Numerical analysis of chloride corrosion of reinforced concrete

German M., Zaborski A.

Czasopismo Techniczne. Budownictwo

2011

R. 108, z. 1-B

47-59

The phenomenon of corrosion can be divided in two stages: the initiation and propagation phases. The initiation phase analysis considers a chloride ions flux described by Nernst-Planck equation. Following the results of initiation phase, a numerical analysis of corrosion propagation phase has been performed. The propagation phase is the time, when corrosion cell is formed. As a result of current flowing through reinforcement, the corrosion products are accumulated at the steel-concrete interface, what generates the tensile stresses in concrete, causing cracking. On the surface longitudinal cracks and concrete splitting are observed. This leads to the loss of strength of the element.

Zjawisko korozji może być podzielone na dwa etapy: inicjacji i propagacji. Analiza fazy inicjacji obejmuje dotyczy przepływu jonów chlorkowych, który został opisany równaniem Nernsta-Plancka. Na podstawie uzyskanych rezultatów dokonano analizy fazy propagacji korozji. Podczas fazy propagacji korozji utworzone zostaje ogniwo korozyjne, w wyniku czego przez zbrojenie przepływa prąd. Pręt zbrojeniowy ulega korozji, a jej produkty są gromadzone na styku stal-beton. W betonie generowane są naprężenia rozciągające, powodujące zarysowanie widoczne na powierzchni betonu. Korozja chlorkowa prowadzi do zarysowanie, odprysków betonu, utraty przyczepności między stalą i betonem oraz utratą nośności elementu.