Application of potentiostatic measurements according to PN-EN 480-14 in assessment of the efficiency of reinforcement protection against corrosion by concrete with addition of fly ashes

Domagała K., Śliwka A.

Architecture Civil Engineering Environment

|

2017

|

Vol. 10, no. 3

109--115

EN

Replacing part of the cement in the concrete with fly ash - products of solid fuel burning, requires testing, including the degree of the reinforcement protection against corrosion provided by concrete. The paper presents a comparison of the results of the tests of the effectiveness of corrosion protection of reinforced concrete with the addition of calcareous fly ash. Tests were conducted by two electrochemical methods. Results obtained by potentiostatic measurement on reinforcement inserts deposited in cylindrical specimens in accordance with EN 480-14 standard were compared with studies investigating the progress of reinforcement corrosion caused by chlorides in loaded and cracked test elements made of these concretes. Tests of the cracked elements reflect the behaviour of reinforced concrete construction during operation in adverse environmental conditions, classified as standard XD and XS exposure classes. Comparison of the tests indicates the potential for potentiostatic measurement to be used to current assessment of protective properties of concrete with mineral additives.

PL

Zastąpienie części cementu w betonie popiołami lotnymi - produktami spalania paliw stałych, wymaga przeprowadzania badań, w tym stopnia ochrony zbrojenia przed korozją, którą powinien zapewnić beton. W artykule przedstawiono porównanie wyników badań skuteczności ochrony antykorozyjnej betonu z cementu z dodatkiem wapiennych popiołów lotnych względem stali zbrojeniowej. Badania przeprowadzono metodami elektrochemicznymi. Wyniki uzyskane za pomocą pomiaru potencjostatycznego na wkładkach zbrojeniowych umieszczonych w próbkach cylindrycznych zgodnie z normą EN 480-14 porównano z badaniami postępu korozji zbrojenia wywołanej chlorkami w obciążonych i zarysowanych elementach próbnych wykonanych z tych betonów. Badania elementów zarysowanych odzwierciedlają zachowanie konstrukcji żelbetowej podczas pracy w niekorzystnych warunkach środowiskowych, charskteryzowanych jako klasy ekspozycji XD i XS. Porównanie badań wskazuje na możliwość zastosowania pomiaru potencjostatycznego do bieżącej oceny właściwości ochronnych betonu z dodatkami mineralnymi.

2

Corrosion Resistance Of Electroless Ni-P/Cu/Ni-P Multilayer Coatings

Zhao G. L., Zou Y., Hao Y. L., Zou Z. D.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 2A

1003--1008

EN

Ni-P/Cu/Ni-P multilayer coatings were prepared by deposition of Cu layer between two Ni–P layers. The Cu layer was deposited by metal displacement reaction between Cu2+ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive Ecorr and decreased Icorr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.

PL

Wielowarstwowe powłoki Ni-P/Cu/Ni-P wytworzono metodą osadzania miedzi pomiędzy dwoma warstwami Ni-P. Warstwę Cu otrzymano dzięki reakcji wypierania metalu przez metal (dla miedzi i żelaza). Aby określić właściwości korozyjne jednowarstwowej powłoki Ni-P, dwuwarstwowej Ni-P/Cu oraz trójwarstwowej Ni-P/Cu/Ni-P przeprowadzono pomiary elektrochemiczne w 3,5% roztworze NaCl. Powłoki trójwarstwowe w porównaniu do jednowarstwowych wykazały się większą wartością Ecorr, przy malejącej wartości Icorr. Wskazuje to na poprawę odporności na korozję. Krzywe polaryzacji dla powłok trójwarstwowych charakteryzują się występowaniem dwóch obszarów pasywacji. Poprawa odporności na korozję jest skutkiem nie tylko tzw. zjawiska blokowania porów w miedzi. Powłoka z Cu działała także jako warstwa protektorowa, modyfikując mechanizm korozji i poprawiając odporność korozyjną powłok.

3

Properties of carbide layers produced by means of the vacuum titanizing process combined with galvanic treatment

Kasprzycka E.

Problemy Eksploatacji

|

2006

|

nr 2

81-89

EN

A new technological processes combining a vacuum titanizing with a preliminary electrolytic deposition of Co-W or Ni-Mo alloys on the tool steel surface have been proposed to increase the corrosion resistance of the carbide layers of the TiC type. As a result, composite carbide layers of the TiC+(Co-W) and TiC+(Ni-Mo) type on the steel surfaces have been obtained. It has been proved that the wear resistance by friction of these composite layers produced by means vacuum titanizing of steel covered with electrolytic coatings is as good as the TiC carbides layers produced on the steel surface without electrolytic coatings, but their corrosion resistance is higher.

PL

W pracy przedstawiono wyniki badań dotyczących właściwości użytkowych warstw kompozytowych typu TiC+(Co-W) oraz TiC+(Ni-Mo) wytwarzanych w procesie tytanowania próżniowego na powierzchni stali X210Cr12 pokrytej elektrolitycznie stopami Co-W lub Ni-Mo. Określono właściwości tribologiczne oraz odporność korozyjną warstw. Stwierdzono, że odporność na zużycie przez tarcie warstw kompozytowych typu TiC+Co-W) oraz TiC+(Ni-Mo) wytwarzanych w procesie chromowania próżniowego na stali pokrytej powłokami Co-W lub Ni-Mo, jest równie dobra, jak warstw węglikowych typu TiC, wytwarzanych bez wstępnego osadzania powłoki elektrolitycznej, natomiast ich odporność korozyjna jest kilkakrotnie większa.