Wyniki wyszukiwania - BazTech

1

Study of the Dielectric Properties and Conductivity of Double Coated Glass Fibre Felt Composites

Liu Yuanjun, Wang Caixia, Ma Yiping, Liu Yanyan, Wu Haiying, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2021

|

Vol. 29, no. 4 (148)

75--80

EN

Graphite/talcum powder double-coated glass fibre felt composites were prepared using glass fibre felt as the base material, graphite as the surface absorbing agent, talcum powder as the underlying absorbing agent, epoxy resin E44 as the adhesive and low molecular 650 polyamide as the curing agent. The influences of the surface graphite content and underlying talcum powder content on the dielectric properties and conductivity of glass fibre felt composites were the main focus of the investigation. Results showed that when the frequency is less than 103 Hz, the values of the real and imaginary parts of the dielectric constant for double-coated glass fibre felt composites are largest when the surface graphite content is 50%. When the frequency is larger than 106 Hz, the value of the real part of the conductivity is largest when the graphite contents are 40% and 50%. When the frequency is less than 104Hz, the real part of the dielectric constant of the glass fiber mat composites is the largest when the talc content is 40%, and when talc content is 60%, the imaginary part of dielectric constant of glass fiber mat composites is the largest. The maximum loss tangent value for the composites occurs when the talcum powder content is 40%. When the frequency is larger, the value of the real part of the conductivity increases gradually.

PL

W pracy przygotowano podwójnie powlekane kompozyty filcu z włókna szklanego w postaci grafit/talk. Użyto filcu z włókna szklanego jako materiału bazowego, grafitu jako powierzchniowego środka pochłaniającego, talku jako podstawowego środka pochłaniającego, żywicy epoksydowej E44 jako kleju i poliamidu 650 o niskiej masie cząsteczkowej jako środek utwardzającego. Głównym przedmiotem badań było określenie wpływu zawartości grafitu powierzchniowego oraz zawartości proszku talku na właściwości dielektryczne i przewodność kompozytów z filcu z włókna szklanego. Wyniki wykazały, że gdy częstotliwość jest mniejsza niż 103 Hz, wartości części rzeczywistej i urojonej stałej dielektrycznej dla podwójnie powlekanych kompozytów z filcu z włókna szklanego są największe, gdy zawartość grafitu powierzchniowego wynosi 50%. Gdy częstotliwość jest większa niż 106 Hz, wartość rzeczywistej części przewodnictwa jest największa, gdy zawartość grafitu wynosi 40% i 50%. Maksymalna wartość tangensa strat dla kompozytów występuje, gdy zawartość talku wynosi 40%. Gdy częstotliwość jest większa, wartość rzeczywistej części przewodnictwa stopniowo wzrasta.

2

Discussion on the Tensile and Bending Properties of PAN-based Pre-oxidised Fibre Felt Composite Materials

Liu Yuanjun, Bao Wenli, Zhao Xiaoming

Fibres & Textiles in Eastern Europe

|

2020

|

Vol. 28, no. 2 (140)

57--60

EN

The impact of the mass percentage of PAN-based pre-oxidised fibre felt in a composite material and of the curing temperature on the composite material’s mechanical properties were studied in order to optimise the preparation method of epoxy resin composite material. The results showed that when the dosage of PAN-based pre-oxidised fibre felt was 15% of the mass of epoxy resin and the curing temperature was 170 °C, the tensile and bending properties of the composite materials produced were the best. This study has addressed the absence of reports on this type of composite material, and is expected to lead to the development of applications for this new type of composite material.

PL

W celu zoptymalizowania metody przygotowania materiału kompozytowego z żywicy epoksydowej zbadano wpływ procentu masy wstępnie utlenionego filcu z włókien PAN w materiale kompozytowym i temperatury utwardzania na właściwości mechaniczne materiału kompozytowego. Wyniki pokazały, że najlepsze właściwości rozciągania i zginania wytwarzanych materiałów kompozytowych otrzymano dla 15% ilość wstępnie utlenionego filcu z włókien PAN w stosunku do masy żywicy epoksydowej, a optymalna temperatura utwardzania wynosiła 170 °C. Autorzy pracy oczekują, że przeprowadzone badanie doprowadzi w przyszłości do opracowania aplikacji dla nowego rodzaju materiału kompozytowego.

3

Influence of Ultraviolet Irradiation and Protease on Scale Structure of Alpaca Wool Fibers

Wang Hua, Farha Farial Islam, Memon Hafeezullah

Autex Research Journal

|

2020

|

Vol. 20, no. 4

476--483

EN

The present research aimed to explore the influence of different felt-proofing methods on alpaca fibers’ scale structure. Dyed alpaca fibers were exposed to a particular wavelength of ultraviolet (UV) light for different periods and treated with protease to analyze the felt property and compare with untreated fibers. Experimental results have shown that alpaca fibers have better shrinkage resistance and dyeability after being exposed to UV light, whereas no recognizable change was obtained on the surface of alpaca fibers’ scale structure by scanning electron microscopy (SEM). In contrary, enzyme-treated alpaca fibers revealed improved dye rate and resistance to shrinkage. Especially, damaged scales on many areas of fiber surface were appeared by SEM, which indicates that UV may have a positive effect on enzyme treatment by damaging alpaca fibers’ surface structure and promoting the amount of protease going into the fibers’ inner layers. Therefore, eventually a better shrinkage resistance was obtained.

4

Kondycjonowanie filców prasowych z wykorzystaniem strumienicy parowej

Klepaczka A.

Przegląd Papierniczy

|

2007

|

R. 63, nr 6

331-333

5

Bitumen felt roofing materials: design, detal construction, disposal and recycling

Mikulasova D., Mikulas M.

Zeszyty Naukowe Politechniki Rzeszowskiej. Budownictwo i Inżynieria Środowiska

|

2000

|

z. 32[180], cz.1

375-380

EN

After their service life, building materials become a heavy burden that the building industry and companies dealing with disposal of construction waste must handle. From the point of view of building companies it can be represented by a closed cycle: design - implementation - exploitation - disposal. The presented paper concerns briefly all these stages.