Impact of orthodontic adhesive magnets on the mechanical properties and degree of conversion of a photopolymerized orthodontic adhesive

Al-Hayali Saud Khalil, Abed Mazin Ahmed, Al Qassar Sarmad Salih

Ochrona przed Korozją

|

2023

|

nr 10

329--334

EN

The purpose of this study was to calculate the effects of magnetic field (MF) on the degree of conversion (DC%) and mechanical properties of a photopolymerized orthodontic adhesive. In this investigation, Vega Ortho UV orthodontic adhesive was employed. The applied magnetic field had varying intensities (fixed at 0.01 T, 0.03 T, 0.05 T, 0.1 T, 0.15 T, and 0.2 T and a duration of 5 minutes) and a fixed frequency of 50 Hz. Vickers microhardness and DC% were investigated utilizing the specimens, which were created using circular molds and prepared for compression strength (CS) testing in accordance with ISO 4049. To evaluate DC% before and after MF exposure, Fourier-transform infrared spectroscopy (FTIR/ ATR) was performed. A microhardness tester was used to quantify the samples’ initial VHN while subjecting them to a 500 g load for 15 seconds. After that, properties were evaluated. With the aid of scanning electron microscopy (SEM), the surfaces were evaluated. The one-way analysis of difference and Tukey significant difference tests were used to evaluate the data. Analyses of statistical data showed that DC% tends to rise up to 0.05 T. When compared to the control, VHN and compression strength were considerably decreased after 0.03 T MF (p ≤ 0.05). However, there was a significant difference between the VHN and CS as their values increased with increasing magnetic field intensity. The surfaces of the Vega Ortho were deteriorated, as shown by SEM scans. It was found that the effect of the magnetic field caused changes in the physical and chemical properties.

PL

Celem badania było określenie wpływu pola magnetycznego (MF) na stopień konwersji (DC%) i właściwości mechaniczne fotopolimeryzowanego kleju ortodontycznego. W badaniu zastosowano klej ortodontyczny Vega Ortho UV. Zastosowane pole magnetyczne miało różne natężenia (0,01 T, 0,03 T, 0,05 T, 0,1 T, 0,15 T i 0,2 T przez 5 minut) i stałą częstotliwość 50 Hz. Mikrotwardość Vickersa i DC% ustalono z wykorzystaniem próbek, które zostały wykonane przy użyciu okrągłych form i przygotowane do badania wytrzymałości na ściskanie (CS) zgodnie z normą ISO 4049. Do oceny DC% przed ekspozycją na działanie pola magnetycznego i po niej wykorzystano spektroskopię w podczerwieni z transformacją Fouriera (FTIR/ATR). Do ilościowego określenia początkowej wartości VHN próbek użyto mikrotwardościomierza, poddając je obciążeniu 500 g przez 15 sekund. Następnie dokonano oceny właściwości. Ocenę powierzchni przeprowadzono za pomocą skaningowej mikroskopii elektronowej (SEM). Dane poddano jednokierunkowej analizie różnic i testowi istotnej różnicy Tukeya. Analizy danych statystycznych wykazały, że DC% ma tendencję do wzrostu do poziomu 0,05 T. W porównaniu z próbką kontrolną wartości VHN i wytrzymałości na ściskanie uległy znacznemu zmniejszeniu po oddziaływaniu 0,03 T MF (p ≤ 0,05). Istniała jednak znacząca różnica między VHN i CS, ponieważ ich wartości rosły wraz ze wzrostem natężenia pola magnetycznego. Powierzchnie Vega Ortho uległy degradacji, jak wykazały skany SEM. Stwierdzono, że wpływ pola magnetycznego spowodował zmiany właściwości fizykochemicznych.

2

Effects of Different Inorganic Fillers on Mechanical Properties and Degree of Conversion of Dental Resin Composites

Stencel R., Pakieła W., Barszczewska-Rybarek I., Żmudzki J., Kasperski J., Chladek G.

Archives of Metallurgy and Materials

|

2018

|

Vol. 63, iss. 3

1361--1369

EN

The aim of the study was to evaluate the influence of different fillers on the chosen functional properties of experimental composites based on typical polymeric matrix, in order to understand the effect of different fillers on their properties and to develop a simple base composite for further investigations with experimental fillers, e.g. with antimicrobial properties. Previous experiments have been usually based on commercially available composites of unknown composition or compilation of monomers, without reinforcing fillers. Scanning electron microscopy was used to investigate the quality of fillers’ dispersion, which was satisfying. Results showed significant differences between materials’ diametral tensile strength (p = 0.0019), compressive strength (p < 0.0001), Vickers microhardness (p < 0.0001), flexural modules (p = 0.0018), and the degree of conversion (p < 0.0001), but flexural strength was not significantly different (p = 0.0583). Investigations indicated that no filler type had an especially positive impact on the mechanical properties, but reinforcement effect was achieved by proper compilation of silica nanofiller and variable glass fillers. Nanofiller decreased the degree of conversion.

3

Assessment of degree of conversion of polymer-based orthodontic adhesive resins

Kuśmierczyk D., Czerwiński M., Tykarska M., Małkiewicz K.

Polimery

|

2017

|

T. 62, nr 6

466--471

EN

Degree of conversion (DC) of selected currently used orthodontic adhesive materials, after their polymerization with dental curing light, were investigated in laboratory conditions. Samples of four orthodontic adhesives (Contec LC, Transbond XT, Transbond Plus and Resilience) were prepared in Teflon matrices and then formed into the thickness of 1 mm. After the baseline measurement of crosslinking of the materials with Fourier transform infrared spectroscopy (FT-IR) the samples were cured with treatment light, and then 1 and 24 h after the completion of the photopolymerization process, the values of DC were evaluated. The results were analyzed using the Statistica 8.0 software package. In the process of hypothesis testing the level of significance was assumed at α = 0.05. The statistical analysis yielded significant differences between DC values of orthodontic adhesives tested in both time periods and a significant increase after 24 h storage of the studied orthodontic adhesive systems. It was stated that DC values of the visible light-cured orthodontic adhesives assessed in the present study depend of the type of the composite material. A significant increase in DC occurring with extended period of observation proves that polymerization of dental adhesive materials is a long-term process.

PL

Przeprowadzono w warunkach laboratoryjnych badania stopnia konwersji (DC) wybranych, stosowanych współcześnie ortodontycznych materiałów adhezyjnych po ich polimeryzacji pod wpływem światła widzialnego lampy stomatologicznej. Próbki czterech klejów ortodontycznych (Contec LC, Transbond XT, Transbond Plus i Resilience) przygotowano w teflonowych matrycach, a następnie uformowano do grubości 1 mm. Po wykonaniu za pomocą spektroskopii w podczerwieni z transformacją Fouriera (FT-IR) pomiaru początkowego usieciowania próbek, poddawano je działaniu lampy zabiegowej, a następnie po 1 i 24 h od zakończenia procesu fotopolimeryzacji wyznaczano wartości DC. Uzyskane wyniki analizowano korzystając z pakietu statystycznego Statistica 8.0. W procesie testowania hipotez statystycznych przyjęto poziom istotności α = 0,05. Analiza statystyczna wykazała istotne różnice pomiędzy wartościami DC badanych klejów ortodontycznych wyznaczonymi po upływie 1 i 24 h oraz istotny wzrost DC podczas 24-godzinnego przechowywania ocenianych próbek. Stwierdzono, że wartość DC ocenianych układów adhezyjnych polimeryzowanych światłem widzialnym zależy od rodzaju materiału. Istotny wzrost wartości DC zachodzący wraz z wydłużeniem czasu obserwacji może świadczyć o tym, że polimeryzacja stomatologicznych materiałów adhezyjnych jest procesem długotrwałym.

4

Degree of conversion of dental composite materials in relation to different light-curing parameters

Malara P., Czech Z., Świderski W.

Journal of Achievements in Materials and Manufacturing Engineering

|

2015

|

Vol. 70, nr 2

60--69

EN

Purpose: The aim of the work was determine conversion degree of composite dental materials with different resins in relation to different light-curing parameters. Design/methodology/approach: The article provides an insight on factors influencing conversion degree of composite materials. Standardized samples made of Herculite XRV based on a methacrylate resin and Filtek Silorane based on silorane resin and were cured using two types of Light Curing Units (LCUs) – halogen and LED. The samples were cured at different distances and for different times. Findings:Research has showed that the polymerization of Filtek Silorane composite is significantly slower than polymerization of Herculite XRV composite. Extending exposure time does not compensate for decrease of light intensity caused by increase of the distance of the light source from the surface of cured composite. Research limitations/implications: Further studies on degree of conversion of dental composite materials will allow to expand the knowledge on characteristics of materials used in dental clinical practice. Practical implications: Evaluation of curing methods, curing parameters and good knowledge on units used in light-curing of composite materials allow to acquire filling materials with best functional qualities. Originality/value: The paper presents degree of conversion of composite materials based on different matrixes and cured with different methods.

5

Calorimetric study of thermally-activated polymerization of urethane-dimethacrylate monomers

Barszczewska-Rybarek I.

Polish Journal of Applied Chemistry

|

2009

|

Vol. 53, nr 2

117-122

EN

The thermally activated curing behaviour of a series of urethane-dimethacrylates, derived from dicarbamatcs of oligocthylcne glycols monomethacrylates and aliphatic, cycloaliphatic and aromatic diisocyanates, were examined by differential scanning calorimetry (DSC). The effect of monomer structure on the onset (T") and peak temperatures (Tp), the degree of double bonds conversion (DC) and the activation energy (Ea) were studied. A distinct dependence of the molar mass and chemical structure of the monomer on the above parameters is seen from the collected data.

6

Wpływ wtrysku dodatkowych strumieni substratów na pracę reaktora rewersyjnego

Thullie J., Kurpas M., Bodzek M.

Inżynieria Chemiczna i Procesowa

|

2001

|

T. 22, z. 3E

1405--1410

PL

W pracy przedstawiono model reaktora rewersyjnego z wtryskiem międzystopniowym. Zastosowanie wtrysku wyraźnie obniża maksymalny wzrost temperatury w złożu obniżając równocześnie konwersję. Jednakże znaczne obniżenie maksymalnej temperatury katalizatora nie powoduje drastycznego spadku minimalnego stopnia konwersji.

EN

A model of a reverse flow reactor with an injection of cold feed was investigated. The injection caused a decrease in maximum temperature and conversion. However the decrease in maximum temperature of catalyst bed is lower than in minimum conversion.