Cross-linked epoxy-isocyanate blends containing Epidian-6 modified by glycols

Bratychak M., Ivashkiv O., Bruzdziak P., Namiesnik J., Shyshchak O.

Polimery

2016

T. 61, nr 5

316--321

Polymeric films of cross-linked structure may be formed using epoxy-isocyanate blends composed of Epidian-5 epoxy resin, 4,4'-diphenylmethanediisocyanate (MDI), Z-1 polyamine hardener and Epidian-6 epoxy resin modified by glycols. The effect of the component natures and ratio, process temperature and time on the gel-fraction content, as well as film hardness, was examined. The chemistry of the film forming process was determined using infrared-spectroscopy (IR).

Z mieszaniny epoksydowo-izocyjanianowej, otrzymanej z żywicy epoksydowej Epidian-5, utwardzacza Z-1 i diizocyjanianu 4,4'-metylenodifenylu (MDI), oraz żywicy epoksydowej Epidian-6 zmodyfikowanej glikolami wytwarzano folie polimerowe o usieciowanej strukturze chemicznej. Oceniano wpływ składu jakościowego i ilościowego mieszaniny, temperatury oraz czasu reakcji na zawartość frakcji żelowej gotowych folii polimerowych i ich twardość. Przebieg procesu formowania folii badano metodą spektroskopii w podczerwieni (IR).

Trimerization of 3-isocyanatomethyl-3/5A5-trimethylcyclohexyl isocyanate (IPDI)

Wejchan-Judek W., Polus I., Doczekalska B., Pertek H.

Polimery

2001

T. 46, nr 2

131-132

Trimerization of IPDI was studied in relation to catalyst type and reaction temperature. 2,4,6-tris(Dimethylaminomethyl)phenol (DMP-30), potassium acetate (K 64), l,4-diazabicyclo[2.2.2]octane (DABCO), tetrabutyl orthotitanate (TBT), and a DMP-30/K 64 binary system were used as catalysts (used in 1, 2 or 5% based on IPDI weight). When dissolved in butyl acetate and stirred for 1 h at 80°C with 5% of DMP-30, IPDI yielded a trimer melting at 286-289°C (Table 1). The most active catalyst was K 64 (added 1% by wt., as a solution in ethyl acetate containing 15% of K): in 1 h at 80°C, a trimer was obtained in 98% yield. TBT (1%, 5%), DMP-30 (1%), DABCO, and K 64 (1%, 23°C) proved to be inactive as catalysts. In the binary system studied, the DMP-30 was found to inhibit the catalytic action of the K 64 consistuent.

Badano przebieg trimeryzacji IPDI w zależności od rodzaju katalizatora i temperatury reakcji. Jako katalizatory (1, 2 lub 5% mas. w przeliczeniu na IPDI) zastosowano 2,4,6-tris(di-metyloaminometylo)fenol (DMP-30), octan potasu (K 64), l,4-diazabicyklo[2.2.2]oktan (DABCO), ortotytanian tetrabutylu (TBT) oraz układ dwuskładnikowy DMP-30/K 64. IPDI rozpuszczony w octanie butylu i mieszany w ciągu 1 h (temp. 80°C) z 5% DMP-30 tworzy trimer o tt. 286-298"C (tabela 1). Najaktywniejszym katalizatorem okazał się K 64 (w postaci roztworu w octanie etylu zawierającego 15% K), dodawany w ilości 1% mas. w przeliczeniu na IPDI; pozwala on na otrzymanie (lh, temp. 80°C) trimeru z wydajnością 98%. TBT (1%, 5%), DMP-30 (1%), DABCO oraz K 64 (1%, temp. 23°C) okazały się nieaktywne jako katalizatory. W układzie dwuskładnikowym DMP-30/K 64, DMP-30 inhibituje katalityczne działanie K 64.