Synthesis and structure of hydroxyapatite/tannin composites

Anggresani Lia, Rahayu Aster, Perawati Santi, Yulianis Yulianis, Sintia Ulma, Setiawan Randi

Polimery

2024

Vol. 69, nr 9

484--491

Hydroxyapatite (HA)-tannin composites were obtained by precipitation using Ca(OH)2 as calcium precursor and (NH4)2HPO4 or H3PO4 as phosphate precursors, with tannin acting as a chelating agent. FT-IR confirmed the presence of functional groups derived from tannin in the composite, and XRD showed trace amounts of calcium carbonate. The crystal sizes of HA and HA/tannin were 15–27 nm and 10–29 nm, respectively. SEM showed agglomeration of HA and HA/tannin particles. The size distribution of HA particles was in the range of 0.1–0.2 μm (without tannin), and the size distribution of HA/tannin particles in the range of 0.1–0.4 μm. The obtained results confirmed the formation of strong bonds between tannin and HA.

Metodą wytrącania otrzymano kompozyty hydroksyapatytu (HA) z taniną, stosując Ca(OH)2 jako prekursor wapnia i (NH4)2HPO4 lub H3PO4 jako prekursory fosforanu, przy czym tanina pełniła rolę środka chelatującego. Analiza FT-IR potwierdziła obecność w kompozycie grup funkcyjnych pochodzących z taniny, a analiza XRD wykazała śladowe ilości węglanu wapnia. Wielkość kryształów HA i HA/tanina wynosiła odpowiednio 15–27 nm i 10–29 nm. SEM wykazało aglomerację cząstek HA i HA/tanina. Rozkład wielkości cząstek HA mieścił się w przedziale 0,1–0,2 μm (bez taniny), a rozrzut wielkości cząstek HA/tanina w przedziale 0,1–0,4 μm. Uzyskane wyniki potwierdziły tworzenie się silnych wiązań między taniną a HA.