The Influence of the Microstructural Evolution on the Corrosion Resistance of Cold Drawn Copper Single Crystals in NaCl

Koralnik M., Dobkowska A., Adamczyk-Cieslak B., Mizera J.

Archives of Metallurgy and Materials

2020

Vol. 65, iss. 1

55--64

The aim of the present work was to determine the influence of the microstructural evolution of copper single crystals with the initial orientations of <001> and <111> after cold drawing on their corrosion resistance. Transmission electron microscopy, X-ray diffraction, and electron backscattering diffraction were used to characterize the microstructural changes. To evaluate the corrosion resistance after deformation, open circuit potential, electrochemical impedance spectroscopy, and potentiodynamic polarization analyses were conducted. The microstructural observations showed the presence of dislocation cell structures and shear bands indeformed sample with initial orientation <001> single crystal, as well as a strongly-developed substructure in sample <111>. The material with initial orientation of <001> was more resistive in analyzed medium than material with the initial orientation of <111>.

Transformations of dominant deformation systems in copper single crystals

Szczerba M. S.

Archives of Metallurgy

2001

Vol. 46, iss. 1

53-64

A close relation between the origin of tensile instability and the onset of deformation stage IV of copper single crystals was found. The tensile instability in single glide oriented copper single crystals belongs to the end of the overshoot phenomena resulting from a change of dominant deformation system - the changeover from primary to conjugate slip dominance. The identical transformation in deformation mechanism was found to be responsible for the onset of stage IV of plastic deformation of copper single crystals tested in rolling. Structural and mechanical observations and 4.2 K electrical resistivity measurements performed on the deformed crystals show, that the change in deformation mechanism causes a significant decrease in the rate of work hardening, a sudden change in the rate of dislocation accumulation, and the redistribution of dislocation arrangements in crystal lattice. It is concluded that the transformation of dominant deformation systems may strongly control deformation properties of face centered cubic crystals at large plastic strains. Finally the low temperature slip-twin transformation is discussed in terms of the change of a dominant deformation system.

W pracy na przykładzie walcowanych i rozciąganych monokryształów miedzi wykazano, że początek IV-tego stadium deformacji oraz początek nicstatcczności rozciągania są zjawiskami fizycznie równoważnymi. W monokryształach miedzi o orientacji środka trójkąta podstawowego, niestateczność rozciągania należy do zjawisk kończących tzw. „overshoot” i wynika ze zmiany dominującego systemu deformacji – zamiana dominującego poślizgu pierwotnego na sprzężony. Identyczna transformacja w mechanizmie deformacji została znaleziona w walcowanych monokryształach miedzi. Przeprowadzone badania mechaniczne i strukturalne oraz pomiary oporności elektrycznej w temperaturze ciekłego helu pokazują, że transformacji dominującego systemu poślizgu towarzyszy znaczny spadek prędkości umocnienia, zmiana prędkości akumulacji dyslokacji oraz zmiana konfiguracji układów dyslokacji deformowanego kryształu. W pracy stwierdzono, że transformacja dominującego systemu poślizgu może istotnie kontrolować właściwości plastyczne kryształów regularnie ściennie centrowanych w obszarach dużych odkształceń plastycznych. W pracy podjęto również dyskusję nad niskotemperaturową transformacją typu poślizg-bliźniakowanie.