The investigations of Fe-Al phases formation arround SHS reaction in isothermal conditions

Pocheć E., Jóźwiak S., Karczewski K., Bojar Z.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

479-482

The composites of magnesium hydride and intermetallic based hydrides: MgH2 + X wt. % FeTi and MgH2 + X wt. % LaNi5 (X = 10, 30 and 50) were synthesized by Controlled Reactive Milling (CRM) in a magneto-mill, under hydrogen atmosphere. The phase structure and morphology of obtained powders were analyzed using XRD and SEM techniques, respectively. Their thermal behavior was investigated by Differential Scanning Calorimetry (DSC) and Temperature Programmed Desorption (TPD). It is found that the DSC hydrogen desorption peak temperature as well as the activation energy of decomposition process of the MgH2 constituent in composites decreases linearly with increasing volume fraction of FeTi and LaNi5. It is demonstrated that the hydrogen desorption in the metal hydride- -intermetallic alloy based hydride composites involves two steps: first, the lower temperature hydride decomposes to intermetallic alloy and H2 and in a subsequent step, most likely, this counterpart catalyses the decomposition of high temperature hydride. The catalytic element introduced into the system from decomposing a simple intermetallic hydride, does not reduce dramatically the total capacity of the composite system.

Kompozyty funkcjonalne na bazie wodorku magnezu i wodorków intermetalicznych: MgH2 + X% mas. FeTi oraz MgH2 + X% mas. LaNi5 (gdzie X = 10, 30 i 50) syntetyzowano przez Kontrolowane Mielenie Reaktywne (KMR) w magnetycznym młynku kulowym. Morfologię materiału zarówno przed procesem mielenia (rys. 1), jak i po mieleniu (rys. 2, 6) badano za pomocą mikroskopii elektronowej skaningowej SEM. Tworzenie się niestabilnych wodorków metalicznych w trakcie procesu mielenia monitorowano, badając spadek ciśnienia w cylindrach młynka (rys. 4). Strukturę fazową uzyskanych kompozytów (rys. 3, 7) określano, wykorzystując technikę XRD. Wyniki pomiarów wielkości ziarna składników kompozytu MgH2 + LaNi5 przedstawiono w tabeli 1. Właściwości termiczne badano techniką DSC oraz TPD. Stwierdzono, iż temperatura piku dekompozycji oraz energia aktywacji procesu dekompozycji MgH2, jako składnika kompozytu, zmniejsza się liniowo wraz ze wzrostem udziału fazy FeTi (rys. 5, 6) oraz LaNi5 (rys. 8, 9). Przedstawiono, iż desorbcja wodoru w kompozytach typu wodorek metalu- wodorek fazy międzymetalicznej przebiega w dwóch etapach: w pierwszym wodorek niskotemperaturowy ulega dekompozycji do fazy międzymetalicznej i wodoru, a w następnym etapie ten składnik katalizuje proces dekompozycji wodorku wysokotemperaturowego. Wprowadzony tą metodą element katalityczny nie obniża w sposób drastyczny całkowitej pojemności układu.

Detonation deposited Fe-Al coatings. Part I Morphology of Ni(Al) and Cr(Ni) transition layers and coatings of Fe-Al type sprayed onto carbon steel substrate

Pawłowski A., Senderowski C., Bojar Z., Faryna M.

Archives of Metallurgy and Materials

2010

Vol. 55, iss. 4

1061-1071

The microstructure of transition layers of Ni(Al) - pure Ni with Al and NiAl particles as well as Cr(Ni) - pure Cr in the Ni matrix, occurred between the coating of Fe-Al type intermetallic phases and the 045 carbon steel substrate was analysed in the present work. The investigations were aimed at the adherence of transition layers and the outer coating deposited with the detonation-gas spraying. The structure was examined using the methods of scanning (SEM) and transmission electron (TEM) microscopies as well as the analysis of chemical composition in microareas (EDS). Silica grains at the boundary of the substrate and the layer of Ni(Al), aluminium oxide at the boundary and inside the Ni(Al) layers, an Al based AlNiOx phase, columnar crystals at the boundary of the coating of Fe-Al type phases and an adjacent Cr(Ni) layer were observed. The results were discussed in reference to earlier examinations of bending strength considering cracking and delamination of the coating off the substrate. They were then compared with the state of the boundary between the coating and the steel substrate analysed in former works. It seems, that the substrate boundary free from silica inclusions and the prevention of the formation of aluminium oxides at the boundary of transition layers and the substrate should improve the adherence of the whole multi layer and the coating.

W pracy poddano analizie mikrostrukturę warstw pośrednich: Ni(Al) - czystego niklu z cząstkami Al i faz NiAl oraz warstwy Cr(Ni) - chromu w osnowie Ni, występujących pomiędzy powłoką faz międzymetalicznych typu Fe-Al i podłożem ze stali węglowej 045. Badania wykonano z punktu widzenia przyczyn przyczepności warstw pośrednich i powłoki zewnętrznej, naniesionych przez natryskiwanie detonacyjno-gazowe DGS. Analizę struktury przeprowadzono na podstawie badań metodą skaningowej (SEM) i transmisyjnej mikroskopii (TEM) elektronowej oraz analizy składu chemicznego w mikroobszarach (EDS). Stwierdzono wystąpienie ziaren krzemionki na granicy podłoża z warstwą Ni(Al), obecności ziaren tlenku glinu na granicy i wewnątrz warstw Ni(Al) oraz fazy na bazie glinu AlNiOx i kryształów kolumnowych na granicy powłoki faz typu Fe-Al oraz warstwy Cr(Ni) chromu do niej przylegającej. Wyniki badań mikrostruktury dyskutowano w odniesieniu do rezultatów wcześniejszych pomiarów wytrzymałości na zginanie w aspekcie pękania powłoki oraz delaminacji podwarstwy od podłoża. Porównano je także do stanu granicy powłoki z podłożem stalowym dokonanych w poprzednich pracach. Jest prawdopodobne, iż granice podłoża pozbawione wtrąceń krzemionki oraz zapobieżenie tworzeniu tlenków glinu na granicy warstw pośrednich i podłoża powinno poprawić przyczepność całej multiwarstwy i powłoki.