Study of ceramic pigments with perovskite structure

Dohnalová Ż., Sulcová P., Gorodylova N.

Materiały Ceramiczne

|

2016

|

T. 68, nr 3

188--192

EN

Our attention was focused on preparation of inorganic pigments based on the perovskite structure of SrSnO3, in which part of tin ions was substituted by ions of terbium and titanium or terbium and cerium. The particle size (d50) of all pigments is between 2-3 μm. Powders with the general formula SrSn0.6-xTixTb0.4O3, where x = 0.1-0.6, provide an intensive yellow colour hue in application into an organic binder, and white glossy surfaces in application into a ceramic glaze. A SrSn0.4Ti0.2Tb0.4O3 sample offers the best colour parameters in application into the organic binder: the highest amount of yellow hue (b* = 58.95) and the highest saturation (C = 59.05). Powders with the general formula SrSn0.6-xCexTb0.4O3, where x = 0.1-0.6, also provide an intensive yellow colour hue in application into the organic binder and dark yellow-orange glossy surfaces in application into the ceramic glaze. The most interesting yellow colour hue has powder SrSn0.4Ce0.2Tb0.4O3 applied into the organic binder. In application into the ceramic glaze, an increase of cerium ions content in pigment shifts the hue from yellow to dark orange.

PL

Uwagę skupiono na przygotowaniu nieorganicznych pigmentów opartych na perowskitowej strukturze SrSnO3, w której część jonów cyny podstawiono jonami terbu i tytanu lub terbu i ceru. Rozmiar cząstek (d50) wszystkich pigmentów mieścił sie pomiędzy 2-3 μm. Proszki o wzorze ogólnym SrSn0.6-xTixTb0.4O3, gdzie x = 0.1-0.6, dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i białe połyskujące powierzchnie w zastosowaniu do szkliwa ceramicznego. Próbka SrSn0.4Ti0.2Tb0.4O3 oferuje najlepsze parametr barwne w zastosowaniu do spoiwa organicznego: największy udział odcienia żółtego (b* = 58.95) i największe nasycenie (C = 59.05). Proszki o wzorze ogólnym SrSn0.6-xCexTb0.4O3, gdzie x = 0.1-0.6, również dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i ciemne żółto-pomarańczowe powierzchnie w zastosowaniu do szkliwa ceramicznego. Najbardziej interesujący odcień koloru żółtego ma proszek SrSn0.4Ce0.2Tb0.4O3 zastosowany do spoiwa organicznego. W zastosowaniu do szkliwa ceramicznego wzrost stężenia jonów ceru w pigmencie przesuwa odcień żółty do ciemnopomarańczowego.

2

Study of compounds based on SrMxSn1-xO3šx/2

Adolfova L., Sulcova P., Dohnalova Z., Trojan M.

Materiały Ceramiczne

|

2011

|

T. 63, nr 2

248-250

EN

Inorganic pigments of SrMxSn1-xO3šx/2 type (where M = V, Cr), based on a pseudo cubic structure of SrSnO3, have been prepared by the solid state reaction between SrCO3, SnO2 and oxides V2O5 or Cr2O3 in the temperature range 1300-1500°C with nominal compositions: x = 0.05, 0.1, 0.3. The resultant materials were characterised by XRD, TG-DTA, and colourimetric techniques were used. The pigments containing vanadium as chromophore give creamy, sand and yellow colour into an organic matrix. The increase of temperature caused the creation of pigments with deeper and brighter colour hue. The presence of chromium in compounds produces colour hues from reddish brown to brown. The compounds with higher content of chromium have the lower chroma colour hue.

PL

Pigmenty nieorganiczne typu SrMxSn1-xO3šx/2 (gdzie M = V, Cr), oparte na pseudo-regularnej strukturze SrSnO3, o nominalnym składzie: x = 0,05, 0,1, 0,3, zostały przygotowane za pomocą reakcji w stanie stałym pomiędzy SrCO3, SnO2 i tlenkami V2O5 lub Cr2O3 w zakresie temperatury 1300–1500°C. Otrzymane materiały scharakteryzowano za pomocą metod XRD, TG-DTA, wykorzystano też technikę kolorymetryczną. Pigmenty zawierające wanad jako chromofor dają w organicznej matrycy kolory śmietankowy, piaskowy i żółty. Wzrost temperatury spowodował powstanie pigmentów o głębszym i jaśniejszym odcieniu. Obecność chromu w związkach wywoływała odcienie od brązowo-czerwonawego do brązowego. Związki z wyższą zawartością chromu miały odcień o mniejszym nasyceniu barwy.

3

Study on flame retardant unsaturated polyester resins - an overview of past and new developments

Kicko-Walczak E.

Polimery

|

1999

|

T. 44, nr 11-12

724-729

EN

A review over 1961-1998 with 34 refs. covering directions and results of studies on synthesis, crosslinking and modifications intended to impart flame retardancy to unsaturated polyester resins (UPR). Non-halogenated and halogenated UPR are described, characterized by medium-suppressed flammability, which continue to be marketable despite some environmental demerits. This is true of the resins retarded with tetrahalophthalate compounds and brominated diols; studies are conducted on addition of elemental bromine to double bonds in polyester resins. In addition to flame-retardant, highly lightfast resins are prepared with the aliphatic C-Br bond which, in contrast to the aromatic C-Br, is not dissociated by light rays. No-waste copolymerization of epichlorohydrin with dicarboxylic acid anhydrides is ecologically still essential. Flame retardants and smoke suppressants are grouped into groups comprising hydrated mineral fillers, phosphorus compounds, and inorganics [Sb2O3, Mg(OH)2, MoO3, SnO2, ATH, CaCO3, etc.). Mechanisms operative in flame retardancy and smoke suppression are reviewed, with particular reference to the synergi-stic action of Sb-Cl. 'Flame retardants additives' continue to be the most potent flame retardants and smoke suppressants. Aluminum trihydrate (ATH) is mass used, but is effective only at high concentrations and is now recommended for use when prepared with the bimodal particle size distribution. Mg(OH)2 is another endothermic additive, yet Ca sulfate and Zn borate are cheaper. Low-viscosity phosphoric acid esters, e.g., tris(2-chloroethyl) phosphate, tri(2,3-dibromopropyl) tricresol phosphate, etc. fail to bond with the resin and act also as plasticizers; unsaturated additives, e.g., di(2-chloroethyl) vinyl phosphonate (Stouffer's Fyrol bis-beta), can also be used as crosslinkers. A novel retardant, Great Lakes Chemical's NH-1197 (CN-1197), a bicyclic structure synthesized from pentaerithritol and a phos-phorylant, is a char-forming low-smoke fire retardant. Melamine alone or melamine phosphate and/or superphosphoric acid give satisfactory formulations. Sb2O3 can be replaced by zinc borate, 2ZnO-3B2O3-3.5H2O. Zinc oxide and boron oxide alone are char promoter and char stabilizer, respectively. Zinc hydroxystannate and zinc stannate are novel flame retardants and smoke suppressants, especially for halogenated polyester resins.

PL

Dokonano przeglądu (1961-1997, 34 ods.) dotyczącego inhibitorów płomienia i dymu stosowanych do uniepalniania nienasyconych żywic poliestrowych. Omawiane antypireny ujęto w grupy obejmujące związki chloroorganiczne, uwodnione napełniacze mineralne, związki fosforoorganiczne i związki nieorganiczne [np. Sb2O3, Mg(OH)2, MoO3, SnO2, CaC03]. Boran cynku i/lub Sb2O3 synergizują antypireny chlorowcowe (Sb:Cl < 1:3). Związki fosforu osłabiają synergizm Sb-Cl. Bezwodniki tetrachlorowcoftalowe (Cl, Br) i diole bromowane (np. glikol dibromoneopentylowy) nadal nie utraciły znaczenia, przy czym nadana przez diole odporność na światło jest trwalsza, ponieważ alifatyczne wiązania C-Br rozszczepiają się trudniej niż aromatyczne C-Br. Nowe typy chlorowanych żywic poliestrowych bazują na kopolimeryzacji epichlorochydryny z kwasami dikarboksylowymi. A12O3 o 3H2O (ATH) jest skuteczny gdy jego zawartość wynosi ok. 30% mas., lecz uzyskiwane wówczas produkty są nadmiernie lepkie i przemysłowo nieprzydatne. Natomiast ATH zmodyfikowany powierzchniowo i mający bimodalny rozkład uziarnienia jest użyteczny: nadaje odporność na korozję oraz uniepalnia i redukuje ilość dymu. Działa na zasadzie składnika endotermicznego; podobnie działa Mg(OH)2 z tym, że siarczan Ca i boran Zn są tańsze. Estry fosforowe [np. fosforan tris(2-chloroetylowy) i in.] nie wiążą się chemicznie z żywicą; działają one równocześnie jako plastyfikatory, a estry nienasycone, np. winylofosfonian di(2-chloroetylowy), jako czynniki sieciujące. Nowy antypiren NH-1197 (Great Lakes Chemical Co.) - związek dwupierścieniowy na podstawie penta-erytrytu i czynnika fosforylującego - wspomaga zwęglanie i zmniejsza wydzielanie dymu. Skutecznymi antypirenami są melamina i jej fosforan i/lub kwas superfosforowy. Boran cyrtto, 2ZnO o 3B2O3 o 5H2O, może zastąpić SfaOs. ZnO wspomaga zwęglanie, tlenek boru stabilizuje zwęgliny powstałe w wyniku pirolizy polimeru. Nowe antypireny - cynian i hy-dwksycynian cynku - uniepalniają i redukują ilość dymu.