Influence of a steel surface treatment on the wetting angle and free surface energy

Lipa S., Atraszkiewicz R., Klimek L.

Inżynieria Materiałowa

|

2017

|

Vol. 38, nr 6

285--289

EN

This paper presents the influence of abrasive blasting of various grain sizes and types, electro-etching and heating in an argon-hydrogen atmosphere on the wettability and free surface energy of samples prepared steel strips. The choice of treatments was dictated by the surface preparation for hot-dip zinc-coating. It was shown that the surface abrasive that was blasted with silicon carbide by a 0.300-0.250 mm grain is of a hydrophobic nature. The surface electroetched at room temperature is at the edge of hydrophobicity and hydrophilicity. In contrast, the surfaces treated in the argon-hydrogen atmosphere may be considered to be hydrophilic. In summary, it can be concluded that the suitable choice of treatment has a favourable influence on the adhesive properties of the treated steel substrates, which should result in a solid and strong steel-zinc coating joint.

PL

Właściwe przygotowanie powierzchni dla procesu cynkowania ogniowego stanowi kluczowe zagadnienie poprawności i jakości wykonania tego procesu. Poza czystością powierzchni oraz stopniem jej rozwinięcia jest ważne określenie stopnia jej zwilżalności, co wpływa na jakość wytworzonych powłok cynkowych. W pracy przedstawiono wpływ obróbki strumieniowo-ściernej o różnej wielkości i rodzaju ziarna, elektro-trawienia i wygrzewania w atmosferze argon–wodór na zwilżalność i swobodną energię powierzchni próbek. Wybór sposobów obróbki był podyktowany przygotowaniem powierzchni pod cynkowanie ogniowe.

2

Elektrolitycza obróbka stali chromowo-niklowej w kontekście stanu powierzchni i ubytku materiału

Krzywiecki M., Kucharska B.

Elektronika : konstrukcje, technologie, zastosowania

|

2014

|

Vol. 55, nr 8

87-90

PL

W pracy przedstawiono wyniki elektroobróbki austenitycznej stali chromowo-niklowej 310S. Stal poddano zabiegom elektropolerowania i elektrotrawienia w roztworze na bazie kwasu nadchlorowego oraz 3% roztworze chlorku sodu przy różnych parametrach napięcia i czasu. Badano stan powierzchni stali z użyciem mikroskopu skaningowego oraz ubytek stali w funkcji czasu polerowania. Wykazano efektywność stosowania roztworu kwasu nadchlorowego zarówno pod kątem wygładzenia powierzchni jak i ujawniania mikrostruktury stali. Elektroobróbka w roztworze chlorku sodu powoduje silne zużycie powierzchni i powstawanie wżerów. Na podstawie czasowej charakterystyki procesu elektropolerowania w rozworze kwasu nadchlorowego przy napięciu 32 V określono ilościowe zużycie stali, wynoszące 0,52 μm/s, które może być wykorzystane do kontrolowanego zdejmowania cienkich warstw stali na potrzeby badań gradientu mikrostruktury i tekstury oraz naprężeń.

EN

Austenitic electro treatment results of 310S chrome-nickel steel have been presented in this paper. The steel has undergone the processes of electropolishing and electroetching in a solution based on perchloric acid and a 3% solution of sodium chloride at different parameters of voltage and time. The surface condition of the steel has been examined using a scanning microscope and the loss of steel in the function of polishing time. The effectiveness of using the perchloric acid solution has been determined in terms of both surface smoothing and the exposition of the steel’s microstructure. Electrotreatment in the solution of sodium chloride causes a strong wear of the surface and the occurrence of pittings. Based on the temporary characteristics of the electropolishing process in the solution of perchloric acid at 32 V, the amount wear of steel has been determined amounting to 0,52 μm/s, which can be used for controlled removal of thin layers of steel needed for microstructure,, texture and stresses research.

3

Efekt ujawnienia mikrostruktury w elektrolitycznej obróbce stali chromowo-niklowych

Krzywiecki M., Kucharska B., Spalik M., Wróbel. A.

Inżynieria Materiałowa

|

2011

|

Vol. 32, nr 4

495-498

PL

W pracy przedstawiono wyniki badań elektrolitycznego polerowania i trawienia trzech gatunków stali chromowo-niklowej 304, 310S i 316 w roztworze kwasu nadchlorowego. Trawienie oraz polerowanie prowadzono w różnych warunkach napięciowo-czasowych na stalach z różnie przygotowaną powierzchnią: odtłuszczoną, szlifowaną na papierach ściernych i polerowaną na suknach. Efektywność elektropolerowania i trawienia oceniono za pomocą obserwacji na mikroskopie skaningowym. Wykazano, że ujawnienie struktury stali 304 i 310S jest możliwe za pomocą napięcia polerowania i trawienia odpowiednio 38 V i 10 V. W przypadku stali 316 parametry procesu elektrolitycznego powinny być wyższe. Ponadto wykazano, że struktura ujawnia się efektywniej na powierzchni stali z technologicznym stanem powierzchni po walcowaniu blachy i szlifowanych na papierze ściernym niż na stalach polerowanych na suknach.

EN

The article presents the results of studies on the electrolytic polishing and etching of three chromium-nickel steel grades, 304, 310S and 316, in a perchloric acid solution. Etching and polishing was conducted under varying voltage-time conditions on steels with the surface having been prepared in a different manner: degreased, abrasive paper ground, and cloth polished. The effectiveness of electropolishing and etching was assessed by observation under a scanning microscope. It has been demonstrated that revealing the structure of steels 304 and 310S is possible using a polishing and etching voltage of 38 V and 10 V, respectively, while in for steel 316 the electrolytic process parameters should be higher. It has also been demonstrated that the structure reveals itself more effectively on steels with a technological state condition after sheet rolling and ground with abrasive paper than on cloth polished steels.