Wyniki wyszukiwania - BazTech

1

Circular rotational field in dielectromagnetic

Janta T.

Przegląd Elektrotechniczny

|

2015

|

R. 91, nr 5

92-96

EN

In article example of dielectromagnetics cores working in circular rotational magnetic fields of electric converters are presented. The main advantage of dielectromagnetics can be naturally isotropy of magnetic cores but, in some solutions, profitable can be artificially prepared anisotropy properties. The characteristic with distribution of magnetic circular rotating field in dielectromagnetic made without additional anisotropy process is shown. The obtained measurement results of distribution of magnetic circular rotating field confirm the natural isotropy of dielectromagnetic.

PL

Przedstawiono przykłady magnetowodów pracujących w wirujących kołowych polach magnetycznych wykonanych z dielektromagnetyków. Główną zaletą dielektromagnetyków może być ich naturalna izotropia; natomiast w niektórych przypadkach może być wykorzystana sztucznie wytworzona anizotropia magnetowodu. Wyniki pomiarów właściwości magnetycznych dielektromagnetyku potwierdziły ich naturalną izotropię.

2

Perspektywy zastosowania dielektromagnetyku na magnetowód wirnika silnika asynchronicznego

Janta T.

Górnictwo Odkrywkowe

|

2010

|

R. 51, nr 5

37-42

PL

Magnetycznie miękkie kompozyty proszkowe znajdują coraz szersze zastosowanie jako materiały na magnetowody urządzeń elektrycznych. Specjalnym zainteresowaniem cieszą się dielektromagnetyki. Są to kompozyty proszkowe wykonane z proszku magnetycznie miękkiego domieszkowanego dielektrykiem, najczęściej żywicą, stanowiącym zarówno lepiszcze jak i izolację magnetycznie miękkich cząsteczek. W artykule podsumowano wyniki sprawdzenia możliwości zastosowania magnetyczno-przewodzących dielektromagnetyków Fe-Cu-Sn na magnetowód wirnika silnika indukcyjnego. Badano 3-fazowy silnik asynchroniczny malej mocy z dwuwarstwowym magnetowodem wirnika. Warstwa wewnętrzna to dielektromagnetyk wykonany z proszku żelaza. Warstwę zewnętrzną stanowi wyprasowany na tym walcu cylinder wykonany z magnetyczno-przewodzącego dielektromagnetyku Fe-Cu-Sn.

EN

Soft magnetic powder composites find ever-wider use as active magnetic materials for magnetic cores of electric devices. Special interest is focused on dielectromagnetics. They are powder composites made from soft magnetic powder with an admixture of dielectric, in the form of resins, which both, bind and isolate the soft magnetic particles. The goal of this paper is summary the results of possibilities to use of magneto-conductive dielectromagnetics Fe-Cu-Sn Jor magnetic core of induction motor rotor. The core, made as two layers assembly, was tested as a rotor of a small power 3 phase induction motor. An internal part of the core is made as soft magnetic cylinder. Its material is dielectromagnetic made of pure iron. An external layer, in form of sleeve, compacted on the internal part, is made of magnetic-conductive (Fe-Cu-Sn) dielectromagnetic.

3

Dławik indukcyjny z proszkowym rdzeniem dielektromagnetycznym

Przybylski M., Ślusarek B.

Elektronika : konstrukcje, technologie, zastosowania

|

2010

|

Vol. 51, nr 10

124-126

PL

Dławiki indukcyjne, zwane też często cewką z rdzeniem ferromagnetycznym, mają szerokie zastosowanie w wielu urządzeniach elektronicznych, takich jak np. zasilacze, filtry częstotliwościowe. Ich rolą, m.in., jest ograniczenie poboru prądu zmiennego bez strat mocy. W referacie przedstawiono projekt i analizę dławika z rdzeniem ferromagnetycznym z dielektro-magnetyku o indukcyjności 6 mH, maksymalnym prądzie ok. 2 A. Zakres częstotliwość pracy dławika przy maksymalnym prądzie 2 A wynosi od 50 do 1000 Hz. W pracach projektowych założono, że rdzeń dławika wykonany zostanie z magnetycznie miękkiego proszku żelaza spajanego środkiem wiążącym. Opracowano dławik o założonych parametrach eksploatacyjnych. Badania modelu dławika umożliwiły weryfikację uzyskanych parametrów. W ramach przeprowadzonych badań modelu dławika przeprowadzono pomiary: indukcyjności i strat mocy w funkcji częstotliwości i prądu. Przeprowadzono pomiary temperatury rdzenia ferromagnetycznego i uzwojenia w zależności od czasu pracy dławika.

EN

nductors, also called choke coils, are widely applied in many electronic devices such as frequency filters or power supplies. Their purpose is, among other things, limiting changing currents with lower loss than is possible with resistors. The paper presents the design and analysis of an inductor with dielectromagnetic core with inductivity of 6 mH, and maximum current ca. 2A. The range of frequency at maximum current of 2A is 50 to 1000 Hz. For research purposes it was assumed that the core will be made of soft magnetic iron powder bonded by any binding agent. An inductor with parameters as assumed was designed. Comparison of inductors' assumed and received parameters was done. Inductances and iron losses versus current and frequency were measured. Measurements were also taken of the dielectromagnetic core's temperature, as well as of the temperature of winding.

4

Wpływ temperatury pracy na właściwości magnetyczne dielektromagnetyków

Janta T.

Maszyny Elektryczne : zeszyty problemowe

|

2006

|

Nr 75

171-175

EN

Magnetic powder composites find ever-wider use as active magnetic materials for magnetic cores of electric devices. Special interest is focused on dielectromagnetics. They are powder composites made from soft magnetic powder with an admixture of, dielectric in the form of resins, which both bind and isolate the soft magnetic particles. The properties of manufactured dielectromagnetics and their constancy over time is one of the main factors, which determine the use of these materials. When the factors are examined and understood, it will become possible to design magnetic cores in such a way that the predictable changes in their properties will not disqualify the electric devices in the course of their service. In this paper changes in the magnetic properties of dielectromagnetics caused by working temperature are described. The magnetic properties of dielectromagnetics of the specimens were tested after they were stored one year in ambient conditions at a constant temperature of 100°C and (comparative series) at a constant temperature of 21°C and a constant humidity of 50%. The research has shown that the effect of working temperature on the magnetic properties of the tested dielectromagnetics is small and profitable. This is a proof of the high quality of the soft magnetic powder used whose properties remain stable over temperature.

5

Wpływ temperatury pracy na stratność dielektromagnetyków

Janta T.

Kompozyty

|

2006

|

R. 6, nr 4

62-65

PL

Magnetyczne kompozyty proszkowe znajdują coraz szersze zastosowanie jako materiały magnetycznie czynne magnetowodów urządzeń elektrycznych. Ze względu na właściwości oraz prostą technologię szczególnym zainteresowaniem cieszą się dielektromagnetyki. Są to kompozyty proszkowe wykonywane z proszku magnetycznie miękkiego z zastosowaniem, oprócz innych domieszek, dielektryku stanowiącego najczęściej zarówno środek izolujący, jak i wiążący cząstki magnetycznie miękkie. W zastosowaniu tych materiałów istotna jest stałość parametrów magnetycznych i elektrycznych w czasie ich pracy oraz ich niezmienność pod wpływem warunków otoczenia (np. temperatury, wilgotności). Poznanie zmian pozwoli na odpowiednią korektę przy projektowaniu magnetowodów tak, aby zmiany te nie dyskwalifikowały urządzeń w trakcie ich eksploatacji. Zmiany zależą, miedzy innymi, od zastosowanej technologii, rodzaju zastosowanego proszku magnetycznie miękkiego, ilości i rodzaju użytego dielektryku, ilości i rodzaju ewentualnych domieszek i, w końcu, od czynnika narażającego. Wpływ ten znajduje swoje odzwierciedlenie w zmianie różnych właściwości, w tym właściwości magnetycznych, elektrycznych czy też mechanicznych. Stąd zależności te są trudne do jednoznacznego zbadania i opisania. Określono wpływ temperatury pracy magnetowodów wykonanych z dielektromagnetyków na ich stratność. Badane dielektromagnetyki znajdowały się w temperaturze 100°C przez 1 rok. Ich stratność porównano ze stratnością dielektromagnetyków przechowywanych przez ten sam czas w stałej temperaturze otoczenia 21°C oraz stałej wilgotności wynoszącej 55%. Zbadano dielektromagnetyki wykonane z proszku magnetycznie miękkiego ASC 100.29 domieszkowanego żywicą epoksydową Epidian 101 w ilości 0,1 oraz 0,2% wagowo. Schemat blokowy komputerowego systemu pomiarowego przedstawiono na rysunku 1. Zmierzone wartości stratości całkowitej oraz jej składowych: stratności z histerezy oraz z prądów wirowych przedstawiono w tabelach 1 i 2 oraz na rysunkach 2-4. Wykazano, że wpływ temperatury pracy dielektromagnetyków na ich stratność jest mały i korzystny z punktu widzenia ich zastosowania na magnetowody urządzeń elektrycznych - stratność całkowita maleje o około 1%. Świadczy to niewątpliwie o dobrej jakości zastosowanego proszku magnetycznie miękkiego, którego właściwości są stabilne w czasie oraz o wystarczającej, ochronnej warstwie cząstek żelaza wytworzonej przez zastosowany dielektryk.

EN

Magnetic powder composites find ever-wider use as active magnetic materials for magnetic cores of electric devices. Because of their properties and manufacturing technology, dielectromagnetics attract a great interest. They are powder composites made from soft magnetic powder with an admixture of, among others, dielectric in the form of resins, which both bind and isolate the soft magnetic particles. The properties of manufactured dielectromagnetics and their constancy over time as well as the influence of the operating conditions (e.g. temperature) or the medium (e.g. humidity) on them are the main factors, which determine the use of these materials. When the factors are examined and understood, it will become possible to design magnetic cores in such a way that the predictable changes in their properties will not disqualify the electric devices in the course of their service. In this paper changes in the lossiness of dielectromagnetics, made of soft magnetic powder ASC 100.29 with an admixture of epoxy resin Epidian 101 in the amount of 0.1 and 0.2% by weight, caused by working temperature are described. Dielectromagnetics for tests were compacted in form of ring samples with dimensions 50x60x5 mm. Applied compacted pressure was 800 MPa. Samples were cured at temperature 200°C in the resistance furnace in the course of 1 hour. The lossiness of dielectromagnetics of the specimens were tested after they were stored one year in ambient conditions at a constant temperature of 100°C and (comparative series) at a constant temperature of 21°C and a constant humidity of 50%. Block diagram of the computer system for lossiness measurements is presented in Figure 1. The density and total lossiness of tested dielectromagnetics at induction 0.5 T and 1 T for frequencies 50 Hz are shown in Table 1 and in Figure 2 (at B = 1 T). Distribution of lossiness for frequencies 50 Hz are presented in Table 2 and in Figures 3 and 4. Values of eddy current loss are very small, about 3% of hysteresis loss (Table 2). The research has shown that they increase by 14% (Fig. 4) does not essentially effect on total lossiness (Fig. 2). The effect of working temperature on the lossiness of the tested dielectromagnetics is small and profitable - the total lossiness decreased about 1% (Table 1, Fig. 2). This is a proof of the high quality of the soft magnetic powder and dielectric used whose properties remain stable over temperature.

6

Wpływ rodzaju i zawartości dielektryku na właściwości dielektromagnetyków

Gaworska D., Węgliński B., Szafran M., Wiśniewski P.

Kompozyty

|

2005

|

R. 5, nr 1

46-50

PL

Dielektromagnetyki są kompozytami proszkowymi, które znajdują coraz szersze zastosowanie jako magnetowody urządzeń elektrycznych. W pracy zaprezentowano podstawowe właściwości dielektromagnetyków wykonanych przy użyciu nowych rodzajów dielektryków, jak np. kompozycje: szkła wodnego i NaOH, Glifosu i NaH2PO4 oraz szkła wodnego i NaH2PO4, a także spoiwa: dyspersja Tarflenowa, dyspersja poli(akrylowo-styrenowa), emulsja poli(winylobutyralu) oraz FIumix C, otrzymanych metodą prasowania z użyciem wysokich ciśnień. Badania właściwości kompozytów prowadzono w dwóch etapach: badania wstępne i badania zasadnicze. W badaniach wstępnych zawartość spoiwa w kompozytach wynosiła 5%. W etapie zasadniczym ilość spoiwa w kompozytach proszkowych zmniejszono do 1% wag. w stosunku do proszku żelaza w celu zbadania wpływu zawartości składników na właściwości magnetowodów. Badania magnetyczne wykonano na próbkach toroidalnych o wymiarach [phi]60[phi] 50x5 mm otrzymanych w procesie prasowania ciśnieniem 800 MPa. W badaniach wstępnych wypraski, w zależności od zastosowanego spoiwa, wygrzewano w temperaturze 200°C/0,5 h (próbki PUB-5%, DT-5%, PAS-5%), 600°C/0,5 h (próbki SWNa-5%, PF-5%, Glifos-5%, FLC-5%, SP-Glifos-5%, SPNa-5%). Na podstawie wstępnych badań magnetycznych kompozytów (rys. rys. 1 i 2) do dalszych badań wybrano SWNa, Glifos i SPNa. Następnie wybrane próbki poddano kolejnej obróbce cieplnej w temperaturze 800° C/1 h w celu sprawdzenia wytrzymałości termicznej spoiwa. Niestety zaobserwowano duży wzrost stratności całkowitej badanych próbek, co świadczy o zniszczeniu właściwości dielektrycznych spoiwa na skutek działania zbyt wysokiej temperatury (rys. 2). W badaniach zasadniczych wypraski wygrzewano w temperaturze 5OO°C/0,5 h (próbki SWNa-1%, Glifos-1%, SPNa-1%) i poddano badaniom magnetycznym. Wyniki tych badań przedstawiono na rysunkach 3-7. Zmniejszenie ilości spoiwa wpłynęło na poprawę właściwości magnetycznych kompozytów (rys. rys. 5 i 6). Badania wykazały, że rodzaj i ilość zastosowanego spoiwa ma wpływ na właściwości dielektromagnetyków, a najkorzystniejszymi właściwościami cechował się kompozyt SPNa-1%, charakteryzujący się najniższą stratnością (rys. 7).

EN

Dielectromagnetics are powder composites which are more and more widely used as magnetic cores for electric devices. The paper present basic parameters of dielectromagnetics obtained by employment of new kinds of dielectrics i.e. compositions: water-glass-NaOH, Glifos-NaH2PO4, water-glass-NaH2PO4; and binders: ,,Tarflen" dispersion, poly(acrylic-styrene) dispersion, poly(vinyl-buthyral) emulsion and Flumix C, obtained as the result of die pressing under high value pressure values. Studies on parameters of the composites were conducted in two stages: initial tests and core tests. In initial tests the binder content was equal 5 wt.%. In core tests, binder content was decreased to 1 wt.% in relation to the iron powder in order to investigate the influence of the components' amount on the properties of magnetic cores. Magnetic tests were conducted on ring samples with dimensions [phi]60[phi]50x5 mm, which were obtained using die pressing method under 800 MPa. In initial tests the samples were heated in temperature of 200°C/0.5 h (samples PUB-5%, DT-5%, PAS-5%), 600°C/0.5 h (samples SWNa-5%, PF-5%, Glifos-5%, FLC-5%, SP-Glifos-5%, SPNa-5%), depending on the kind of binder used. The initial magnetic tests of composites (Figs 1, 2) resulted in a selection of only the SWNa, Glifos and SPNa samples for further research. Subsequently, samples were heated in 800°C/1 h in order to check thermal strength of the binder and of the dielectric. Unfortunatelly, high increase of total energy loss was observed, what indicated that insulating properties of the binder had been annihilated because of the influence of high temperature (Fig. 2). In core tests, samples were heated at 500°C/0.5 h (SWNa-1%, Glifos-1%, SPNa-1%) and they later underwent magnetic tests. Reduction the binder's amount results in better magnetic parameters (Figs 5, 6). The research shows that the kind of the binder used and its amount has an effect on dielectromagnetics' parameters and the most beneficial properties were indicated for SPNa-1 % composite, which was characterized by the lowest total energy lost (Fig. 7).

7

Zastosowanie dielektromagnetyków i dielektromagnesów w wysokoobrotowych silnikach specjalnego przeznaczenia

Ślusarek B., Szeląg W., Długiewicz L., Gromek J.

Elektronika : konstrukcje, technologie, zastosowania

|

2005

|

Vol. 46, nr 12

70-72

PL

Głównym celem prowadzonych prac było opracowanie wysokoobrotowego silnika o wzbudzeniu magnesami trwałymi, przeznaczonego do napędu turbiny gazowej z zastosowaniem proszkowych materiałów magnetycznych, zarówno magnetycznie miękkich, jak i magnetycznie twardych. Zastosowanie tego typu materiałów spowodowało konieczność opracowania nowych metod projektowania jak i technologii wytwarzania tego typu silników elektrycznych.

EN

New powder magnetic materials allow changing of design and technology of manufacturing of electric machines. Such changes simplify technology and make production process less time consuming, reducing the production costs. Combination of advantages of powder magnetic materials together with modern computational methods creates new opportunity for designers and makes possible working out modern and effective electric machines. The main goal of presented research is working out the high speed motor excited with permanent magnets designed as drive of the gas turbine joining application of both soft and hard powder magnetic materials in one electric machine.

8

Właściwości magnetyczne dielektromagnetyków w polach przemiennych i wirujących

Bajorek R., Bajorek J., Węgliński B.

Przegląd Elektrotechniczny

|

2004

|

R. 80, nr 2

172-175

PL

W artykule przedstawiono wyniki badań eksperymentalnych właściwości magnetycznych magnetowodów wykonanych z dwóch różnych dielektromagnetyków. Badania prowadzono w polach przemiennych i wirujących o częstotliwości 50Hz. Wykonano zdjęcia struktury składnikowo-fazowej próbek, które potwierdzają otrzymane wyniki badań szczególnie w przypadku znacznego wzrostu stratności.

EN

In this work research results concerning magnetic properties of magnetic cores made of two different dielectromagnetics powders were presented. The researches were conducted in alternating and rotating fields at frequency of 50Hz. Photos of specimens' componential-phase structure confirm obtained results particularly in case of significant increase in magnetic core losses.

9

Wpływ zjawisk starzeniowych na stratność dielektromagnetyków

Janta T.

Maszyny Elektryczne : zeszyty problemowe

|

2004

|

Nr 69

51-54

EN

Lately magnetic powder composites find ever wider use as active magnetic materials for magnetic cores of electric devices. Because of their proprieties and manufacturing technology, dielectromagnetics attract a great interest. They are powder composites made from soft magnetic powder with an admixture of, among others, dielectric in the form of resins which both bind and isolate the soft magnetic particles. The properties of manufactured dielectromagnetics and their constancy over time as well as the influence of the operating conditions (e.g. temperature) or the medium (e.g. humidity) on them are the main factors which determine the use of these materials. When the factors are examined and understood, it will become possible to design magnetic cores in such a way that the predictable changes in their properties will not disqualify the electric devices in the course of their service. In this paper changes in the lossiness of dielectromagnetics, made of soft magnetic powder ASC 100.29 with an admixture of epoxy resin Epidian 101 in the amount of 0.1% and 0.2% by weight, caused by ageing are described. The lossiness of dielectromagnetics of the specimens were tested twice: immediately after they were made (t=0) and one year later (t=365). The dielectromagnetics were stored in ambient conditions at a constant temperature of 21°C and a constant humidity of 50%. The research has shown that the effect of ageing phenomena on the lossiness of the tested dielectromagnetics is small, about 3%. This is a proof of the high quality of the soft magnetic powder used whose properties remain stable over time.

10

Wpływ zjawisk starzeniowych na właściwości magnetyczne kompozytów proszkowych typu dielektromagnetyk

Janta T.

Kompozyty

|

2004

|

R. 4, nr 12

384-388

PL

Magnetyczne kompozyty proszkowe znajdują ostatnio coraz szersze zastosowanie jako materiały magnetycznie czynne magnetowodów urządzeń elektrycznych. Ze względu na właściwości oraz prostą technologię szczególnym zainteresowaniem cieszą się dielektromagnetyki. Są to kompozyty proszkowe wykonywane z proszku magnetycznie miękkiego z zastosowaniem, oprócz innych domieszek, dielektryku w formie żywic, które stanowią zarówno środek wiążący, jak i izolujący cząsteczki magnetycznie miękkie. Istotna w zastosowaniu tych materiałów, oprócz właściwości po wyprodukowaniu, jest stałość tych parametrów w czasie oraz, co stanowi odrębne zagadnienie, wpływ na nie zmienionych warunków otoczenia (np. temperatury, wilgotności). Poznanie tych zależności pozwoli na ewentualną korektę przy projektowaniu magnetowodów tak, aby zachodzące zmiany właściwości dielektromagnetykow nie dyskwalifikowały urządzeń w trakcie eksploatacji. Zjawisko jest trudne do jednoznacznego zbadania i opisania ze względu na mnogość czynników je obejmujących. Zmiany zależeć bowiem mogą, między innymi, od rodzaju zastosowanego proszku magnetycznie miękkiego, ilości i rodzaju użytego dielektryku, ilości i rodzaju ewentualnych domieszek i, w końcu, od czynnika narażającego. Wpływ ten znajduje swoje odzwierciedlenie w zmianie różnych właściwości, np. właściwości magnetycznych, elektrycznych czy też mechanicznych. W pracy przedstawiono wynikające ze zjawisk starzeniowych zmiany właściwości magnetycznych dielektromagnetykow wykonanych z proszku magnetycznie miękkiego ASC 100.29 domieszkowanego żywicą epoksydową Epidian 101 w ilości 0,1 oraz 0,2% wag. Badania właściwości magnetycznych próbek przeprowadzono dwukrotnie - pierwszy raz po ich wykonaniu oraz powtórnie po upływie l roku. Między pomiarami dielektromagnetyki znajdowały się w warunkach otoczenia: w stałej temperaturze 21°C oraz stałej wilgotności wynoszącej 55%. Zmierzone wartości i przebiegi krzywej magnesowania oraz, wynikającej z niej, przenikalności magnetycznej względnej przedstawiono w tabeli l i na rysunkach 2-7. Badania wykazały, że w zakresie przedstawianych właściwości magnetycznych wpływ zjawisk starzeniowych jest praktycznie niezauważalny. Świadczy to niewątpliwie o dobrej jakości zastosowanego proszku magnetycznie miękkiego, którego właściwości są stabilne w czasie.

EN

Lately magnetic powder composites find ever wider use as active magnetic materials for magnetic cores of electric devices. Because of their proprieties and manufacturing technology, dielectromagnetics attract a great interest. They are powder composites made from soft magnetic powder with an admixture of, among others, dielectric in the form of resins which both bind and isolate the soft magnetic particles. The properties of manufactured dielectromagnetics and their constancy over time as well as the influence of the operating conditions (e.g. temperature) or the medium (e.g. humidity) on them are the main factors which determine the use of these materials. When the factors are examined and understood, it will become possible to design magnetic cores hi such a way that the predictable changes in their properties will not disqualify the electric devices in the course of their service. Since the problem is a complex one it is difficult to explore. The changes depend on, among others, the kind of magnetically soft powder, the amount and kind of dielectric, the amount and kind of admixtures and finally, on the exposure. The affected properties include magnetic, electric and mechanical properties. In this paper changes in the magnetic properties of dielectromagnetics, made of soft magnetic powder ASC 100.29 with an admixture of epoxy resin Epidian 101 in the amount of 0.1 and 0.2% by weight, caused by ageing are described. The magnetic properties of the specimens were tested twice: immediately after they were made and one year later. The dielectromagnetics were stored in ambient conditions at a constant temperature of 22°C and a constant humidity of 50%. The magnetization curve values and shapes and the corresponding relative magnetic permeabilities are shown in Table 1 and in Figures 2-7. The research has shown that the effect of ageing phenomena on the magnetic properties of the tested dielectromagnetics is practically negligible. This is a proof of the high quality of the soft magnetic powder used whose properties remain stable over tune.

11

Własności ruchowe silników indukcyjnych małej mocy z wirnikiem z materiałów kompozytowych

Antal L., Janta T.

Maszyny Elektryczne : zeszyty problemowe

|

2003

|

Nr 66

53-58

EN

Magnetic composites can be very useful for magnetic cores of electrical motors, especially because they are easy to get mass produced. Application of magnetic-conductive dielectromagnetics for rotors of induction motor is discussed. Circuit-field models of this motor are designed by using numerical calculations. Circuit-field model of a motor with such a rotor, which takes electrical coil outhang of stator and shorting rings of rotor, nonlinearity of magnetic materials, rotation of rotor and symmetrical power supply into account, and is additionally confirmed by results of tests on motor models made in practice allows working out computation for both static and dynamic machine characteristics. The compliance of results for numerical calculation and experimental tests makes it possible to apply computational model in order to seek for desired magnetic and electrical properties of the materials. Moreover, optimal dimensions of the particular layers of the two-layer rotor can be determined on that ground. The motors made of this kind of new material are not optimal. This paper confirms that magnetic-conductive layer should have higher: electric conductive, magnetic permeability and magnetic saturation.

12

Dielektromagnetyki Fe-Cu i możliwość ich zastosowania na magnetowód wirnika silnika indukcyjnego

Janta T.

Zeszyty Naukowe. Elektryka / Politechnika Śląska

|

2001

|

z. 176

145-152

PL

Celem pracy jest przedstawienie wyników badań właściwości dielektromagnetyków magnetyczno-przewodzących Fe-Cu oraz przeprowadzonej praktycznej weryfikacji możliwości ich zastosowania na magnetowody wirników silników indukcyjnych. Właściwości dielektromagnetyków zmierzono na znormalizowanych próbkach pierścieniowych. W celu zastosowania zbadanych dielektromagnetyków Fe-Cu na magnetowód wirnika trójfazowego silnika indukcyjnego małej mocy opracowano i przedstawiono jego technologię. Magnetowód wykonano jako dwuwarstwowy. Warstwa wewnętrzna to magnetycznie miękki walec z dielektromagnetyku Fe, natomiast warstwę zewnętrzną stanowi wyprasowany na tym walcu cylinder z dielektromagnetyku magnetyczno-przewodzącego Fe-Cu. Miedź wprowadzona do mieszanki nie przechodzi w dalszym procesie technologicznym w fazę ciekłą, co umożliwia wykonanie zewnętrznej warstwy Fe-Cu o praktycznie dowolnym udziale składników. Przedstawiono wybrane charakterystyki silnika z wykonanymi wirnikami posiadającymi zewnętrzne pierścienie zwierające oraz bez tych pierścieni.

EN

The aim of this paper is to present results of tests of magnetic properties of magnetoconductive dielectromagnetics Fe-Cu and practical verification of possibilities to use them for magnetic core of induction motor rotor. Magnetic properties of the applied dielectromagnetics, including Fe-Cu dielectromagnetics, which were measured on normalized toroidal samples, are presented and described. To apply measured dielectromagnetics for magnetic core of 3-phase small power induction motor rotor elaborated and presented its technology. The core, made as two layers assembly, was tested as a rotor of a small power 3 phase induction motor. An internal part of the core is made as soft magnetic cylinder. Its materials is dielectromagnetic made of pure iron. An external layer, in form of sleeve, compacted on the internal part, is made of magnetic-conductive (Fe-Cu) dielectromagnetic. Copper applied in this part was not in liquid phase during any stage of processing, what enables manufacture of the external layers with not limited composition of its components. Chosen parameters and performance characteristics of the motor with rotors of various configurations of short-circuited rings are presented and discussed in the paper as well.