Effect of Iron Phases Crystallization on the Durability of the Bimetallic Connection Between Ring Inserts and the Piston Casting

Szucki Michał, Piątkowski Jarosław, Czerepak M.

Archives of Foundry Engineering

2023

Vol. 23, iss. 2

112--118

The article presents the most important causes of the unstable connection between cast iron ring inserts and the silumin casting of an engine piston. It is shown that manufacturing defects are mainly related to the alfin processing of inserts in Al-Si alloy (the so-called AS9 alloy). Exceeding the permissible iron content in AS9 alloy causes the crystallization of brittle -Al5FeSi phases. Their unfavorable morphology and large size are the main reasons for the weakening of the diffusion connection between the inserts and the piston, causing an unacceptable proportion of defective products. The study presented in this work was conducted under industrial conditions on a population of 10.000 pistons. Quality control data, production parameters, as well as the micro- and macro-structures of the cast iron inserts, and the interface area between the inserts and the silumin piston, were analyzed. Material and technological solutions have been proposed to reduce the occurrence of casting defects at the insert-piston joint. This includes the introduction of so-called "morphological correctors" of the -Al5FeSi phases, reducing the possibility of gaseous impurities in the AS9 alloy and optimizing the temperature of the alfin alloy.

Effect of non-ideal phase separation on a multi-unit crystallization process performance

Dudczak J.

Inżynieria Chemiczna i Procesowa

2003

T. 24, z. 3

379-390

A perfect separation of the solid phase from its equilibrium liquid phase is usually assumed in the papers on crystallization system synthesis. In practice, a considerable amount of solution may accompany the crystalline phase separated. In multi-unit crystallization systems with recycle streams, the imperfect phase separation affects the flow rates of all process streams and may even lead to the process infeasibility. The influence of separation efficiency in the process units on the performance of a three-stage crystallization process with one solid and one liquid recycle has been examined.

Praktycznie we wszystkich pracach poświęconych problemowi syntezy systemów krystalizacyjnych przyjmuje się założenie, że faza stała oddzielana jest od roztworu macierzystego w sposób idealny. W rzeczywistości, wydzielone kryształy niosą ze sobą znaczące ilości roztworu. W przypadku systemów krystalizacyjnych zbudowanych z kilku bloków krystalizacyjnych połączonych strumieniami zwrotnymi, niedoskonały rozdział faz wpływa na natężenia przepływu strumieni i może w krańcowych przypadkach prowadzić do nierealizowalności procesu. W pracy przestudiowano wpływ sprawności rozdziału faz w blokach krystalizacyjnych na działanie trójblokowego systemu krystalizacyjnego z jednym stałym i jednym ciekłym strumieniem recyrkulacyjnym.