This paper presents a comparative study of the preparation and characterisation of Fe38.5Co38.5 Nb7 P15Cu1 alloy produced by mechanical alloying (MA) and rapid quenching (RQ) method. In order to obtain the starting mixture (SS) in the present study, we opted for the replacement of elemental Nb and P powders with ferroalloy powders of niobium and phosphorus. Benzene was used as a control agent of the process (PCA) for wet MA. The samples obtained (powders and ribbons) were characterised by X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), X-ray microanalysis (EDX), magnetic measurements M(H) and thermomagnetic measurements M(T). After 40 h of wet MA, the alloy was partially amorphous, and the ribbons obtained by RQ do not show an amorphous state. Also, the magnetic measurements show the influence of the method used on the magnetic properties.
Modern production of non-ferrous metals is imperfect due to the loss of rock mass and metal in the technological chain ore mining to metal production. Processing of zinc oxide and oxidized copper ores by hydrometallurgical, pyrometallurgical and flotation methods is associated with formation of dump cakes, clinkers and flotation tailings. Therefore, all these methods are characterized by a low coefficient of complex use of raw materials (for example, for the Waelz process this coefficient is not higher than 35%). To increase the degree of complex processing of oxide raw materials, it is necessary to change the attitude to raw materials and create industrial technologies based on new principles. The article presents theoretical and applied research results on complex processing of oxidized copper and zinc oxide ores based on the new attitude to raw materials and new effective technologies allowing us to increase significantly the level of raw materials’ complex processing. Theoretical regularities, features and optimal technological parameters of new methods of complex processing of oxide, zinc and oxidized copper ores were found based on the ideology of a universal technological raw material and the simultaneous production of several products in one furnace unit.
W publikacji przeanalizowane zostały najważniejsze parametry fizykochemiczne kilku wybranych węgli kamiennych w kontekście wykorzystania ich jako reduktory w procesie wytopu żelazokrzemu. Z przedstawionych w publikacji węgli przydatnych jako reduktory, węgiel z kopalni Wujek był stosowany w przeszłości (wyczerpane zasoby), z kopalń Staszic i Wieczorek jest stosowany obecnie, a węgle z kopalń: Bogdanka, Piast i Ziemowit charakteryzowane są jako potencjalnie możliwe do zastosowania w postaci mieszanek z innymi węglami. W pracy porównano parametry węgli uzyskane: w analizie technicznej, elementarnej, przy badaniu składu popiołu, z pomiaru refleksyjności witrynitu oraz reakcyjności wobec SiO i CO2.
EN
In the publication were analyzed the most important physicochemical parameters selected a few bituminous coals in the context of their use as reductors in the process of smelting ferrosilicon. From the presented in the publication coals useful as reductors, the Wujek coal has been used in the past (exhausted resources), Staszic and Wieczorek coals are currently used, while Bogdanka, Piast and Ziemowit coals are characterized as potentially usable in blends with other coals. At work were compared parameters of coals obtained in: technical and elemental analysis, examination of ash composition, vitrinite reflectance measurement and reactivity of selected coal towards SiO and CO2.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The article presents the requirements regarding the carbon reducers used in the processes of melting ferroalloys by means of electrothermal methods. The quality and the constancy of the carbon reducers’ properties have a significant impact on the course of electrothermal processes of melting ferroalloys. The influence is particularly significant in the commonly used continuous processes. The paper describes the properties of such carbon reducers as: metallurgical coke, hard coal, semi-coke, petroleum coke and charcoal. The paper also presents the influence of the reducers’ chemical composition and granulation on the process of melting ferroalloys in electric furnaces. The following properties of the above mentioned reducers were investigated: electric resistance, reactivity and durability.
PL
W artykule przedstawiono wymagania odnośnie własności reduktorów węglowych stosowanych w procesach wytapiania żelazostopów metodami elektrotermicznymi. Jakość i niezmienność własności reduktorów węglowych wywiera istotny wpływ na przebieg procesów elektrotermicznego wytapiania żelazostopów zwłaszcza w powszechnie obecnie stosowanych procesach ciągłych. W pracy omówiono własności takich reduktorów węglowych jak: koks metalurgiczny, węgiel kamienny, półkoks, koks naftowy i węgiel drzewny. Omówiono wpływ składu chemicznego i granulacji reduktorów na przebieg procesów wytapiania żelazostopów w piecach elektrycznych. Zbadano takie własności wymienionych powyżej reduktorów węglowych jak rezystancja elektryczna, reakcyjność i wytrzymałość.
5
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przeprowadzono walidację metod analizy chemicznej żelazomanganu, żelazokrzemu i żelazochromu. Walidację przeprowadzono zapomocą certyfikowanych materiałów odniesienia. Stwierdzono bardzo dobrą zgodność otrzymanych wyników z wartościami certyfikowanymi. Wyznaczono następujące parametry statystyczne: odchylenie standardowe powtarzalności, odchylenie standardowe precyzji pośredniej, niepewność pomiaru złożoną standardową, niepewność rozszerzoną. W wyniku realizacji pracy stosowane w Laboratorium metody analizy żelazostopów spełniają wymagania normy PN-ISO/IEC 17026 oraz wymagania odbiorców.
EN
Validation of methods for chemical analysis of ferromanganese, ferrosilicon and ferrochromium was carried out. This validation was performed using certified reference materials. Very good conformity of the obtained results to the certified values was found out. The following statistical parameters were determined: standard deviation for repeatability, standard deviation for intermediate precision, combined standard uncertainty and extended uncertainty of measurement. As a result of this work, the methods for analysis of ferroalloys used in the Laboratory comply with requirements of PN-ISO/IEC 17025 and requirements of the users.
6
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy przedstawiono wyniki badań odporności korozyjnej stopu na osnowie fazy międzymetalicznej FeAl w środowisku korozyjnym ciekłego HCl i H2SO4. Określono skłonność materiału do aktywacji powierzchni w czasie oddziaływań korozyjnych. Dokonano próbę określenia szybkości procesów korozyjnych oraz odporności na korozję naprężeniową. Zwrócono również uwagę na przebieg korozji wżerowej. Badania zakończono na ocenie stanu powierzchni po procesie korozyjnym.
EN
The article presents the results of research conducted to determine the alloy corrosion resistance on FeAl boundary in a corrosive medium of HCl and H2SO4 solutions. The material susceptibility to surface activation in a corrosive medium was determined. A test was conducted to determine the influence of time on the corrosion rate and on the stress corrosion resistance. Pitting corrosion was also observed. The research concluded on the evaluation of the surface state after the corrosion process.
The deformation process of composite wire from ingots was under study. Stability of deformation of composite materials with the insertion filled with powder-like various materials (in that number fragile), is shown. Differences of nature and mechanical properties of filler materials composite insertion and steel matrix does not cause of to the non-uniformity of layers' deformation at composite goods processing.
PL
Proces odkształcenia drutu kompozytowego, poczynając od wlewków, był przedmiotem niniejszej pracy. Wykazano stabilność odkształcenia materiałów kompozytowych wypełnionych różnymi materiałami (również kruchymi) w formie proszkowej. Różnice w charakterze odkształcenia i własnościach mechanicznych kompozytowych wypełniaczy i osnowy stalowej, nie powodują niejednorodności odkształcenia warstw przy wytwarzaniu wyrobów kompozytowych.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W artykule usystematyzowano wiadomości o cynkowaniu zanurzeniowym. Przedstawiono chronologicznie rozwój procesu zabezpieczania przed korozją stopów żelaza w ciekłym cynku. W formie skróconej opisano metody cynkowania. Przedstawiono strukturę powłok cynkowych otrzymanych na podłożu żelaza w tradycyjnym procesie cynkowania oraz w procesie cynkowania wysokotemperaturowego. Podano przykłady struktury powłok otrzymanych na różnych gatunkach stali jak również na wysokowęgłowych, odlewniczych stopach żelaza, co pozwoliło na zobrazowanie wpływu składu chemicznego i fazowego podłoża na budowę powłoki. Wskazano znaczący wpływ powłok cynkowych na poprawę odporności korozyjnej stopów żelaza pracujących w agresywnym środowisku. Omówiono rozwój procesu cynkowania na przełomie ostatnich kilkudziesięciu lat, oraz przedstawiono perspektywy dalszego rozwoju.
EN
The paper systematizes the knowledge about dip galvanizing. It presents development of the process of protecting ferroalloys against corrosion in liquid zinc and shortly describes galvanizing methods. Also, the structure has been presented of zinc coatings obtained on an iron substrate in a conventional galvanizing process as well as in high-temperature galvanizing. Examples have been provided of the structure of coatings obtained on different steel grades and on high-carbon, casting ferroalloys, which has enabled the illustration of the influence of the chemical and phase compositions on the coating's structure. The paper also emphasizes the influence of zinc coatings on enhancement of the corrosion resistance of ferroalloys working in an aggressive environment. Development of the galvanizing process has been discussed throughout a few dozen years and the prospects for its further development have been presented.
9
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W artykule przedstawiono wyniki eksperymentów wprowadzania dodatków stopowych metodą pneumatyczną przy zastosowaniu lancy nie zanurzonej. Prowadzone eksperymenty mają w założeniu wyjaśnić niektóre aspekty dynamiki strumienia dwufazowego, mającej zasadniczy wpływ na wyniki procesu. Przeanalizowano głównie wpływ wielkości ziarna wdmuchiwanego żelazostopu na efektywność przyswajania chromu przez ciekłe żeliwo. Zastosowania lancy nie zanurzonej wymaga specyfika pieców indukcyjnych.
EN
This paper presents results of pneumatic injection of alloy additions using non-immersed lance. The experiments should explain some aspects of diphase stream dynamics, which fundamentally influences on the results of the process. Influence of injected ferroalloys grain size for increasing of chromium contents was analyzed. Experiments were concern for a case of injection into an induction furnace with non-submerged lance (above the liquid) powder injection into liquid cast iron.