Microstructure and texture of ECAP processed AlCu4SiMn and AlCu5AgMgZr alloys

Kuśnierz J., Mathon M-H., Dutkiewicz J., Baudin T., Jasieński Z., Penelle R.

Archives of Metallurgy and Materials

2005

Vol. 50, iss. 2

367-377

The superplastic flow occurring in materials of ultra-fine grained structure allows to reducing the drawing temperature. It may be profitable when applied to aluminium alloys like AlcuZr, subjected to superplastic forming. The texture, based on neutron diffraction pole figure measurements of two alloys i.e. AlCu4SiMn and AlCu5AgMgZr during the equalchannel angular pressing (ECAP) is discussed in the paper. Structure observations by means of optical microscopy, transmission electron microscopy (TEM) and electron back scattered diffraction (EBSD) technique for OIMTM and local texture measurements have been applied to obtain a precise and detailed description of structure and orientation changes.

Wytworzenie ultra-drobnokrystalicznej mikrostruktury pozwala na obnizenie temperatury płyniecia nadplastycznego. Wykorzystanie tego zjawiska może przyczynić się do uzyskania wymiernych korzyści podczas kształtowania poprzez płynięcie nadplastyczne elementów ze stopów Al takich jak AlCuZr.W pracy przedstawiono wyniki pomiarów tekstury stopów AlCu4SiMn i AlCu5AgMgZr wyciskanych w kanale kątowym (metoda ECAP). Wykorzystano obserwacje struktury za pomocą mikroskopu optycznego, elektronowego (TEM) i skaningowego w zakresie analizy obrazu (OIMTM) oraz tekstury lokajnej (EBSD) w celu szczegółowego opisu struktury i zmian orientacji.

Analysis of texture formation homogeneity processes during equal-channel angular pressing

Zhilina M. V., Bonarski J., Scherbakov A. V., Alexandrov I. V., Makarychev K.

Archives of Metallurgy and Materials

2005

Vol. 50, iss. 2

479-485

Experimental investigations of texture formation processes were conducted in selected zones of cross section of bulk billets, subjected to equal channel angular (ECA) pressing. Pure Cu and Ti with fcc and hcp lattices, respectively were chosen as investigated materials. There was considered a case of 12 ECA pressing passes (route Bc). The angle of channels’ intersection during ECA pressing was 90°. ECA pressing rate was 6 mm/s. In the case of Cu deformation was carried out at room temperature and in the case of Ti it was elevated to 450°C. Experimental tests were carried out by means of X-ray diffraction technique. For both investigated materials, the incomplete back-reflection pole figures in selected areas of prepared samples were registered. The texture functions calculated on the basis of such incomplete pole figures enabled to calculate both the complete and inverse pole figures, and to perform the qualitative and quantitative texture analysis. Conclusions on texture homogeneity during ECA pressing of bulk Cu and Ti ingots were drawn.

Eksperymentalne badania procesu tworzenia tekstury przeprowadzono w wybranych obszarach przekroju poprzecznego litych próbek poddanych wyciskaniu w kanale kątowym (ECA) o przekroju kwadratowym. Materiałami wybranymi do badań były Cu i Ti o strukturze odpowiednio fcc i hcp. Rozważano przypadek 12 przepustów wyciskania (droga Bc), przy czym kąt zakrzywienia kanału wynosił 90°. Szybkość wyciskania wynosiła 6 mm/s. W przypadky Cu deformacje przeprowadzono w temperaturze pokojowej, podczas gdy Ti w 450°C. Badania tekstury uzyskanych materiałów przeprowadzono metodą dyfrakcji rentgenowskiej. Wyznaczono niekompletne figury biegunowe wybranych obszarów uzyskanych próbek. Obliczone na podstawie niekompletnych figur biegunowych funkcje tekstury umożliwiły obliczenie kompletnych i odwrotnych figur biegunowych oraz pozwoliły na jakościową i ilościowa analizę tekstury. Wyciągnieto wnioski o jednorodności tekstury podczas wyciskania ECA sztabek Cu i Ti.