Damage characterization of aluminum 2024 thin sheet for different stress triaxialities

Majzoobi G. H., Kashfi M., Bonora N., Iannitti G., Ruggiero A., Khademi E.

Archives of Civil and Mechanical Engineering

2018

Vol. 18, no. 3

702--712

Due to its attractive mechanical properties, aluminum 2024 is widely used in aircraft manufacturing industries, especially as fiber metal laminates, such as GLARE. In the present work, a series of experiments for different stress triaxialities are used to study the ductile damage of Al 2024 considering continuum damage mechanics (CDM). Stress triaxiality is produced using notched specimens. The main objective of the present study is to predict the local equivalent plastic strain to fracture and introducing a relation which describes the effect of stress triaxiality factor (TF) on it in the medium range of stress triaxiality. Hence, a nonlinear damage model is utilized for Al 2024 and its parameters are determined by an experimental/numerical/optimization procedure using tensile test on plain specimens. The experiments showed that for large notch specimens (Al-NL) and medium notch samples (Al-NM) fracture started from the center of the notch root of the specimens, whereas for small notched specimens (Al-NS) the failure initiated from the notch root surface. Finite element simulations are performed using the presented nonlinear damage model and are compared with the experimental data. Results show that the proposed damage model can predict the damage evolution for different stress triaxialities.

Elaboration of ductile fracture criteria based on punching forgeability test

Lisiecki Ł., Skubisz P.

Computer Methods in Materials Science

2016

Vol. 16, No. 2

70--75

A new approach of forgeability test, based on compression-punching state of stress was proposed. Comparison of the results of the presented research methodology with standard compression test is presented. The new forgeability test is designed to generate controllable failure location for good plasticity materials, which high the level of stresses accompanying the fracture. Different shape of tools and specimens tend to show the effect of geometry on the areas of concentrations of tensile and shear stresses, which play important role in formation of cracks. The paper presents the methodology based on laboratory tests of compression and pseudo-punching performed on laboratory rig with 5MN hydraulic press and numerical FEM simulation of the tests on commercial code with introduction of the elaborated fracture criteria.

W artykule przedstawiono nową koncepcję laboratoryjnego testu ściskania. Wyniki standardowego testu porównano z rezultatami osiągniętymi podczas badań z użyciem narzędzi wykonujących wgłębienia w próbkach. Nowa propozycja wyznaczania odkształcalności granicznej jest dedykowana materiałom o dobrej plastyczności, gdzie pęknięcia są powodowane osiągnięciem wysokiego poziomu naprężeń. Zmiana kształtu odkształcanych próbek oraz narzędzi wywołały wymaganą koncentrację naprężeń rozciągających oraz stycznych sprzyjającą powstawaniu wad. Badania stanowią połączenie testów laboratoryjnych z wykorzy¬staniem prasy hydraulicznej o maksymalnej sile nacisku 5MN oraz symulacji numerycznej MLS.