Wyniki wyszukiwania - BazTech

1

Quantitative assessment of the influence of plasma hardfacing parameters on the metallurgical melting of an austentic steel coating with a substrate material made of C45 steel

Bazychowska Sylwia, Starosta Robert, Dudzik Krzysztof

Journal of KONBiN

|

2022

|

Vol. 52, iss. 3

27--51

EN

In this paper, based on a quantitative analysis of the parameters of plasma hardfacing of C45 steel with CastoMag 45554S wire, an optimisation of the hardfacing process parameters has been carried out. Experimental researches were carried out on the basis of an orthogonal plan, and the optimum hardfacing parameters, e.g.: intensity, voltage, wire feeding speed, were determined by the multiple regression method and the Taguchi method. It was found that the main current of the plasma arc had the greatest influence on the value of the fusion index. The highest S/N value was obtained for the following parameters: I = 120 A, U = 31 V, vn = 0.75 m/min, vd = 3.9 m/min, z = 12 mm.

PL

W oparciu o ilościową analizę parametrów napawania plazmowego stali C45 drutem CastoMag 45554S dokonano optymalizacji parametrów procesu napawania. Badania realizowano na podstawie planu ortogonalnego, a optymalne parametry napawania np.: natężenie, napięcie, prędkość podawania drutu zostały wyznaczone metodą regresji wielokrotnej oraz metodą Taguchi. Ustalono, że największy wpływ na wartość współczynnika wtopienia ma natężenie prądu głównego łuku plazmowego. Największą wartość współczynnika S/N uzyskano przy parametrach: I = 120 A, U = 31 V, vn = 0,75 m/min, vd = 3,9 m/min, z = 12 mm.

2

Wpływ wybranych parametrów technologicznych metody MIG na wielkość kropli z brązu CuSN6 w chwili przerywania jarzenia łuku

Haduch J.

Przegląd Spawalnictwa

|

2006

|

R. 78, nr 2-3

23-25

3

Badanie wpływu obniżonej temperatury na pękanie złącza spawanego

Dymski S., Giętka T., Stawicka Z., Kaczmarek M.

Archiwum Odlewnictwa

|

2005

|

R. 5, nr 17

99--106

PL

Badania dotyczyły spawanych płyt próbnych ze stali 18G2A drutem elektrodowym Union K56-Thyssen metodą GMA. Spawanie odbyło się półautomatycznie w osłonie gazu Corgon (82 % Ar+18 % CO2). Zginanie udarowe wykonano na próbach udarnościowych o wymiarach 10x10x55 mm z karbem V w zakresie temperatur 20÷–60 oC. Karb V umiejscowiono w osi spoiny, strefie wpływu ciepła, i w linii obejmującej spoinę i strefę wpływu ciepła (strefa przejściowa). Badano również udarność materiału podstawowego. Wyznaczono temperaturę kruchości badanych elementów spoiny. Analizę uzupełniono badaniami przełomów za pomocą elektronowego mikroskopu skaningowego (SEM).

EN

The examinations concerned the welded tentative plates of steel 18G2A of GMA method with the weld deposit – Union K56-Thyssen. The welding took place semi-automatically under the protection of gas Corgon (82 % Ar + 18 % CO2). The impact bending was executed on the tension impact test of the dimensions 10x10x55 mm with V – notch in the range of temperatures 20 ÷ –60oC. V– notch was localized in the axis of weld, in heat affected zone and in the line which includes the weld, the heat affected zone (transition zone). The impact of parent material was also tested. The brittle point of the elements of weld which were tested was marked on the basis of the results. The analysis was completed through the examinations of fractures by means of the scanning electron microscope (SEM).

4

Zastosowanie standardowego zasilacza łuku do zrobotyzowanego spawania

Kozak T., Olejnik K., Wasielewski P.

Przegląd Spawalnictwa

|

2004

|

R. 76, nr 5-7

89-93

5

Nowe spojrzenie na stałą topienia drutów elektrodowych.

Piątkowski T.

Biuletyn Instytutu Spawalnictwa w Gliwicach

|

1999

|

R. 43, nr 5

138-140

PL

W celu uwzględnienia czynnika ekonomicznego we wskaźniku charakteryzującym wydajność stapiania, zaproponowano modyfikację współczynnika stapiania elektrody w taki sposób, aby wyrażał się on ilorazem masy stopiwa i energii potrzebnej do jego stopienia w jednostce czasu. Próby napawania przeprowadzone przy zastosowaniu drutu litego i drutów proszkowych w osłonie CO2 i różnych mieszanek gazowych wykazały, że zmodyfikowany współczynnik stapiania lepiej charakteryzuje koszty spawania od współczynnika dotychczas stosowanego, ponieważ uwzględnia on energochłonnośc procesu.

EN

With a view to include the economical aspect in the index characterizing deposition efficiency it has been proposed such a modification of metal deposit factor that it is a ratio of weld material mass and heat necessary for melting it in a time unit. The tests of weld surfacing carried out with use of solid wire and tubular wires under shield of CO2 and various gas mixtures have shown that the welding cost is better characterised by the modified metal deposit factor than by the factor used till now because the last-mentioned does not take into account the energy consumption in a welding process.