The Rate of Metal Oxygen Reduction from the Slag of the Direct-To-Blister Flash Smelting Process

Rogóż K., Kucharski M.

Archives of Metallurgy and Materials

2010

Vol. 55, iss. 1

317-323

A slag from the direct-to-blister flash smelting process, as well as the same slag modified by CaO and MgO additions, were reduced by powdered graphite. The ratę of the oxygen removal from these slags was determined at 1523 K, 1573 K and 1623 K. It was found that, for the original slag and the slag modified by CaO and MgO additions with xCao = 0-25, and xMgo = 0.25, the oxygen removal follows a reaction of the first order. For a higher concentration of the slag modifiers, the reduction process is controlled by mass transport.

Praca zawiera wyniki badań nad kinetyką otrzymywanego odmiedziowania żużla z procesu jednostadialnego Outokumpu za pomocą sproszkowanego grafitu. Badania przeprowadzono dla żużla otrzymanego bezpośrednio z pieca zawiesinowego oraz dla tego samego żużla modyfikowanego dodatkami CaO i MgO w temperaturach 1523K, 1573K i 1623K. Dla żużla wyjściowego oraz żużli modyfikowanych dodatkiem CaO (xCao = 0,25) lub dodatkiem MgO (xMgo =0,25) stwierdzono, że proces redukcji jest reakcją pierwszego rzędu. Dla żużli o większych stężeniach modyfikatorów (xCao = 0,3, xMgo = XcaO = 0,25) proces redukcji jest kontrolowany przez transport masy.