Effect of Heat Treatment Conditions on the Morphology of α Phase and Mechanical Properties In Ti-10V-2Fe-3Al Titanium Alloy

Bogucki R., Mosór K., Nykiel M.

Archives of Metallurgy and Materials

2014

Vol. 59, iss. 4

1269--1273

The influence of heat treatment on the microstructure and mechanical properties was studied in the Ti-10V-2Fe-3Al titanium alloy for two heat treatment schemes (α + β) and β + (β + α), which resulted in different morphologies of the α phase. Scheme I resulted in the α-phase of globular morphology, whose volume fraction did not change much during annealing. Scheme II led to obtaining a needle-like α-phase, whose amount increased together with heating time. The phenomenon of stress-induced martensitic transformation was observed in the material with needle-like morphology annealed for 15 and 30 min. Longer times of annealing effected in the decay of that transformation, provided the volume fraction of α-phase exceeded 50%.

W pracy przedstawiono wyniki badan wpływu obróbki cieplnej na mikrostrukture i własciwosci mechaniczne stopu tytanu Ti-10V-2Fe-3Al, które analizowano w dwóch schematach obróbki cieplnej (α + β) oraz β + (β + α). Uzyskane mikrostruktury charakteryzowały sie rózna morfologia fazy α. W schemacie I obserwowano globularna faze α, której udział objetosciowy nie ulegał znacznym zmianom w funkcji czasu wygrzewania. W schemacie II faza α miała kształt iglasty i jej udział objetosciowy wzrastał z czasem wygrzewania. W próbkach o iglastej morfologii fazy α dla czasów wygrzewania 15 min. i 30 min. zaobserwowano wystepowanie zjawiska przemiany martenzytycznej indukowanej naprezeniem. Zastosowanie dłuzszych czasów wygrzewania ujawniło zanik dodatkowej.