Wyniki wyszukiwania - BazTech

1

Cyclic oxidation resistance of Co–9Al–9W new cobalt-based superalloy

Moskal Grzegorz, Tomaszewska Agnieszka, Migas Damian, Niemiec Dawid

Inżynieria Materiałowa

|

2019

|

Vol. 40, nr 2

39--45

EN

Cobalt-based superalloys are class of new heat-resistant materials for components of turbine engines. The γ/γʹ phase microstructure similar to nickel-based analogue, provide excellent creep resistance as well as resistance to corrosion and oxidation. Superior high temperature resistance drives intensive development of Co-based superalloys. The aim of paper is assessment of high temperature oxidation behaviour of Co–9Al–9W alloy in as-cast state. The cyclic oxidation performance of Co–9Al–9W alloy was studied at temperature 800°C and 900°C. The cyclic oxidation test was carried out under laboratory air atmosphere with time of exposure 25 hours and multiplicity of it. The scale morphology after cyclic oxidation test was investigated. The evaluation of scale concerned macrostructure, microstructure, chemical and phase composition of surface. Surface of tested alloys after oxidation was characterized using X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and light microscopy (LM). Obtained data revealed that Co–9Al–9W alloy showed acceptable resistance to cyclic test at temperature 800°C. The oxide scale at this variant showed mainly Co oxides as an dominant phase. At higher temperature – 900°C the strong effect of spallation of scale was observed as results of CoWO4 complex oxide formation.

PL

Celem pracy była charakterystyka odporności na utlenianie nowego typu stopów na bazie kobaltu umacnianych fazą Co3(Al, W). Ocenie poddano stop Co–9Al–9W (% at.) w stanie po odlaniu i homogenizacji. Wykonano próby odporności na utlenianie cykliczne w cyklach 25-godzinnych w atmosferze powietrza. Zakres prezentowanych badań obejmował pomiary masy próbek po kolejnych cyklach, ocenę stanu powierzchni z uwzględnieniem procesów jej odpadania, jak również charakterystykę składu chemicznego i fazowego powstałej zgorzeliny oraz jej budowę morfologiczną.

2

Struktura i wybrane właściwości użytkowe powłok Ni-Cr na podłożach ze stopu TiAINb

Godlewska E., Mania R., Mitoraj M.

Elektronika : konstrukcje, technologie, zastosowania

|

2009

|

Vol. 50, nr 9

80-82

PL

Rozpuszczanie się gazów w powierzchniowych warstwach stopów na osnowie faz międzymetalicznych Ti-46AI-BNb wpływa na ich właściwości mechaniczne (m. in. wzrost kruchości) i stanowi poważny problem ograniczający ich praktyczne zastosowanie. Jedną z metod zapobiegania temu zjawisku jest stosowanie powłok ochronnych. W pracy zaproponowano powłokę o składzie Ni-20Cr otrzymywaną techniką rozpylania magnetronowego. Skuteczność nałożonej warstwy badano podczas testu cyklicznego utleniania w temperaturze 700 oraz 800°C. Analizowano przebieg zmian masy próbek w funkcji czasu utleniania oraz budowę i skład tworzących się zgorzelin. Słowa kluczowe: fazy międzymetaliczne Ti-AI, powłoki otrzymywane techniką magnetronową, cykliczne utlenianie.

EN

Dissolution of gases (oxygen, nitrogen) during the initial stages of oxidation of Ti-AI intermetallics deteriorates their mechanical properties (causes embrittlement) and limit practical application. Deposition of protective coatings and inhibition of diffusion processes could possibly improve Ti-AI oxidation resistance. This work is concerned with the influence of Ni-20Cr magnetron sputtered coatings on Ti-46AI-8Nb oxidation in thermal cyclic conditions at 700 and 800°C. Oxidation kinetics, mechanical properties of the alloy/coating/scale system as well as morphology and composition of the scale were investigated.

3

Warstwy ochronne na stopie TiAlNb nanoszone techniką magnetronową : odporność na utlenianie

Godlewska E., Mania R., Mitoraj M.

Elektronika : konstrukcje, technologie, zastosowania

|

2007

|

Vol. 48, nr 10

30-31

PL

W początkowych fazach utleniania stopów na osnowie faz międzymetalicznych Ti-AI następuje rozpuszczanie się tlenu w warstwach powierzchniowych, co wpływa niekorzystnie na ich właściwości mechaniczne, powodując m.in. zwiększenie kruchości. Ograniczenie dordzeniowej dyfuzji tlenu mogłoby poprawić żaroodporność. W tym celu podjęto próbę naniesienia na powierzchnię stopu Ti-46AI-8Nb powłoki zawierającej nikiel oraz chrom, wykorzystując technikę magnetronową. W wyniku tego procesu otrzymano cienką warstwę o grubości poniżej 1um. Żaroodporność stopu z powłoką badano w powietrzu, poddając go działaniu cyklicznie zmiennych temperatur. Analizowano kinetykę utleniania, morfologię, skład chemiczny i fazowy powstałych zgorzelin.

EN

Initial stages of oxidation of the TiAl intermetallics involve oxygen dissolution, which is believed to have a detrimental effect on the mechanical properties (embrittlement of surface layers). Improvement of the oxidation resistance might be possible by preventing oxygen diffusion. In this study a magnetron-sputtered coating containing Ni and Cr was deposited on the Ti-46AI-8Nb alloy. Its thickness was less than 1 um. The oxidation resistance of thus coated alloy was investigated in air, at a temperature of 700 and 800 C, under thermal cycling condition. Mass change measurements were continued up to 300 hours. The post-test examination included morphology, chemical composition and phase composition of the oxidation products and of the near-surface area of the alloy.