Nanocrystallinie TiNi, Ti2Ni alloys for hydrogen storage

Balcerzak M., Nowak M., Jurczyk M.

Inżynieria Materiałowa

2012

Vol. 33, nr 5

370--373

Mechanical alloying (MA) process was introduced to produce nanocrystalline TiNi- and Ti 2Ni-type alloys. XRD analysis showed that after 8 h of milling the starting mixture of the elements had decomposed into an amorphous phase. Following the annealing in high purity argon at 750°C for 0.5 h, XRD confirmed the formation of the CsCl- and CFe3W3-type structures with a crystallite sizes of about 30 nm, respectively. These materials were used as negative electrodes for a Ni-MHx. In the nanocrystalline TiNi and Ti2Ni powders, at 3rd cycle, discharge capacities up to 260 mAhg–1 and 172 (at 40 mAg–1 discharge current) were measured, respectively. The Ti2Ni hydrogen storage alloy is attractive for secondary battery, because of inexpensive raw materials.

Nanokrystality stopów typu TiNi i Ti 2Ni wytworzono za pomocą mechanicznej syntezy (MA). Analiza XRD wykazała, że po 8 godzinach mielenia mieszanka wyjściowych składników utworzyła fazę amorficzną. W wyniku wyżarzania materiałów w atmosferze argonu w 750°C przez 0,5 godziny powstały struktury typu CsCl i CFe 3W3 o wielkości krystalitów rzędu 30 nm, których obecność została potwierdzona przez badania XRD. Materiały te wykorzystano do utworzenia ujemnej elektrody dla akumulatorów typu Ni-MHx. Pojemność rozładowania elektrod w trzecim cyklu wynosiła odpowiednio 260 dla TiNi oraz 172 mAhg –1 dla Ti 2Ni (przy prądzie rozładowania wynoszącym 40 mAg –1). Stop Ti 2Ni jest atrakcyjnym materiałem do produkcji baterii akumulatorowych ze względu na niską cenę surowców.