Cut-resistant functional coated aramid knitted textiles

Kropidłowska Paulina, Irzmańska Emilia

Polimery

2024

Vol. 69, nr 10

590--597

The effect of SiO2 (0.5–2.5 wt%) with a particle size of 1–5 μm on the rheological and tensile properties as well as cut resistance of aramid fabrics coated with a thin layer of silica-containing latex was investigated. The rheological properties of the latex were assessed based on the dependence of viscosity on shear rate. The developed polymer coatings belong to the group of nonlinear, shear-thinning viscoelastic fluids, since their viscosity decreases with increasing shear rate. A 40% increase in cut resistance was obtained with increasing SiO2 content in the latex.

Zbadano wpływ SiO2 (0,5–2,5% mas.) o wielkości cząstek 1–5 μm na właściwości reologiczne i mechaniczne przy rozciąganiu oraz odporność na przecięcie tkanin aramidowych pokrytych cienką warstwą lateksu zawierającego krzemionkę. Właściwości reologiczne lateksu oceniono na podstawie zależności lepkości od szybkości ścinania. Opracowane powłoki polimerowe należą do grupy nieliniowych, rozrzedzanych ścinaniem płynów lepkosprężystych, ze względu na to, że ich lepkość zmniejsza się wraz ze wzrostem szybkości ścinania. Uzyskano 40% wzrost odporności na przecięcie wraz ze wzrostem zawartości SiO2 w lateksie.