Regenerated Cellulose/Graphene Composite Fibers with Electroconductive Properties

Kulpinski Piotr, Jeremiasz K. Jeszka, Malolepszy Artur, Stobinski Leszek

Autex Research Journal

|

2022

|

Vol. 22, no. 2

177--183

EN

Conductive cellulose fibers may find application in producing antistatic materials and fibrous electronic elements for smart textiles (textronics). In this paper, we present a method of fabrication of cellulose fibers modified with the reduced graphene oxide (rGO) and graphene oxide (GO). The fibers were obtained by using N-methylmorpholine-N-oxide (NMMO) as a direct solvent, adding dispersion of GO during the cellulose dissolution process. In the next step, the GO enclosed in the fibers was reduced for ca. half an hour at 90°C with the excess of water solution of hydrazine to obtain fibers containing rGO. The viscosity of the spinning solution increased when GO was added; however, the difference is important at low shearing rates but decreases at high shearing rates, similar to that used in the process of fiber spinning. Cellulose fibers containing 3, 4, 6, and 10% w/w of rGO were obtained. Fiber morphology was studied using electron microscopy. The results of the electrical properties’ measurements showed that the conductivity of modified fibers strongly depends on the concentration of rGO. At 10% rGO conductivity was 9 x 10−3 S/cm. The mechanical properties of the obtained fibers were slightly changed by the presence of GO and rGO. Tenacity and elongation at break decreased with the increase in the content of GO and rGO in the fibers but remain at an acceptable level from the textiles processing point of view.

2

Synteza i właściwości elektroprzewodzące materiałów na bazie silikonu do zastosowań w przemyśle obuwniczym

Olszewski P. K., Tarnawski I., Falkiewicz-Dulik M.

Technologia i Jakość Wyrobów

|

2017

|

R. 62

4--16

PL

W pracy przedstawiono wyniki badań nad syntezą silikonów przewodzących na bazie addycyjnego silikonu HT33 oraz dwóch rodzajów przewodzących włókien: poliakrylonitrylowych modyfikowanych solami miedzi (Nitril-Static, Instytut Włókiennictwa) oraz węglowych (T700 GC, Toray). Przedstawiono zależności rezystywności od rodzaju i zawartości składników przewodzących oraz warunków syntezy materiałów. Najlepsze wyniki w zakresie właściwości elektroprzewodzących osiągnięto dla silikonów zawierających 5% włókien węglowych (rezystywność skrośna poniżej 30 Ω·cm). W artykule wskazano możliwe zastosowania otrzymanych materiałów do produkcji obuwia.

EN

The results of investigations on the synthesis of conductive silicones based on HT33 silicone additive and two types of conductive fibers: polyacrylonitrile fibers modified with copper salts (Nitril-Static, Instytut Włókiennictwa) and graphite fibers (T700 GC, Toray). Resistivity, was determined on the type and content of conductive components and materials synthesis conditions. The best results in electroconductive properties were achieved for silicones containing 5% of carbon fibers (cross resistivity below 30 Ω·cm). The article mentions the possible applications of obtained materials for the manufacture of footwear.

3

Badania fizyko-mechaniczne przewodzących kompozytów silikonowych przeznaczonych na spody obuwia

Olszewski P. K., Tarnawski I., Falkiewicz-Dulik M.

Technologia i Jakość Wyrobów

|

2017

|

R. 62

17--26

PL

W pracy przedstawiono wyniki badań nad przewodzącymi kompozytami otrzymanymi na bazie addycyjnego silikonu HT33 oraz dwóch rodzajów przewodzących włókien: poliakrylonitrylowych modyfikowanych solami miedzi (Nitril-Static, Instytut Włókiennictwa) oraz węglowych (T700 GC, Toray). Przedstawiono zależności twardości i wytrzymałości na rozciąganie od rodzaju i zawartości składników przewodzących oraz warunków otrzymywania materiałów. Dane z pomiarów fizyko-mechanicznych porównano z wynikami badań przewodnictwa elektrycznego. Optymalne właściwości mechaniczne i elektryczne pozwalające na zastosowanie opracowanego materiału w obuwnictwie uzyskano dla silikonu zawierającego 2% włókien węglowych. W artykule wskazano możliwe zastosowania otrzymanych materiałów do produkcji obuwia.

EN

The results of investigations on the synthesis of conductive composites based on HT33 silicone additive and two types of conductive fibers: polyacrylonitrile fibers modified with copper salts (Nitril-Static, Instytut Włókiennictwa) and graphite fibers (T700 GC, Toray). Hardness and tensile strengths were determined on the type and content of conductive components and materials manufacturing conditions. Physico -mechanical data were compared with results of resistivity measurements. The optimum mechanical and electrical properties of the developed material for use in footwear industry were obtained for silicone containing 2% of graphite fibers. The article mentions the possible applications of obtained materials for the manufacture of footwear.