Wyniki wyszukiwania - BazTech

1

Spiekane kompozyty magnezowe typu in situ

Olszówka-Myalska A

Mechanik

|

2016

|

R. 89, nr 5-6

504--505

PL

W artykule przedstawiono możliwości wykorzystania metalurgii proszków do wytwarzania kompozytów z osnową magnezową umacnianych fazami wytworzonymi in situ z reaktywnych komponentów. Problem zilustrowano na przykładzie mieszaniny mikroziarnistych proszków Mg-Ti-Al oraz mieszaniny mikroziarnistego proszku Mg z nanoziarnistym proszkiem SiO2. Scharak-teryzowano efekty strukturalne i umocnienie.

EN

The possibilities of powder metallurgy application for fabrication of magnesium matrix composites with rein-forcing phases formed in situ due to reactive components interaction were presented. As an issue illustrating the mixture of micro-sized Mg-Ti-Al powders and micro-sized Mg with nanosized SiO2 were applied. There were characterized a structural and strengthening effects.

2

Wpływ czasu mielenia na mikrostrukturę i skład fazowy magnesów Sm-Fe-N

Pawlik P., Wysłocki J. J., Pawlik K., Kaszuwara W., Leonowicz M.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 1

19-35

PL

Badano magnesy Sm-Fe-N wytworzone metodą dyfuzji reaktywnej. Stosując dyfrakcję rentgenowską i spektroskopię moessbauerowską stwierdzono, że badany magnes składa się z magnetycznie twardych faz: Sm2Fe17N0.86 i SmFe5 oraz fazy magnetycznie miękkiej alfa-Fe. Ponadto określono udziały objętościowe poszczególnych faz. Przeprowadzono obserwacje mikrostruktury z użyciem zarówno mikroskopu optycznego, jak i skaningowego mikroskopu elektronowego oraz transmisyjnego mikroskopu elektronowego. Zbadano również zmiany właściwości magnetycznych, takich jak: koercja, jHc, remanencja Mr i maksymalna gęstość energii magnetycznej (BH)max w zależności od czasu mielenia magnesów Sm-Fe-N.

EN

Permanent magnets Sm-Fe-N produced by reactive diffusion method were investigated. Using X-ray diffraction and Moessbauer spectroscopy it was found that this magnet consists of hard magnetic phases: Sm2Fe17N0.86 and SmFe5 and soft magnetic alpha-Fe phase. Furthermore, volume fractions of these phases were determined. The microstructure observations were performed using an optical metallographic microscope, a scanning electron microscope and a transmission electron microscope. Moreover, the changes in magnetic properties, such as coercive force jHc, remanence Mr and energy product (BH)max depending on grain size of the Sm-Fe-N magnet were reported.

3

Temperature dependence of the magnetization in Sm-Fe-N magnets with different grain size

Pawlik P., Wysłocki J. J., Olszewski J., Leonowicz M., Kaszuwara W.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 1

5-18

EN

The temperature dependence of the magnetization in Sm-Fe-N permanent magnets produced by reactive diffusion method with different grain size (from 8.6 to 0.97 micrometer), were investigated. Applying X-ray diffraction and Moessbauer spectroscopy, it was found that this magnet consists of hard magnetic phases: Sm2Fe17N0.86 and SmFe5 and soft magnetic alpha-Fe phase. Furthermore, the volume fractions of these phases were determined. The measurements of temperature dependence of magnetization reveal an unusual increase of magnetization just below Curie temperature. This is related to the changes in the volume fractions of the constituent phases, in particular to the increase in the alpha-Fe phase with high value of saturation magnetization Ms, and the decrease in hard magnetic Sm2Fe17N0.86 phase.

PL

Zbadano wpływ temperatury na namagnesowanie magnesów Sm-Fe-N o różnej wielkości ziarna (od 8,6 do 0,97 mikrometra), wytworzonych metodą dyfuzji reaktywnej. Stosując dyfrakcję rentgenowską i spektroskopię moessbauerowską, stwierdzono, że badany magnes składa się z magnetycznie twardych faz: Sm2Fe17N0,86 i SmFe5 oraz fazy magnetycznie miękkiej alfa-Fe. Ponadto określono udziały objętościowe poszczególnych faz. Pomiary zależności namagnesowania od temperatury pozwoliły stwierdzić nietypowy wzrost namagnesowania w temperaturach bliskich temperaturze Curie, związany ze zmianą zawartości objętościowej faz składowych, a w szczególności wzrostem zawartości fazy alfa-Fe o wysokiej wartości namagnesowania nasycenia Ms oraz spadkiem zawartości fazy magnetycznie twardej Sm2Fe17N0.86.