Eutectoid Reaction Ar1 of Cast Iron GJS-400-15 in Isothermal Conditions

Szykowny T., Romanowski Ł., Giętka T.

Archives of Foundry Engineering

2014

Vol. 14, iss. 3

93--98

This scientific paper presents the research on influence of austenitizing temperature on kinetics and evolution of the spheroidal plain cast iron during eutectoid reaction in isothermal conditions. The cast iron has been austenitized in temperatures of 900, 960 or 1020°C. Therewere two temperature values of isothermal holding taken into consideration: 760 or 820°C. The order of creation of reaction products and their morphology have been analyzed. The particular attention has been paid to the initial stage of transformation. The qualitative research has been executed using the transmission electron microscope (TEM), as well as quantitative research (LM). The influence of austenitizing temperature has also been determined on transformation kinetics and structural composition. It was found that the increase of austenitizing temperature is conductive to the initial release of structures by metastable system. A reduction of time was observed of the initial stage of transformation at temperature close to Ar12 with its simultaneous elongation at temperature close to Ar11, with an increase of austenitizing temperature. The dependences obtained by the metallographic method confirm the prior results of dilatometric research of eutectoid reaction.

Electron microscopy studies of the eutectoid reaction in ZrO2-MgO ceramics.

Czeppe T., Zięba P., Pawłowski A.

Inżynieria Materiałowa

2001

R. XXII, nr 4

267-269

The early stages of the eutectoid decomposition of the partially stabilized ZrO2, containing 8.0 and 11.0 mol.% MgO were investigated using analytical electron microscopy. The initiation of the reaction was preceeded by the movement of the original grain boundaries. Then the formation of cellular microstructure of the MgO rods in monoclinic ZrO2 phase occurs. However, the crystallographic orientation of the monoclinic phase is the same as that of grain from which the growth originally started. Sharp decrease of the MgO content across the reaction front suggests that the interface diffusion is the main controlling factor of the eutectoid decomposition.

Analityczna mikroskopia elektronowa została wykorzystana do badań wczesnego stadium przemiany eutektoidalnej w częściowo stabilizowanym ZrO2 zawierającym 8 i 11 mol.% MgO. Stwierdzono, że rozpoczęcie przemiany poprzedzone jest migracją pierwotnych granic ziaren. Następnie na migrującej granicy tworzy się komórkowa struktura złożona z MgO o kształcie prętów, oraz roztworu stałego stanowiącego ZrO2 o symetrii monoklinicznej, czyli takiej samej jak orientacja ziarna, z którego wzrost komórkowy się rozpoczął. Gwałtowna zmiana zawartości MgO na froncie reakcji wskazuje, że czynnikiem kontrolującym wzrost eutektoidalny jest dyfuzja na migrującej granicy ziarna.