Wyniki wyszukiwania - BazTech

1

Cell adhesion on spin-coated poly(butylene succinate-co-dilinolene succinate) (PBS-DLS) copolyesters

Kantor-Malujdy Nina, Sokołowska Martyna, Sobolewski Peter, El Fray Mirosława

Engineering of Biomaterials

|

2021

|

Vol. 24, no. 163

57

2

Produkcja, właściwości i kierunki rozwoju biodegradowalnych poliestrów ze szczególnym uwzględnieniem kopolimerów alifatyczno-aromatycznych

Ukielski R., Kondratowicz F., Kotowski D.

Polimery

|

2013

|

T. 58, nr 3

167-176

PL

Artykuł stanowi przegląd literaturowy dotyczący produkowanych przemysłowo kopoliestrów alifatyczno-aromatycznych (AAC) i poliestrów alifatycznych zdolnych do degradacji. Szczególną uwagę poświęcono światowym pracom badawczym nad nowymi typami kopoliestrów alifatyczno-aromatycznych.

EN

The paper is a literature review concerning the industrially produced aliphatic-aromatic copolyesters (AAC) and aliphatic polyesters capable of degradation. Particular attention was given to worldwide studies on new types of aliphatic-aromatic copolymers.

3

Degradowalne, włóknotwórcze kopoliestry tereftalanu etylenu i kwasu mlekowego

Grzebieniak K., Ratajska M., Twarowska-Schmidt K.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2003

|

Vol. 52, nr 25

411-412

EN

Random copolyesters of ethylene terephalate (ET) and L-lactic (LA) having [eta]red=72-82 cm3/g (by the method for PET) were studied. They contained short sequences of ETx(x=2.8-3.3) and 25.5-29.5 mol% of LA mainly in form of individual units (LAy component with y<1.25) and showed Tg=58-64C (after synthesis) and penetrometrically measured melting temperature, Tmp=120-185C (after annealing). The melt-spun 56dtex/16f multifilament yarn having tenacity c..20 cN/tex and elongation 23% was obtained using the copolyester with properties [eta]red=81 cm3/g , Tg=63C and Tmp -185C. Hydrolytic degradation (55C, pH 7.35) as well as biodegradation tests in aqueous medium (35 and 55C) and in compost (55C) were performed using samples in form of pressed sheets and fibres. Distinet degradation of copolymers was observed only at temperature 55C (close to Tgvalues). It was found that hydrolytic degradability of copolyesters, which was mainly responsible for their behaviour during tests of biodegradation, was highly dependent on parameters of their chemical structure (X and y values).

4

Teraphthalic Acid Obtainable from Poly(ethylene terephthalate) Wastes

Michalski A.

Fibres & Textiles in Eastern Europe

|

2001

|

Vol. 9, no. 1 (32)

40--43

EN

The results of studies on the technology applied for utilisation of poly(ethylene terephthalate) wastes left after production of bottles and other products by means of their processing into terephthalic acid and ethylene glycol are presented in this paper. For the purposes of the above processing, the method of hydrolysis in an inactive environment without any application of frequently used acids or alkalis has been chosen. Terephthalic acid of 95-99.9% purity has been obtained. Its quality allows its use as a raw-material in numerous synthesis processes including its re-use in the manufacture of polyethylene terephthalate, as well as its use in the production of co-polyamides and polyester amides etc.

PL

Przedstawiono wyniki badań nad technologią utylizacji odpadów butelkowych i po-produkcyjnych poli (tereftalanu etylenu) poprzez ich przetworzenie na kwas tereftalowy i glikol etylenowy. Wybrano w tym celu metodę hydrolizy w środowisku obojęt¬nym, bez użycia często stosowanych kwasów lub alkaliów. Otrzymano kwas tereftalowy o czystości 95-99,9%. Jego jakość pozwala na wykorzystanie go jako surowca w wielu syntezach, m. in. ponownie do wyrobu poli (tereftalanu etylenu), do produkcji kopoliamidów, poliestroamidów i in.