Analysis of Nd3+/Yb3+ ions energy transfer in oxyfluoride silicate glass for optical fibre ASE source

Dorosz D., Żmojda J., Kochanowicz M., Dorosz J.

Materiały Ceramiczne

2011

T. 63, nr 1

44-47

The paper presents optimisation of Nd3+/Yb3+ ratio to enhance the emission bandwidth at 1 µm. Analysis of the energy transfer scheme between Nd3+ and Yb3+ ions incorporated in oxyfluoride glass was performed. The highest efficiency (60 %) was measured for the equalvalues of absorption cross-section (Yb3+) and emission cross-section (Nd3+). The emission spectrum with 100 nm bandwidth of the Nd3+/Yb3+ co-doped glass samples under excitation at 808 nm was determined. The fabricated glass with the highest efficiency of energy transfer Nd3+--Yb3+ was used as a core in helical core double clad optical fibre.

Artykuł przedstawia optymalizację stosunku Nd3+/Yb3+ w celu zwiększenia szerokości pasma przy 1 µm. Przeprowadzono analizę schematu przekazywania energii pomiędzy jonami Nd3+ i Yb3+ wprowadzonymi do szkła tlenofluorkowego. Największą efektywność (60 %) zmierzono w przypadku równych wartości przekrojów czynnych na absorpcję (Yb3+) i emisję (Nd3+). Określono widmo emisyjne o szerokości pasma 100 nm w przypadku próbek szkła współdomieszkowanego jonami Nd3+ i Yb3+ wzbudzanych przy 808 nm. Wytworzone szkło o najwyższej efektywności przekazywania energii Nd3--Yb3+ wykorzystano jako rdzeń w światłowodzie typu double-clad o rdzeniu spiralnym.

Rare earth ions doped aluminosilicate and phosphate double clad optical fibres

Dorosz D.

Bulletin of the Polish Academy of Sciences. Technical Sciences

2008

Vol. 56, nr 2

103-111

The paper presents the result of investigations of aluminosilicate (low silica - 25 mol%) and phosphate optical fibres. The methods of glass preparation and their properties are showed. A set of physical measurements including: DTA, DSC, DL analysis, absorption spectroscopy, visible and infrared absorption edges and thermo-physical properties were determined. The stable glass compositions were doped with rare earth elements. Selected proper-ties of obtained glasses are: high transmission, refractive index 1.53-1.68, high solubility of RE ions (up to 10 wt%). Double-crucible and rod-in-tube drawing techniques were applied to obtain aluminosilicate and phosphate double clad optical fibres doped with neodymium and ytterbium ions. Luminescence spectra of manufactured glasses and fibres are presented.