The Effect of Cooling Rate after Homogenization on the Microstructure and Properties of 2017a Alloy Billets for Extrusion with Solution Heat Treatment on the Press

Woźnicki A., Leśniak D., Włoch G., Pałka P., Leszczyńska-Madej B., Wojtyna A.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 3

1663--1670

The influence of cooling rate after homogenization on the 2017A alloy microstructure was analysed. The capability of the θ (Al2Cu) particles, precipitated during various homogenization coolings, for rapid dissolution was estimated. For this purpose, the DSC test was used to determine the effect of the cooling rate after homogenization on the course of melting during a rapid heating. Moreover, the samples after solution heat treatment (with short time annealing) and ageing, were subjected to the microstructure investigations and the microhardness of grains interiors measurements. It was found that cooling after homogenization at 160 °C/h is sufficient for precipitation of fine θ phase particles, which dissolve during the subsequent rapid heating. The cooling at 40 °C/h, causes the precipitation of θ phase in the form of large particles, incapable of further fast dissolution.

The Effect of Homogenization Conditions on the Structure and Properties of 6082 Alloy Billets

Woźnicki A., Leśniak D., Włoch G., Leszczyńska-Madej B., Wojtyna A.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 3A

1764--71

The paper presents the results of laboratory homogenization investigations of the 6082 grade alloys, differing in Mg and Si content. At the first stage, the microstructure of alloys was analysed after homogenization finished with water quenching. SEM/EDS investigations and DSC tests were applied to evaluate the dissolution of the Mg2Si particles and concentration of the main alloying additions in the grains interiors, depending on soaking conditions. In the case of alloy with lower Mg and Si content, homogenization the temperature of 535ºC for 8h is sufficient for significant Mg2Si particles dissolution. For the alloy with higher Mg and Si content, after homogenization the temperature of 550ºC for 8h, the amount of undissolved Mg2Si particles decreases visibly, compared to homogenization at 535ºC for 8h. However, an unfavourable tendency of dispersoids growth is observed and these soaking conditions are not found to be recommended. At the second research stage, the influence of homogenization cooling rate on the size and distribution of the Mg2Si particles observed in the alloys microstructure was analysed. The ability of the Mg2Si particles, precipitated during various homogenization coolings, to rapid dissolution was estimated. For this purpose, the hardness after solution heat treatment with short annealing and ageing was determined and the DSC tests were performed. It was found, that cooling after homogenization at 315ºC/h is sufficient for precipitation of fine Mg2Si particles, which dissolve during subsequent rapid heating. Cooling at 40ºC/h, causes precipitation of Mg2Si phase in the form of large particles, unable for further fast dissolution.

W artykule przedstawiono wyniki laboratoryjnych badań homogenizacji dwóch stopów w gatunku 6082, różniących się zawartością Mg i Si. W pierwszym etapie analizowana była struktura stopów po homogenizacji z chłodzeniem w wodzie. Szczególną uwagę zwrócono na rozpuszczanie cząstek fazy Mg2Si podczas wygrzewania oraz zawartość głównych składników stopowych we wnętrzach ziarn. Oceny parametrów wygrzewania dokonano w oparciu o badania SEM/EDS oraz testy DSC. W przypadku stopu z niższą zawartością Mg i Si, homogenizacja w temperaturze 535ºC przez 8 h jest wystarczająca dla znaczącego rozpuszczenia cząstek fazy Mg2Si. W przypadku stopu z wyższą zawartością Mg i Si, po homogenizacji w temperaturze 550ºC przez 8h, udział nierozpuszczonych cząstek Mg2Si spada wyraźnie, w porównaniu z homogenizacją w temperaturze 535ºC przez 8h. Jednakże, stwierdzono niekorzystną tendencję do rozrostu dyspersoidów, zatem tych warunków wyżarzania nie uznano za rekomendowane. W drugim etapie analizowano wpływ szybkości chłodzenia z temperatury homogenizacji na wielkość i dystrybucję cząstek Mg2Si obserwowanych w strukturze stopów. Wykonano badania SEM oraz dokonano oceny możliwości szybkiego rozpuszczania cząstek Mg2Si wydzielonych podczas chłodzenia z temperatury homogenizacji z różnymi szybkościami. W tym celu wykonano badania twardości stopów po przesycaniu z krótkim wygrzewaniem oraz starzeniu, jak również badania DSC. Stwierdzono, że studzenie z temperatury homogenizacji z szybkością 315ºC/h jest wystarczające dla wydzielenia drobnych cząstek Mg2Si, które ulegają rozpuszczeniu podczas późniejszego gwałtownego nagrzewania. Chłodzenie z temperatury homogenizacji z szybkością 40ºC/h powoduje wydzielanie fazy Mg2Si w postaci dużych cząstek, które nie ulegają pełnemu rozpuszczeniu podczas późniejszego szybkiego nagrzewania.