Wyniki wyszukiwania - BazTech

1

The influence of quaternary ammonium salts on mechanical properties of light-cured resin dental composites

Zalega Maja, Nowak Joanna, Bociong Kinga

Polimery

|

2023

|

Vol. 68, nr 4

193--205

EN

The composite consisting of bis-GMA/UDMA/HEMA/TEGDMA monomer mixture forming a polymer matrix filled with silanized silica (45 wt%) was modified with CTAB or DODAB quaternary ammonium salts (0.5‒2.0 wt%). The hardness, flexural strength as well as diametrical tensile strength of the composite before and after modification were evaluated. The type and amount of salt affected the hardness, flexural strength, and shrinkage stress; however, they did not influence the diametral tensile strength of the tested composites.

PL

Kompozyt składający się z mieszaniny monomerów bis-GMA/UDMA/HEMA/TEGD¬MA tworzących osnowę polimerową napełnioną silanizowaną krzemionką (45% mas.) modyfikowano czwartorzędowymi solami amoniowymi CTAB lub DODAB (w ilości 0,5‒2,0% mas.). Zbadano twardość, wytrzymałość na zginanie oraz wytrzymałość na średnicowe rozciąganie kompozytu przed i po modyfikacji. Rodzaj i ilość soli miały wpływ na twardość, wytrzymałość na zginanie oraz naprężenia skurczowe, nie wpłynęły natomiast na wytrzymałość na średnicowe rozciąganie badanych kompozytów.

2

Physicochemical properties of the surface of light-cured dental composites after their modification with liquid rubber

Pałka Krzysztof

Engineering of Biomaterials

|

2021

|

Vol. 24, no. 163

54

3

Wpływ warunków fotopolimeryzacji na wybrane właściwości mechaniczne kompozytów stomatologicznych

Nowacka Agnieszka, Klepka Tomasz

Polimery

|

2019

|

T. 64, nr 4

272--281

PL

Badano wpływ warunków fotopolimeryzacji na wybrane właściwości mechaniczne kompozytów stomatologicznych na bazie żywicy dimetakrylanowej, o zawartości fazy nieorganicznej 22–65 % mas. Stosowano naświetlanie ciągłe i przerywane z jednorodnym i zmiennym natężeniem światła. Stwierdzono, że twardość wyznaczona metodą Shore’a oraz wartość maksymalnej siły ścinającej, a także przyczepność kompozytu do podłoża metalowego ściśle zależą od natężenia i czasu naświetlania. Z wykorzystaniem stanowiska pin-on-disc wyznaczono wartości współczynnika tarcia oraz zużycia trybologicznego badanych kompozytów stomatologicznych. Największą twardość Shore’a wykazywały kompozyty naświetlane metodą SOFT-START, a najmniejszą – naświetlane metodą ciągłą jednorodną. Największe wartości siły były generowane podczas odrywania od podłoża kompozytu naświetlanego metodą PULSE DELAY.

EN

The paper presents the results of an investigation of the effect of photopolymerization conditions on the selected mechanical properties of dental composites based on dimethacrylate resin with an inorganic phase content ranging from 22 wt % to 65 wt %. The continuous and intermittent lighting was used with uniform and variable light intensity. It was found that the Shore hardness, maximum shear force value and adhesion of the composite to the metal substrate are strongly dependent on the radiation intensity and exposure time. The tribological properties (friction coefficient and wear resistance) of dental composites were also determined using a pin-on-disc station. The highest values of Shore A hardness were measured for the composites exposed to light using SOFT-START mode, while the lowest hardness value was observed for the composite irradiated in uniform continuous mode. It was found that the highest force values were generated when the composite was exposed to light in the PULSE DELAY mode.

4

Polymerization shrinkage and compressive strength of microhybrid dental composite

Liber-Kneć Aneta, Łagan Sylwia

Engineering of Biomaterials

|

2019

|

Vol. 22, no. 153 spec. iss.

22

5

Modyfikacja światłoutwardzalnego kompozytu stomatologicznego wybranymi poliedrycznymi oligomerycznymi silseskwioksanami

Bociong K., Krasowski M., Szczesio A., Anyszka R., Kalicka K., Sokołowski J.

Polimery

|

2018

|

T. 63, nr 7-8

515--523

PL

Komercyjny światłoutwardzalny kompozyt stomatologiczny GrandioSO Flow poddano modyfikacji za pomocą wybranych poliedrycznych oligomerycznych silseskwioksanów zawierających grupy metakrylowe (M-POSS) lub akrylowe (A-POSS). Fotopolimeryzację z wykorzystaniemdiodowej lampy o mocy rzeczywistej 1400 mW/cm2 prowadzono przez 60 s w sposób ciągły z jednej strony próbki. Naprężenia generowane w wypełnieniu obliczano na podstawie wzorów teorii sprężystości. Oceniano również efektywność polimeryzacji i właściwości mechaniczne spolimeryzowanych kompozytów, m.in. średnicową wytrzymałość na rozciąganie, wytrzymałość na trójpunktowe zginanie oraz mikrotwardość metodą Vickersa. Stwierdzono, że najmniejsze naprężenia skurczowe, wynoszące ~9 MPa, generuje kompozyt zmodyfikowany dodatkiem do osnowy 2% mas. M-POSS lub 5% mas. A-POSS. Modyfikacja prowadzi także do niewielkiego zmniejszenia twardości oraz wytrzymałości na trójpunktowe zginanie, z zachowaniem właściwej dla materiału niemodyfikowanego wartośc iDTS (DTS – diametral tensile strength) w wypadku materiału zawierającego 2% mas. M-POSS. Dodatek do żywicznej osnowy 5% mas. A-POSS wpływa na pogorszenie wszystkich właściwości wytrzymałościowych, wciąż jednak pozostają one na poziomie zadowalającym i porównywalnym do właściwości dostępnych na rynku materiałów typu flow.

EN

The commercial light-curable dental composite Grandio SOFlow was subjected to modification with selected polyhedral oligomeric silsesquioxanes containing methacrylic (M-POSS) or acrylic (A-POSS) groups. Photopolymerization was carried out using LED lamp with a real power of 1400 mW/cm2 continuously for 60 s on one side of the sample.The stress generated by the filling was calculated on the basis of the elasticity theory. The polymerization efficiency and mechanical properties of polymerized composites were also evaluated, including diametral tensile strength (DTS), three-point bending strength and Vickers microhardness. It was found, that the lowest shrinkage stress of ~ 9 MPa was generated by the composite modified with 2 wt % M-POSS or 5 wt % A-POSS. The modification also leads to a slight decrease in hardness and three point flexural strength, while maintaining a comparable DTS value of a material containing 2 wt % M-POSS. In the case of modification with 5 wt % A-POSS, a decrease in all strength parameters is observed, but they still remain at a satisfactory level and are comparable to the properties of flow materials available commercially.

6

Mechanical properties of Easy Fill composites after storage in mouthwashes

Nowak M., Kalamarz I., Chladek G.

Journal of Achievements in Materials and Manufacturing Engineering

|

2018

|

Vol. 88, nr 1

25--34

EN

Purpose: The aim of the presented work was to investigate the influence of different mouthwashes on the chosen mechanical properties of different dental restorative composites. The null hypothesis was that the mouthwashes have influence on these properties. Design/methodology/approach: Four different restorative composites were used (Easy Fill Nano, Easy Fill Micro Hybrid, Easy Fill Flowable, Easy Fill Bulk). Samples were conditioned in different media: mouthwashes (Listerine Total Care with ethanol, Listerine Total Care Sensitive – alcohol-free) and distilled water. The samples were polymerized in Teflon moulds. The compressive strength, diametral tensile strength (DTS) and Vickers microhardness were examined. Findings: The research showed that the surface of composite materials was particularly sensitive to the action of mouthwashes. Both types of solutions, containing ethanol and without it lowered the microhardness values. The mouthwashes may also decrease other mechanical properties, like compressive strength of diametrical tensile strength. The results of the carried out investigations showed good mechanical properties of the tested materials, analogous to other materials of this type. Research limitations/implications: Other important properties of dental filling storied in mouthwashes should be analysed in future, including microgap between tooth and filling. Practical implications: The result contradicts the popular view that mouthwashes that do not contain ethanol are in general safer for composites in the context of reduction of mechanical properties. Both types of mouthwashes may reduce mechanical properties. Originality/value: The results of mechanical properties investigations of Easy Fill composites were presented and compared to other commercial materials. The changes of mechanical properties were also analysed after storing in different types of mouthwashes. So far, there has been no such research for these materials.

7

Wybrane właściwości mechaniczne eksperymentalnego kompozytu stomatologicznego. Cz. 1

Bociong K., Nowak J., Szczesio A., Sokołowski K., Sokołowski J.

Przemysł Chemiczny

|

2017

|

T. 96, nr 6

1360--1363

PL

Zbadano wybrane właściwości mechaniczne eksperymentalnego kompozytu stomatologicznego, przed i po jego modyfikacji wybranymi monomerami dimetakrylowymi. Badania uwzględniały ocenę mikrotwardości, średnicowej wytrzymałości na rozciąganie oraz wytrzymałości na zginanie. Kompozyt eksperymentalny charakteryzuje się zadowalającymi właściwościami mechanicznymi, biorąc pod uwagę niewielką zawartość napełniacza, porównywalnymi do niektórych materiałów typu flow. Wprowadzenie monomerów dimetakrylanowych do matrycy kompozytu stomatologicznego powoduje zmiany właściwości mechanicznych tylko w niewielkim stopniu.

EN

An expt. dental composite based on dimethacrylate resins and silanized SiO₂ was modified by addn. of 1,6-hexanediol or diurethane dimethacrylates, photocured (14000 mW/cm2) for 10 or 20 s (1 mm) and studied for micro-hardness, diam., tensile strength and tree-point bending strength. The modified composite showed satisfying mech. properties comparable to some com. flow materials. A slight decrease in mech. properties was however obsd.

8

The modification of dental resin composite using selected dimethacrylate monomers

Bociong K., Rylska D., Sokołowski J.

Inżynieria Materiałowa

|

2017

|

Vol. 38, nr 1

46--50

EN

The use of dimethacrylate resin composite in dentistry involves the potential of shrinkage and then stress contraction. This leads in consequence to defects and even secondary caries. The aim of this study was to modify the commercial resin-based composite using selected monomers and to assess the influence of such additives on polymerization stress and bulk mechanical properties. The polymer matrix was modify due to implementation monomers with differentiated chemical constitution. Stresses generated by the filling were calculated on the basis of the theory of elasticity patterns. The depth of cure and microhardness was evaluated as well. On the basis of measurements, it has been found that stress could be reduced even up to a half when composite is chemical modified by adding not less than 0.25 wt % of 1,6-hexanediol dimethacrylate or diurethane dimethacrylate.

PL

Celem pracy była modyfikacja uniwersalnego materiału nanohybrydowego z wykorzystaniem monomerów dimetakrylanowych o zróżnicowanej budowie chemicznej i różnym ciężarze cząsteczkowym oraz ocena wpływu przeprowadzonej modyfikacji na naprężenia skurczowe generowane podczas naświetlania kompozytu.

9

Polymerization shrinkage of dental composites

Pałka K., Zaszczyńska A., Kleczewska J.

Engineering of Biomaterials

|

2017

|

Vol. 20, no. 143 spec. iss.

62

10

Wpływ metody fotopolimeryzacji kompozytów stomatologicznych na bazie żywic dimetakrylanowych na naprężenia skurczowe oraz wybrane właściwości utwardzonego materiału

Bociong K., Krasowski M., Domarecka M., Sokołowski J.

Polimery

|

2016

|

T. 61, nr 7-8

499--508

PL

Materiały kompozytowe na bazie żywic dimetakrylanowych, stosowane w stomatologii zachowawczej, polimeryzowano różnymi metodami za pomocą światła o różnej gęstości mocy. Analizowano wpływ sposobu naświetlania kompozytu na powstające w materiale naprężenia skurczowe oraz wybrane właściwości utwardzonego kompozytu. Próbki naświetlano z jednej strony w sposób: ciągły, przerywany, z zastosowaniem metody soft-start lub pulse delay. Oceniono efektywność polimeryzacji, średnicową wytrzymałość na rozciąganie (DTS) oraz mikrotwardość Vickersa (HV) badanych kompozytów. Stwierdzono, że najmniejsze naprężenia skurczowe są generowane podczas naświetlania kompozytu w sposób konwencjonalny (naświetlanie ciągłe) oraz metodą pulse delay, natomiast największe naprężenia skurczowe występują w materiale naświetlanym w sposób przerywany. Ponadto kompozyt naświetlany metodą pulse delay charakteryzuje się największą twardością HV1. Nie stwierdzono statystycznie istotnych różnic między DTS próbek polimeryzowanych w różny sposób. Niezależnie od czasu i warunków naświetlania kompozytów stopień konwersji jest zadowalający i wynosi nie mniej niż 65%.

EN

The composite materials used in conservative dentistry were obtained through polymerization of dimethacrylate resins by light with different power density. The effects of composite irradiation method on the shrinkage stresses induced in the material and selected properties of the cured product were analyzed. The polymerization was carried out for 60 s irradiating the sample from one side continuously, intermittently (after every 20 sec exposure the samples were conditioned for 5 min), by using the "soft-start” method (10s at 200 mW/cm2, 5 s at 200–1400 mW/cm2, remaining time at 1400 mW/cm2) or "pulse delay” method (2 s at 200mW/cm2, 2 min break, 58 s at 1400 mW/cm2). The efficiency of polymerization, diametral tensile strength (DTS) and Vickers microhardness (HV) of the composites were evaluated. It was found that the smallest stresses are generated during the irradiation of the composite in aconventional way (continuous exposure) and using "pulse delay” method. The largest stresses occur in the material irradiated in an intermittent way. The composite irradiated using "pulse delay” method has the highest hardness HV1. There are no statistically significant differences between DTS of the differently polymerized samples. Regardless of how long and by what method the composites were cured their degree of conversion was satisfactory and not lower than 65%.

11

Polymerization shrinkage of new flow-type dental composite using micro-CT

Pałka K., Zaszczyńska A., Kleczewska J.

Engineering of Biomaterials

|

2016

|

Vol. 19, no. 138 spec. iss.

75

12

In vitro evaluation of selected properties of new flow-type dental composite

Pałka K., Wysocka S., Belcarz A.

Engineering of Biomaterials

|

2016

|

Vol. 19, no. 138 spec. iss.

74

13

Probabilistic model for flexural strength of dental composites used in modeling reliability of the “tooth-dental composite” system

Bartnik G., Pieniak D., Niewczas A. M., Marciniak A.

Eksploatacja i Niezawodność

|

2016

|

Vol. 18, no. 1

136--141

EN

In the article the application of Bayesian probabilistic modeling was presented as a way to standardize analytics of measurement results, which completes the operational and procedural standardization of determining the strength of dental composites. The traditional way of conducting studies of strength performed as services and calculations, and which do not refer to previous studies, was changed into an adaptation process of knowledge accumulation in a form of an increasing precise models. Probabilistic flexural strength models were used to create a reliability ranking of studied dental composites. Conceptualization of reliability of a biotechnological system, such as a “tooth-dental composite” required the expansion of the notion of“failure” with random events involving the occurrence of compatibility failure.

PL

W pracy przedstawiono zastosowanie bayesowskiego modelowania probabilistycznego jako sposobu standaryzacji opracowania wyników pomiarów, uzupełniającego standaryzację operatorowo – proceduralną wyznaczania wytrzymałości kompozytów stomatologicznych. Tradycyjny sposób prowadzenia badań wytrzymałościowych, wykonywanych usługowo i obliczeniowo nienawiązujących do badań poprzednich, zmieniono w adaptacyjny proces kumulacji wiedzy w postaci coraz dokładniejszych modeli. Probabilistyczne modele wytrzymałości na zginanie wykorzystano do utworzenia rankingu niezawodnościowego badanych kompozytów stomatologicznych. Konceptualizacja niezawodności układów biotechnologicznych takich jak „ząb – wypełnienie stomatologiczne” wymagała rozszerzenia zakresu pojęcia uszkodzenie o losowe zdarzenia polegające na zaistnieniu niezgodności pomiędzy komponentami układu biotechnologicznego (compability failure).

14

Comparative study of wear resistance of the composite with microhybrid structure and nanocomposite

Pieniak D., Walczak A., Niewczas A. M.

Acta Mechanica et Automatica

|

2016

|

Vol. 10, no. 4

306--309

EN

The aim of the study was to compare microhardness and wear resistance of ceramic-polymer composites with micro and nanohybrid structure. For the studies commercial composites were used, containing filler particles of the same type but different sizes, nanosized (Filtek Ultimate) and micro-sized (Filtek Z250) composites. Tribological testing was conducted using ball-on-disc micro-tribometer. Vickers testing method was applied for microhardness studies with the use of Futertech FM 700 device. It has been demonstrated that the wear of Filtek Ultimate is almost twice lower in comparison to wear of Filtek Z250 composite. It has been concluded that the use of filler nanoparticles significantly increased wear resistance of the material. Additionally, lack of correlation between material microhardness and wear resistance has been demonstrated.

15

Study of ceramic-polymer composites reliability based on the bending strength test

Walczak A., Pieniak D., Niewczas A., Niewczas A. M., Kordos P.

Journal of KONBiN

|

2015

|

No. 3 (35)

169--178

EN

In this paper the reliability assessment of structural reliability of the selected light-cured dental composites based on the biaxial flexural strength test results has been presented. A two-parameter Weibull distribution was applied as a reliability model in order to estimate probability of strength maintenance in the analysed population. Weibull distribution parameters were interpreted as a characteristic material strength (scale parameter) and structural reliability parameter in terms of ability to maintain strength by each of specimen from the general population (shape parameter). 20 composite specimens underwent strength tests, including 2 "flow" type composites and 2 standard composites (with typical filler content). "Flow" type composites were characterized with lower characteristic strength and higher structural reliability comparing to other studied composites.

PL

W artykule przedstawiono ocenę niezawodności strukturalnej wybranych światłoutwardzalnych kompozytów stomatologicznych na podstawie wyników testu wytrzymałości na zginanie dwuosiowe. Wykorzystano dwuparametrowy rozkład Weibull’a jako model niezawodności w celu oszacowania prawdopodobieństwa zachowania wytrzymałości materiału w analizowanej populacji. Parametry rozkładu Weibull’a interpretowano jako wytrzymałość charakterystyczną materiału (parametr skali) oraz wskaźnik niezawodności strukturalnej w sensie zdolności do zachowania charakterystycznej wytrzymałości przez każdy z egzemplarzy populacji generalnej (parametr kształtu). Próbie wytrzymałościowej poddano po 20 próbek kompozytów, w tym 2 kompozyty typu ,,flow” oraz 2 kompozyty standardowe (z typową ilością wypełniacza). Kompozyty typu ,,flow” charakteryzowały się niższą wytrzymałością charakterystyczną oraz wyższą niezawodnością strukturalną w porównaniu z pozostałymi badanymi kompozytami.

16

Badania wytrzymałości na ściskanie fotoreaktywnych wypełnień stomatologicznych utwardzanych światłem widzialnym

Świderski W., Czech Z., Malara P.

Przemysł Chemiczny

|

2014

|

T. 93, nr 12

2214-2217

PL

Utwardzano kompozyty stomatologiczne na bazie żywic epoksydowych, uretano-akrylanowych oraz akrylanowych zawierających oligomer 2,2-bis[4(2-hydroksy-3-metakryloglicerylo)fenolowy], dimetakrylan uretanowy, wielofunkcyjny akrylan, fotoinicjator kamforochinon oraz koinicjator 4-dimetylo-aminobenzoesan etylu, stosując światło widzialne emitowane przez polimeryzacyjną lampę LED. Jako napełniacz zastosowano hydroksyapatyt. Przeprowadzono badania wytrzymałości na ściskanie badanych fotoreaktywnych kompozytów stomatologicznych, porównując je z wytrzymałością utwardzanych światłem widzialnym wybranych komercyjnych kompozytów stomatologicznych.

EN

Oligomeric 2,2-bis[4(2-hydroxy-3-methacrylglyceril)phenol] Bis-GMA, an urethane dimethacrylate, a multifunctional acrylat, camphoroquinone photoinitiator and Et 4-dimetyl-aminobenzoate co-initiator were compounded and cured by using visible light from a light-emitting diode. Hydroxyapatite was used as a filler. The photoreactive dental composites were studied for compression strength by a std. method. The composites were as good as com. ones.

17

The influence of light curing parameters on wear resistance of selected resin-based dental composites

Malara P., Czech Z., Świderski W.

Journal of Achievements in Materials and Manufacturing Engineering

|

2014

|

Vol. 64, nr 2

62--71

EN

Purpose: The aim of the work was to test influence of curing time and distance of the light source on wear resistance of composite dental materials. Design/methodology/approach: The following study provides an insight into factors influencing wear resistance of composite materials. Standardized samples were made of methacrylate-based material Herculite XRV and silorane-based material Filtek Silorane and were tested using two types of Light Curing Units (LCUs) – halogen and LED. The distance of light source and time of curing differed between samples. Findings: Filtek Silorane composite compared to Herculite XRV composite guarantees higher wear resistance, regardless of the used LCU type. Using LED LCU compared to halogen LCU allows to obtain higher wear resistance both for Herculite XRV and Filtek Silorane composite. The lower the distance of light source the higher the wear resistance of composite material. Research limitations/implications: Further studies will provide additional information on other properties such as compressive strength, and degree of conversion. Practical implications: This article shows important comparison between older and newer composite technology. It provides practical information on polymerization methods. Originality/value: Article shows broad spectrum of different curing methods, important to the composite material use in dentistry.

18

Zastosowanie obróbki tribochemicznej do poprawy połączenia kompozyt-kompozyt uzyskanego podczas naprawy wypełnień

Sokołowski K., Sokołowska A., Szynkowska M. I., Domarecka M., Rylska D., Sokołowski J.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 6

881--884

PL

W celu uzyskania połączenia materiałów kompozytowych podczas naprawy wypełnień jest konieczne odpowiednie przygotowanie ich powierzchni, umożliwiające wytworzenie tak mikromechanicznego, jak i chemicznego połączenia. Starzenie się matrycy polimerowej z upływem czasu stwarza ograniczone możliwości uzyskania połączeń chemicznych. Rozwiązaniem problemu może być zastosowanie obróbki tribochemicznej w połączeniu z silanizacją powierzchni, zapewniającej oprócz mechanicznego także chemiczne połączenia materiałów kompozytowych. Celem pracy była ocena wpływu obróbki tribochemicznej na wytrzymałość połączenia materiałów kompozytowych z wcześniej spolimeryzowanym kompozytem. Badania przeprowadzono na próbkach mikrohybrydowego materiału kompozytowego Spectrum TPH3/Dentsply, poddanych procesowi starzenia obejmującego przechowywanie w atmosferze powietrza przez 24 miesiące. Następnie próbki szlifowano na mokro papierami ściernymi 500C i po osuszeniu powietrzem poddano obróbce tribochemicznej. Obróbka obejmowała wstępne piaskowanie korundem 110 μm (Rocatec Pre) i końcowe korundem 110 μm modyfikowanym krzemionką (Rocatec Plus), a następnie aplikację silanu. Próbki grup kontrolnych piaskowano korundem 110 μm oraz 50 μm i silanizowano. Na powierzchnię obydwu grup aplikowano i polimeryzowano system wiążący oraz materiał kompozytowy. Wytrzymałość połączenia materiałów badano w próbie ścinania za pomocą urządzenia Zwick Z020Zwick-Rooel. Dodatkowo w badaniach mikroskopowych (SEM-EDS) oceniono strukturę powierzchni próbek kompozytu i skład chemiczny. Zastosowanie obróbki tribochemicznej umożliwia rozwinięcie powierzchni i zapewnia uzyskanie wytrzymałości połączenia kompozyt-kompozyt porównywalnej z obróbką strumieniowo-ścierną korundem 110 μm bądź 50 μm.

EN

The appropriate preparation of the composite surface can guarantee micromechanical and chemical bond between dental composites during repair of resin restoration. The polymer matrix aging leads to lower capability of creating chemical bond. The application of tribochemical process, together with silanization, that provide both chemical and micromechanical bond between dental composites, might be an option. The aim of this study was to evaluate the influence of tribochemical process on the bond strength between dental composites and previously polymerized composite. Research was conducted on speciments of microhybrid dental composite Spectrum TPH3/Dentsply, that had undergone aging process (24 months storage in air). Samples were subsequently wet-polished with 500C abrasive paper, dried with air and treated with tribochemical process. Process included initial sandblasting with 110 μm corundum (Rocatec Pre) and final sandblasting with 110 μm silica-modified corundum (Rocatec Plus) and silane application. Samples from control groups were sandblasted with 110 μm and 50 μm corundum and silanized. All samples were covered with bonding system and dental composite, that were polymerized. Bond strength was evaluated in shear test, using Zwick Z005/Zwizk-Roel testing device. Surface structure and chemical composition was evaluated using SEM-EDS. The application of tribochemical process allows for surface development and provides composite-composite bond comparable to sandblasting with 50 μm or 110 μm corundum.

19

Wpływ sposobu wypełniania ubytku na naprężenia skurczowe indukowane przez materiały kompozytowe typu bulkfill

Sokołowska A., Jaroniek M., Domarecka M., Sokołowski K., Szynkowska M. I., Sokołowski J.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 5

538--541

PL

Przyczyną niepowodzeń klinicznych przy wykonywaniu wypełnień kompozytowych są głównie naprężenia skurczowe polimeryzującego materiału. Jedną z metod ograniczenia naprężeń indukowanych na granicy wypełnień i tkanek zębów są techniki warstwowej polimeryzacji wypełnień. W ostatnich latach zostały wprowadzone materiały typu bulkﬁll, kompozyty o zmienionych właściwościach, zmodyfikowanej transmisji światła i zmienionym układzie katalitycznym, przystosowane do wypełniania ubytku w grubych, 4 mm warstwach materiału. Przy braku informacji o ich właściwościach zachodzi konieczność oceny naprężeń skurczowych tych materiałów w zależności od sposobu ich aplikacji, co pozwoli na rzeczywistą ocenę wartości lansowanej ostatnio techniki wypełniania ubytków bulkﬁll w porównaniu z tradycyjnymi, warstwowymi technikami aplikacji i polimeryzacji materiałów. W pracy określono wielkości naprężeń skurczowych indukowanych podczas polimeryzacji przez materiały kompozytowe typu bulkﬁll w porównaniu z materiałami tradycyjnymi w zależności od sposobu wypełniania ubytku (technika bulkﬁll, polimeryzacja warstwowa z wykorzystaniem warstw poziomych i skośnych). Przeprowadzono elastooptyczne pomiary wielkości naprężeń zredukowanych w badaniach na płytkach z optycznie czułej żywicy epoksydowej oraz analizę stanu naprężeń wokół wykonanych wypełnień. Pomiary przeprowadzono za pomocą polaryskopu kołowego FL200/Gunt, wykorzystując do analizy program komputerowy ACD-System oraz metody analizy matematycznej. Materiały o tradycyjnym składzie matrycy polimerowej indukowały większe naprężenia skurczowe od materiałów typu bulkﬁll i obserwowano istotne zmniejszanie się naprężeń dla aplikacji warstwowej poziomej (średnie naprężenia) i skośnej (najmniejsze naprężenia). Materiały typu bulkﬁll indukowały mniej sze naprężenia, a dla materiału Tetric Evo Ceram Bulk Fill nie wykazano wpływu sposobu aplikacji na wielkość naprężeń skurczowych.

EN

The reason for clinical failure after appllication of composite restorations is, at most, the phenomenon of shrinkage stresses, occuring during polymerization of dental composites. Among the methods of reducing the stresses, induced on the margin of restoration and tooth hard tissues, are multilayer polymerization techniques. However, in recent years new bulkﬁll dental composites, with changed properties, different cathalitic system and modiﬁed light transmission, adjusted to fill cavities in layers up to 4 mm thick, were released. With the lack of information on their properties, evaluation of shrinkage stresses due to the methods of application is necessary. It should provide the assessment of the real value of bulkﬁll application method in comparison to multilayer application and polymerization techniques. In this research, quantities of shrinkage stresses of various bulkﬁll dental composites in comparison to traditional composites during polymerization were measured in dependance to application method (bulkﬁll, multilayer technique including horizontal and oblique layers). In photoelastic research with use ofplates made of photoelastic sensitive epoxy resin, measurements of reduced stresses quantities and analysis of stresses condition around restorations were made. Measurements were conducted with use of FL200/Gunt circular polariscope, ACD-System software for computer analysis and various methods of mathematical analysis. Materials of traditional matrix compound induced higher stresses than bulkfill dental composites, signiﬁcantly lower stresses for horizontal layers application method (average stresses) and oblique layers application method (lowest stresses) were also obseryed. Bulkﬁll dental composites induced lower stresses, for Tetric Evo Ceram Bulk Fill composite no impact of application method on shrinkage stresses was showed.

20

Wpływ czasu i warunków polimeryzacji na właściwości kompozytów dentystycznych

Bociong K., Sokołowski J., Rylska D.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 5

430--433

PL

Na właściwości kompozytów dentystycznych oprócz struktury chemicznej i właściwości matrycy polimerowej, zawartości fotoinicjatorów oraz wypełniaczy istotnie wpływa sposób prowadzenia polimeryzacji. Dysponując materiałem o składzie ustalonym obligatoryjnie, jego właściwości można projektować, prowadząc polimeryzację pulsacyjną lub zmieniając czas naświetlania materiału. W pracy zbadano wpływ czasu oraz rodzaju polimeryzacji (ciągła a przerywana) na właściwości materiału Filtek Ultimate w masie i w warstwie wierzchniej. Badania uwzględniały ocenę twardości, mikrotwardości, średnicowej wytrzymałości na ściskanie oraz oszacowanie stopnia konwersji. Strukturę materiału scharakteryzowano metodą skaningowej mikroskopii elektronowej Z użyciem EDS w celu oceny składu chemicznego. Otrzymane wyniki sugerują, że zmienny czas naświetlania kompozytów dentystycznych na bazie żywic dimetakrylanowych może mieć moderujący wpływ na właściwości materiału. Wydłużenie czasu polimeryzacji prowadzi do uzyskania kompozytów o większej twardości oraz średnicowej wytrzymałości na rozciąganie, jak również o większym stopniu konwersji. Niezależnie od czasu i sposobu naświetlania kompozytów stopień konwersji jest zadowalający i wynosi zawsze nie mniej niż 65%. Nie zauważono istotnych statystycznie różnic między właściwościami próbek polimeryzowanych w sposób ciągły lub przerywany. Dzięki czemu jest możliwe w sprzyjających warunkach dopolimeryzowanie próbek, tak aby osiągnąć pożądane właściwości.

EN

The properties of dental composites are dependant on both: the chemical structure and properties of the polymer matrix and the content of ﬁllers and photoinitiators and the mode of the polymerization as well. The material that composition is obligatory set its properties can be designed by changing the exposure time of the material or irradiation mode. The effect of time and the type of polymerization (continuous vs intermittent) on the properties of Filtek Ultimate was examined. Research was focused on the evaluation of hardness, microhardness, diametral tensile strength and to estimate the degree of conversion. The structure of the material were characterized by scanning electron microscopy and using EDS method to evaluate the chemical composition. The results suggest that a variable curing time and method of dental composite consist of resin imethacrylate may have a moderating effect on the properties of the material. Extension of the time of polymerization leads to composite with a higher hardness, a diametral tensile strength as well as a higher degree of conversion. Regardless of time and method of composite curing degree of conversion is satisfactory and it°s always not less than 65%. No statistically signiﬁcant differences between the properties of the samples polymerized in a continuous or intermittent way were observed.