The effect of shrinkage reducing admixture and expansive admixture on properties of mortars with Portland and slag cement

Gołaszewski Jacek, Gołaszewska Małgorzata

Archives of Civil Engineering

|

2022

|

Vol. 68, nr 2

337--353

EN

Both shrinkage reducing admixtures (SRA) and expansive admixture (EXP) can be used to reduce the risk of cracking in concrete. Synergistic effect of using both of those admixtures simultaneously was a was found, however little information can be found on the effects of using both EXP and SRA on the properties of mortars and concrete other than shrinkage. Therefore in this paper, effect of adding both EXP and SRA on properties of mortars outside of their effect on shrinkage is researched. Mortars with Portland cement CEM I were modified by adding EXP and SRA in amount of full dose recommended by the producer, and half of the recommended dose. Research consisted of tests of properties of fresh mortars (consistency, initial setting time, hydration heat) and hardened mortars (compressive strength and drying shrinkage). It has been found that using both SRA and EXP admixtures leads to maintaining the same setting time which can be prolonged if only SRA is used, decreased compressive strength, possibility of increased consistency. Synergistic effect on shrinkage was also confirmed.

PL

Jednym z głównych problemów mogących powodować spadek trwałości betonu jest pękanie związane z jego skurczem. Zjawisko skurczu betonu jest jednym z częściej podnoszonych problemów w technologii betonu, ze względu na fakt, że w dojrzewającym betonie występuje wiele mechanizmów skurczu jednocześnie w różnych okresach, a różne rodzaje skurczu wymagają różnych metod jego redukcji. Aby spróbować ograniczyć skurcz, opracowano wiele metod, m.in. stosowanie środków ekspansywnych lub stosowanie domieszek zmniejszających skurcz (SRA). Środki ekspansywne służą do kompensacji skurczu poprzez pobudzenie reakcji tworzenia ekspansywnego etryngitu w pierwszych godzinach hydratacji, tak by kompensować redukcję objętości w wyniku skurczu chemicznego i autogenicznego. Mechanizm działania SRA jest natomiast łączony głównie z redukcją skurczu wysychania, ze względu na jego działanie związane z kilkoma równoczesnymi efektami zachodzącymi w jego obecności: obniżenie napięcia kapilarnego na skutek niskiego napięcia powierzchniowego oraz stworzenie struktury z mniejszymi porami pojawiającymi się na skutek obniżonego napięcia powierzchniowego, co pozwala na utrzymanie wysokiej wilgotności względnej. W celu lepszej redukcji skurczu podjęto próby stosowania obydwu domieszek jednocześnie, otrzymując bardzo dobre wyniki redukcji skurczu; problemem w powszechniejszym zastosowaniu tej metody jest niewielka ilość informacji o wpływie stosowania domieszki SRA i ekspansywnej na raz na inne właściwości betonów i zapraw. Dlatego w niniejszym artykule przedstawiono analizę wpływu stosowania zarówno domieszki ekspansywnej (EXP) jak i SRA na właściwości zapraw. Zaprawy z cementem portlandzkim CEM I 42.5R (OPC) i CEM III/A 32.5N-LH/HSR/NA (SC) modyfikowano dodając dostępne na rynku domieszki EXP i SRA w ilości pełnej dawki zalecanej przez producenta i połowy zalecanej dawki. Testy przeprowadzono zarówno na zaprawach z tylko jedną domieszką, jak i na ich kombinacji. Badania obejmowały badania właściwości zapraw świeżych (konsystencja, czas początku wiązania, ciepło hydratacji) oraz zapraw stwardniałych (wytrzymałość na ściskanie i skurcz wysychania).

2

Analysis of the properties of expansive concrete with portland and blast furnace cement

Jackiewicz-Rek W., Kuziak J., Jaworska B.

Archives of Civil Engineering

|

2018

|

Vol. 64, nr 4/I

175--196

EN

The properties of expansive concretes made of two types of cement: Portland cement CEM I and blast furnace slag cement CEM III were tested. The expansion of the concrete was caused by using an expansive admixture containing aluminium powder added in an amount of 0.5; 1 and 1.5% of cement mass. It was found that the compressive strength of concrete with CEM I decreased after using an expansive admixture in the amount of more than 0.5% of the cement mass. The compressive strength of concrete with CEM III decrease after addition of admixture in the entire range of dosages used. On the basis of electrochemical measurements, it was found no influence of an expansive admixture on corrosion of reinforcing steel. The use of an expansive admixture causes a slight increase in the effective diffusion coefficient of chloride ions in concrete.

PL

W pracy przedstawiono wyniki badań właściwości betonów ekspansywnych o w/c = 0,37 wykonanych z dwóch rodzajów cementu: cementu portlandzkiego CEM I i cementu hutniczego CEM III. Ekspansję betonu wywołano domieszką ekspansywną zawierającą proszek aluminiowy dozowaną w ilości 0,5; 1 i 1,5% masy cementu. Dotychczas proszek aluminiowy był wykorzystywany w technologii betonu m.in. do napowietrzania betonu, produkcji betonu lekkiego, produkcji betonu komórkowego. Proszek aluminiowy w zasadowym środowisku mieszanki betonowej wchodzi w reakcje, w wyniku których wydziela się gazowy wodór. Pod wpływem ciśnienia wywieranego przez wytwarzający się gaz następuje wzrost objętości mieszanki betonowej. Z tego względu proszek aluminiowy może być wykorzystany do produkcji betonów ekspansywnych, do efektywnego wypełniania trudnodostępnych miejsc takich jak szczeliny czy ubytki, a także do produkcji betonów o ograniczonym skurczu w celu zapobiegania zarysowaniom. W pracy przedstawiono wyniki następujących badań: badanie konsystencji mieszanki betonowej metodą opadu stożka, badanie wytrzymałości na ściskanie betonu oraz badania zdolności ochronnych betonu dla stali zbrojeniowej w zakresie badań korozyjnych stali w wyciągach wodnych z betonów i dyfuzji jonów chlorkowych w betonie. Dodatkowo określono przyrost objętości betonu - ekspansję betonu w czasie do 1 godziny od wymieszania składników mieszanki betonowej.

3

Ocena efektywności domieszek i dodatków redukujących odkształcenia skurczowe kompozytów cementowych

Gruszczyński M.

Materiały Budowlane

|

2009

|

nr 12

40-43