Electric conductivity in epoxy matrix with nanoparticles

Włodarska M., Partyka M., Bąk G. W., Mossety-Leszczak B., Galina H., Florjańczyk Z., Łokaj K.

Scientific Bulletin. Physics / Lodz University of Technology

2012

Vol. 33

107-112

This work presents results of DC conductivity measurements obtained for epoxy matrices with different concentration of the nanofiller. In the first step, optimal curing conditions were determined - which turned out to be similar to those established for a plain epoxy matrix. In order to confirm stability of the matrix, measurements of the current-time dependency were made, which clearly show both the chemical and electric stabilization at the given temperature. All the obtained materials appeared to be good insulators with high activation energy. It was observed that the activation energy decreases slightly with increasing concentration of the nanofiller.

W pracy zaprezentowano wyniki pomiarów przewodnictwa stałoprądowego uzyskane dla matryc epoksydowych z różnym stężeniem nanonapełniacza. Początkowo ustalono optymalne warunki sieciowania, które były podobne do tych ustalonych dla samej matrycy. W celu potwierdzenia stabilności matrycy przeprowadzono pomiary zależności prądu od czasu, które dobrze obrazują zarówno stabilizację chemiczną, jak i elektryczną w danej temperaturze. Wszystkie uzyskane materiały okazały się dobrymi izolatorami z dużą energią aktywacji. Zauważono, że wraz ze wzrostem stężenia nanocząstek energia aktywacji nieznacznie maleje.

Conductivity in cured epoxy resins containing a biphenyl unit

Włodarska M., Izdebski M., Bąk G. W., Mossety-Leszczak B., Galina H.

Scientific Bulletin. Physics / Lodz University of Technology

2010

Vol. 31

87-95

Conductivity of two epoxy matrices based on the same monomer was compared. The epoxy monomer had symmetric structure and contained the biphenyl group which induced additional phase transitions in the pure material. Two amines responsible for different curing mechanisms were used to prepare the matrices. Wide ohmic regions were observed in both materials but quite high activation energy results in quick drop of conductivity at low temperatures and the materials can be treated as good isolators below 100°C. The obtained results are comparable with traditional epoxy resins.

Porównano przewodnictwo dwóch matryc epoksydowych, opartych na tym samym monomerze. Monomer epoksydowy miał budowę symetryczną i zawierał grupę bifenylową, która wpłynęła na powstanie dodatkowych przejść fazowych w czystym materiale. Do wytworzenia matryc użyto dwóch amin odpowiedzialnych za różne mechanizmy sieciowania. W obu materiałach zaobserwowano szerokie przedziały przewodnictwa omowego, ale duża energia aktywacji powoduje szybki spadek przewodnictwa w niskich temperaturach i poniżej 100°C materiały te mogą być traktowane jak dobre izolatory. Otrzymane wyniki są porównywalne z tradycyjnymi żywicami epoksydowymi.