych i emisji lotnych związków organicznych z tych płyt. Do badań użyto wiórów włóknistych z dwuletnich odrostów korzeniowych robinii (Robinia Pseudoacacia L.) oraz wierzby (Salix Viminalis L.), jak również typowych wiórów przemysłowych. Badania wykazały, iż zawartość formaldehydu w płytach wytworzonych z wierzby jest zbliżona do zawartości formaldehydu w płytach z wiórów przemysłowych. Stężenie lotnych związków organicznych, mierzone po 4 tygodniach przechowywania płyt, jest istotnie mniejsze niż obowiązujące ograniczenia.

Screw holding performance of panels made of fibrous chips

Kowaluk G., Fuczek D.

Drewno : prace naukowe, doniesienia, komunikaty

2010

vol. 53, nr 184

77-81

The aim of the research was to investigate the face screw withdrawal resistance of panels produced from fibrous chips of willow Salix Viminalis L. and black locust Robinia Pseudoacacia L. A series of laboratory 3-layer panels were produced from fibrous chips as well as from industrial particles. The results were compared to commercial industrial panel performance. The investigation shows that the panels from black locust have lower screw withdrawal resistance in comparison with the industrial panel. In the case of higher density willow panel the screw withdrawal resistance was better than that of the industrial panel.

Przedstawiono wyniki badań zdolności utrzymywania wkręta płyt wytworzonych z nietypowych cząstek drzewnych – wiórów włóknistych. W warunkach laboratoryjnych wykonano serię trójwarstwowych płyt o różnych gęstościach, z dwóch rodzajów wiórów włóknistych. Surowcem do produkcji wiórów włóknistych była wierzba Salix Viminalis L. oraz robinia Robinia Pseudoacacia L. Wykonano również płyty z wiórów przemysłowych. Wyniki zostały porównane z badaniami płyty przemysłowej. Badania wykazały niższą wytrzymałość na wyciąganie wkręta płyt wytworzonych z wiórów włóknistych z robinii, w porównaniu do płyty przemysłowej. Płyty o wyższej gęstości z wierzby charakteryzowała istotnie wyższa wytrzymałość na wyciąganie wkręta niż płyty komercyjne.