Assessment of Evaporator Tubes Corrosion in Low-Emission Steam Boilers

Łabanowski J., Topolska S., Ćwiek J.

Advances in Materials Science

2008

Vol. 8, nr 4(18)

14-21

Degradation examinations of outer surface of low-emission steam boiler evaporator tubes are presented in the paper. Metallographic evaluation of scale morphology, its micro sites chemical composition analysis and distribution of elements on cross sections have been performed. Water-wall tubes were exposed in steam boiler for up to two years period. Common tubes made of 16Mo3 steel suffered sulfide and molten salts corrosions. Thermal sprayed tubes with the single layer of 70%Ni 30%Cr alloy show better corrosion resistance, but become also susceptible to sulfide corrosion due to presence of internal voids and cracks. Double layer Al2O3/Ni-30Cr coatings withstand corrosion attack for more than one year operation, then failed due to internal heterogeneity and cracks generation.

High temperature corrosion of evaporator tubes in low-emission steam boilers

Łabanowski J., Ćwiek J., Topolska S.

Advances in Materials Science

2007

Vol. 7, nr 2(12)

26-31

Degradation examinations of outer surface of evaporator tubes of the OP-230 low-emission steam boiler are presented in the paper. Metallographic evaluation of scale morphology, its micro sites chemical composition analysis and linear distribution of elements on cross sections have been performed. Evaluation of chemical compounds existed in deposited layer was also in-vestigated. Sulfide corrosion bas been aimed as the main reason of premature thinning of evaporator tube walls at lower levels of combustion chamber, and molten salt corrosion at highest levels.