Analysis of crystallite size changes in a hematite and magnetite formed on steel used in the power idustry

Gwoździk M.

Technical Sciences / University of Warmia and Mazury in Olsztyn

|

2018

|

nr 21(1)

65--73

EN

The paper presents results of studies on the crystallite sizes of oxide layer formed during a long-term operation on 10CrMo9-10 steel at an elevated temperature (T = 545° C, t = 200,000 h). This value was determined by a method based on analysis of the diffraction line profile, according to a Scherrer formula. The oxide layer was studied on a surface and a cross-section at the outer and inner site on the pipe outlet, at the fire and counter-fire wall of the tube. X-ray studies were carried out on the surface of a tube, then the layer’s surface was polished and the diffraction measurements repeated to reveal differences in the originated oxides layer.

2

Changes of crystallite sizes in the oxide layer forming during long-term operation of 10CrMo9-10 steel

Gwoździk M.

Technical Sciences / University of Warmia and Mazury in Olsztyn

|

2017

|

nr 20(3)

289--296

EN

The paper contains results of the studies on X-ray diffraction analysis XRD (studying the phase composition, crystallite sizes) of oxide layers on 10CrMo9-10 steel, operated for a long time at an elevated temperature (T = 525°C, t = 200,000 h). The oxide layer was studied on a surface and a cross-section at the outer on the inlet both on the fire and counter-fire side of the tube wall surface. X-ray studies were carried out on the outer surface of a tube, and then the layer surface was polished down and the diffraction measurements were performed again to determine crystallite size in oxide layers. Based on the width and the position of the main coat and substrate reflections, the size of the crystallites was determined using the Scherrer formula.

3

Analiza zmian wielkości krystalitów w warstwie magnetytu powstałej na stali 10CrMo9-10

Gwoździk M.

Hutnik, Wiadomości Hutnicze

|

2013

|

Vol. 80, nr 11

766--768

PL

W pracy przedstawiono wyniki badań wielkości krystalitów magnetytu powstałego podczas długotrwałej eksploatacji rur ze stali 10CrMo9-10 od strony spalin. Próbki do badań pobrano z rurociągu, który pracował w temperaturze T=575oC w czasie 100 000 godzin. Przeprowadzono pomiary dyfraktometryczne z powierzchni zewnętrznej elementu, następnie powierzchnię spolerowywano za każdym razem wykonując pomiary rentgenograficzne. Analizę rentgenowską przeprowadzono przy użyciu dyfraktometru SEIFERT 3003 T/T z zastosowaniem lampy o anodzie kobaltowej λCo = 0,17902 nm.

EN

The paper presents results of studies on the crystallite sizes of magnetite formed (on the flue gas side) during a long-term operation on 10CrMo9-10 steel. Test specimens were taken from a pipeline operated at 575°C for 100 000 hours. X-ray studies were carried out on the tube outside surface (on the flue gas side), then the layer’s surface was polished and the diffraction measurements repeated to reveal differences in the originated oxides layer. X-ray phase analysis was performed using a SEIFFERT 3003 T/T X-ray diffractometer, with a cobalt tube of λCo = 0.17902 nm wavelength.

4

Analysis of crystallite size and lattice deformations changes in an oxide layer on P91 steel

Gwoździk M., Nitkiewicz Z.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 1

31-34

EN

The paper contains results of studies on X-ray diffraction analysis XRD (studying the phase composition, crystallite sizes and lattice deformations) of oxide layers on P91 steel, operated for a long time at an elevated temperature (T = 535°C, t = 70,000 h). X-ray studies were carried out on the inner surface of a tube, and then the layer surface was polished down to 3.5 um and the diffraction measurements were performed again to determine individual oxide layers. It has been found that a three-zone oxide layer is formed as a result of long-term operation of P91 steel at the temperature of 535°C. Hematite occurs on the inner surface of the tube. Then magnetite appears below hematite. Going deeper into the layer there is a spinel, i.e. a mixture of magnetite and chromite. A visible decay of total intensity for Fe2O3 is observed already at the polishing depth of 3.5 um. In the case of Fe3O4 and FeCr2O4 an increase in total intensity is observed already from 7 um, what manifests in narrowing the diffraction line and hence in increasing the crystallites size and in the relaxation of stresses in this oxide layer. The broadening of a diffraction line caused by a small size of crystallites is expressed by the Scherrer relationship. Instead, the beta2 broadening resulting from lattice distortions (relaxation of stresses) was determined from the Taylor relationship.

PL

Praca zawiera wyniki badań dotyczących rentgenowskiej analizy dyfrakcyjnej XRD (badanie składu fazowego, wielkości krystalitów i odkształceń sieciowych) warstw tlenkowych na stali P91 długotrwale eksploatowanej w podwyższonej temperaturze (T=535 C, t=70000h). Badania rentgenograficzne przeprowadzono na powierzchni wewnętrznej rury, następnie powierzchnie warstwy spolerowywano na głebokość 3,5 um i ponownie wykonywano pomiary dyfrakcyjne w celu określenia poszczególnych warstw tlenkowych. Stwierdzono, ze w wyniku długotrwałej eksploatacji stali P91 w temperaturze 535 C powstaje trójstrefowa warstwa tlenków. Na powierzchni wewnętrznej rury występuje hematyt. Następnie poniżej hematytu pojawia sie magnetyt. Idąc dalej w głąb warstwy występuje spinel, tj. mieszanina magnetytu i chromitu. Widoczny zanik intensywności całkowitej dla Fe2O3 obserwuje się już na głębokości polerowania 3,5 um. W przypadku Fe3O4 i FeCr2O4 od 7 _m obserwuje się już wzrost intensywności całkowitej, co przejawia się zwężeniem linii dyfrakcyjnej, a tym samym zwiększeniem wielkości krystalitów i relaksacja naprężeń w tej warstwie tlenków. Poszerzenie linii dyfrakcyjnej spowodowane mała wielkością krystalitów wyraża się zależnością Scherrera. Natomiast zwężenie wynikające ze zniekształceń sieciowych (relaksacji naprężeń) wyznaczono z zależności Taylora.