Influence of bath type for zinc plating and passivation with trivalent chromium compounds on the corrosion resistance and appearance of coatings obtained

Kołodziej Mateusz, Niciejewska Anna, Winiarski Juliusz

Ochrona przed Korozją

|

2023

|

nr 5

132--138

EN

Zinc coatings obtained in electrolytic zinc plating differ in terms of corrosion resistance and their visual aspect depending on the brightener and basic components used. In order to achieve industrial properties and a desired appearance of the coatings, commercial organic additives made by Galvano-Partners and Dipsol were used. It has been shown that a greater effect on corrosion resistance can be achieved when the same passivation is applied to different zinc substrates. Electrolytically applied zinc from a zinc chloride solution and with thin-film passivation shows a higher polarization resistance after 24 h compared to a coating obtained using two technologies utilizing (alkaline) baths based on sodium zincate, despite having the same conversion coating. In the aspect of one electrolytic zinc coating with different chromate coatings, disproportions between the successive conversion technologies are noted in the polarization resistance. Potentiodynamic curves describing a zinc coating with different chromate layers applied indicate a major variation in the barrier properties of the studied material.

PL

W zależności od wykorzystanego składnika wybłyszczającego oraz składników podstawowych otrzymywane powłoki cynkowe z cynkowania elektrolitycznego różnią się pod względem odporności korozyjnej oraz wizualnie. By uzyskać właściwości przemysłowe oraz określony wygląd powłok, wykorzystano komercyjne dodatki organiczne firm Galvano-Partners oraz Dipsol. Jeszcze większy wpływ na odporność korozyjną ma zastosowanie pasywacji chemicznej przez wytworzenie powłok konwersyjnych na powłokach cynkowych. Istotne różnice daje nawet zastosowanie tej samej pasywacji na różnym podłożu cynkowym: cynk nałożony elektrolitycznie w kąpieli sporządzonej na bazie chlorku cynku (zwanej słabo kwaśną) i z pasywacją cienkopowłokową (0,07 μm ±0,03 μm) wykazuje po 24 h wyższą rezystancję polaryzacyjną w porównaniu z powłoką wytworzoną zgodnie z dwoma technologiami, w których wykorzystuje się kąpiele sporządzone na bazie cynkanu sodu (zwane alkalicznymi), pomimo tej samej powłoki konwersyjnej. W wypadku takich samych powłok cynkowych wytworzonych elektrolitycznie, lecz pokrytych różnymi powłokami konwersyjnymi uzyskanymi chemicznie w wyniku zastosowania kąpieli sporządzonych na bazie związków chromu trójwartościowego obserwuje się różną odporność korozyjną w zależności od zastosowanych technologii wykonywania powłok konwersyjnych. Krzywe potencjodynamiczne otrzymane dla próbek z powłoką cynkową z nałożonymi różnymi warstwami konwersyjnymi wskazują na zróżnicowanie odporności korozyjnej badanego materiału.

2

Zabezpieczenia antykorozyjne profili aluminiowych stosowanych w budownictwie

Gawron M.

Materiały Budowlane

|

2017

|

nr 9

41--42

3

Conversion coatings with enhanced corrosion resistance deposited on electrogalvanized steel from titanium(III) chloride containing bath

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2015

|

nr 11

384--387

EN

Cr-free conversion coatings were deposited from a bath containing: titanium(III) chloride, fluorosilicic acid, hydrogen peroxide and oxalic acid. An XPS analysis of the coating deposited for 3 min showed titanium to be present mainly at the +4 oxidation state number and zinc at the +2 oxidation state number, in the form of oxides and hydroxides. Silicon forms silicates. DC polarization showed that the corrosion current densities for the coatings deposited for 30 s – 6 min were below 1 μA·cm−2 and lower than that of zinc coating. EIS and neutral salt spray test revealed that in order to ensure good protective properties deposition should be conducted for at least 3 minutes.

PL

Bezchromowe powłoki konwersyjne otrzymano z kąpieli zawierającej: chlorek tytanu(III), kwas fluorokrzemowy, nadtlenek wodoru oraz kwas szczawiowy. Analiza XPS powłoki osadzanej przez 3 minuty wykazała obecność tytanu na +4 stopniu utlenienia oraz cynku w formie utlenionej, zarówno pod postacią tlenków jak i wodorotlenków. Na podstawie pomiarów polaryzacyjnych stałoprądowych obliczono szybkość korozji w 0.5 M NaCl powłok osadzanych w zakresie 30 s do 6 min, która była niższa od 1 μA·cm−2 oraz niższa od szybkości korozji porównawczej powłoki cynkowej. Badania zmiennoprądowe metodą EIS oraz test w komorze solnej pozwoliły stwierdzić, że dobre właściwości ochronne posiadają powłoki bezchromowe osadzane przez przynajmniej 3 minuty.

4

Wpływ modyfikacji wstępnej obróbki powierzchniowej stopu AA2024-T3 na właściwości ochronne powłoki organicznej

Kapuścińska A., Kwiatkowski L.

Inżynieria Powierzchni

|

2015

|

nr 2

41--46

PL

Celem pracy było opracowanie metody wstępnej obróbki powierzchniowej stopu AA2024-T3 i zbadanie jej wpływu na właściwości ochronne powłoki organicznej w porównaniu z powłoką naniesioną na podłoże chromianowane. Zasadniczym procesem przygotowania powierzchni było fosforanowanie amorficzne. Etap doszczelnienia uzyskanej w tym procesie powłoki fosforanowo-tlenkowej przeprowadzono metodą chemiczną w wodnym roztworze krzemianu sodu z dodatkiem inhibitora 2-merkaptobenzoksazoł (MBX, wariant I) oraz w procesie zol-żel z prekursorów tetrametoksysilan (TMOS)/dietoksydimetylosilan (DEDMS) z wprowadzonym do mieszaniny inhibitorem MBX (wariant II). Odporność korozyjną wytworzonych powłok konwersyjnych pokrytych powłoką organiczną oceniono za pomocą elektrochemicznej spektroskopii impedancyjnej EIS. Mimo tego że pierwsza metoda doszczelnienia jest znacznie wygodniejsza w aplikacji oraz mniej kosztowna, to nie zapewnia odporności korozyjnej porównywalnej z powłoką hybrydową TMOS/DEDMS. Widma impedancyjne zarejestrowane dla wariantu doszczelnienia powłoki fosforanowanej w procesie zol-żel z MBX w początkowej fazie ekspozycji w roztworze 0,5 MNa2SO4 + 0,01M NaCl o pH =6,0 wskazują na porównywalne z powloką chromianową właściwości ochronne. Po 168 godzinach ekspozycji pojawienie się drugiej stałej czasowej dla systemu ochronnego z powloką hybrydową, świadczy o pogorszeniu właściwości barierowych, podczas gdy dla powłoki organicznej na podłożu chromianowanym przebieg widm nie uległ zmianie podczas pełnego cyklu badań.

EN

The study was aiming at the development of surface pre-treatment of AA2024-T3 alloy prior to organic coating as the alternative to chromating. The main conversion coating was obtained by means of amorphous phosphating followed by two types of sealing process. The process of sealing was carried out in an agueous solution of sodium silicate with the addition of 2 mercaplobenzoxazole (MBX, version I) and in sol-gel process using precursors TMOS/DEDMS which were successfully used in another work for Mg surfaces. This mixture was doped with MBX and performed as version II. The corrosion resistance of amorphous phosphate coating with or without sealing and top coated by organic coating was evaluated using Electrochemical Impedance Spectroscopy (EIS). While an application of the first method is much more robust and less expensive, it does not provide comparable corrosion resistance with the hybrid inorganic-organic layer formed in soil gel process. For the latter, the impedance spectra obtained at the initial stage of exposition in 0,5 M Na2SO4 + 0,01 M NaCl solution showed a similar course to chromate conversion coating, however, unlikely to chromate containing coating system, after a longer time (168 h) an occurrence of a time constant in lower frequencies range indicated an onset of corrosion process.

5

Możliwości doszczelnienia amorficznej powłoki fosforanowej otrzymanej na stopie aluminium AA2024-T3 – przykłady materiałowe i technologiczne

Kapuścińska A., Kwiatkowski L.

Inżynieria Powierzchni

|

2015

|

nr 1

47--57

PL

W artykule przedstawiono wyniki badań nad zwiększeniem odporności korozyjnej stopu AA2024-T3 pokrytego amorficzną powłoką tlenków i fosforanów glinu wytworzonych w procesie fosforanowania. Zastosowano dwa rodzaje płukania uszczelniającego: w roztworach zawierających mieszaninę tetrametoksysilanu, dietoksydimetylosilanu oraz 2-merkaptobenzoksazol (MBX) lub konkurencyjnie w roztworze krzemianu sodu, alternatywnie z dodatkiem taniny lub MBX. Oceniano wpływ rodzaju roztworu, inhibitora oraz warunków suszenia powłok. Badania odporności korozyjnej przeprowadzono metodami elektrochemicznymi w roztworze 0,5M Na2SO4 + 0,01 M NaCl. Na podstawie niezależnie zarejestrowanych krzywych polaryzacji katodowej i anodowej oraz pomiarów impedancji układu metal-powłoka-roztwór elektrolitu stwierdzono, że właściwości ochronne powłoki konwersyjnej uszczelnionej w roztworze krzemianu sodu zawierającego MBX i poddanego suszeniu w temperaturze 100oC (30 min) są równorzędne z powłoką wytworzoną w trudniejszym technologicznie i mniej korzystnym pod względem ekonomicznym procesie zol-żel. Istotnym wynikiem dla płukania w roztworze krzemianu jest brak podatności na korozję wżerową w całym zakresie badanych potencjałów, tj. do 1,5 V względem NEK.

EN

The paper presents the results of studies aiming at the increasing of corrosion resistance of the Al alloy AA2024-T3 coated with an amorphous coating of aluminium oxide and phosphate formed in the phosphating process. Two types of sealing rinse were performed: in solution containing a mixture of tetramethoxysilane, diethoxydimethylsilane, and 2-mercaptobenzoxazole (MBX), and competitive solution of sodium silicate, with the addition alternatively of tannin or MBX. A kind of a solution, inhibitor and drying conditions were assessed. Protective properties of the coatings were evaluated by means of electrochemical methods in a solution containing 0,5M Na2SO4 + 0,01M NaCl at pH = 6,0. Independently recorded anodic and cathodic polarization curves and impedance measurements of metal-coating-solution electrolyte system shown that the protective properties of the conversion coating sealed in a solution containing sodium silicate MBX and subjected to drying at 100°C (30 min.) is equivalent in terms of corrosion protection to the coating formed in the sol-gel process which is technologically more difficult and less cost effective. An important result for sealing rinse in the silicate solution is a lack of susceptibility to pitting corrosion in the entire range of the applied potentials, ie. to +1.5 V versus SCE.

6

Właściwości ochronne bezchromowych powłok konwersyjnych osadzanych z kąpieli na bazie związków Ti(IV), Mn(II) oraz kwasu fosforowego(V) modyfikowanej dodatkiem organicznym

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2012

|

nr 5

224-228

PL

W pracy przedstawiono wyniki badań bezchromowych powłok konwersyjnych zawierających tytan, osadzonych na podłożu cynkowym z kąpieli zawierającej: K2TiF6, H2O2, Mn(NO3)2, H3PO4 oraz dodatkowo polimer o właściwościach błonotwórczych - poli(akrylan sodu). Zbadano wpływ warunków osadzania powłok na ich morfologię (SEM) oraz odporność na korozję (pomiary polaryzacyjne stałoprądowe, testy w komorze solnej). Określono skład chemiczny powłok zawierających dodatek organiczny oraz zaproponowano związki chemiczne, w których występują poszczególne pierwiastki tworzące powłokę (rentgenowska spektroskopia fotoelektronów - XPS, spektroskopia elektronów Augera - AES). Wyniki badań morfologii wykazały, że ze wzrostem czasu osadzania powłok wzrasta ich homogeniczność oraz zanikają pory. Analiza XPS wykazała, że pierwiastkami tworzącymi powłokę są: Mn, Zn, Ti, P, O oraz C, a dodatek organiczny ulega wbudowaniu w powłokę. Otrzymane powłoki o grubości nie przekraczającej 100 nm wyraźnie podnoszą odporność na korozję podłoża cynkowego, przy czym najniższą wartość gęstości prądu korozyjnego zarejestrowano dla powłoki osadzanej w czasie 60 s.

EN

The article presents the results of research on chromium-free Ti-containing conversion coatings. The coatings were deposited on zinc substrate from the solution consisted of: K2TiF6, H2O2, Mn(NO3)2, H3PO4 and a film-forming polymer - sodium polyacrylate. The effect of deposition conditions on their morphology (SEM) and corrosion resistance (DC polarization measurements, salt spray test) were investigated. The chemical composition of the coating and the chemical state of each element was determined by X-Ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES). The results of SEM analysis showed that with increasing deposition time the coating becomes more homogenous. XPS analysis showed that the coating is composed of: Mn, Zn, Ti, P, O and C. Moreover the organic additive is incorporated in the coating after deposition process. The thickness of the selected coating estimated from Auger depth profiling method was less than 100 nm. Coatings deposited from the proposed bath markedly increase the corrosion resistance of bare zinc substrate. The lowest corrosion current density value was recorded for the coating deposited in 60 s.

7

Wielowarstwowe powłoki ochronne na odlewniczych stopach magnezu

Nieużyła Ł., Nawrat G., Krząkała A., Maciej A., Michalska J.

Ochrona przed Korozją

|

2012

|

nr 5

200-203

PL

W pracy przedstawiono wyniki badań dotyczące wytwarzania powłok konwersyjnych na stopie magnezu AZ91D przy zastosowaniu metody elektrochemicznego utleniania plazmowego. Następnie na tak zmodyfikowaną powierzchnię stopu nakładano powłokę SiO2-Al2O3 metodą zol-żel. Przedstawiono morfologię otrzymanych powłok, określono ich chropowatość oraz odporność na korozję. Stwierdzono, że wytworzenie powłok metodą elektrochemicznego utleniania plazmowego, a następnie ich uszczelnienie ceramiczną powłoką tlenkową powoduje wzrost odporności stopu na korozję.

EN

In the present work, we report results of investigations of conversion coatings obtaining on magnesium alloy AZ91D by means plasma electrolytic oxidation (PEO) method. Next, on modified alloy surface SiO2-Al2O3 coating was put on. Morphology of obtained coatings, their roughness and corrosion resistant are presented. It was found that coatings obtained by means PEO method and then tighten with ceramic coating show considerable increase of corrosion resistance.

8

Odporność na korozję powłok bezchromowych otrzymanych z kąpieli na bazie H2ZrF6 modyfikowanej dodatkiem 3-aminopropylotrietoksysilanu

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2012

|

nr 11

541-543

PL

W pracy przedstawiono wyniki badań korozyjnych powłok konwersyjnych zawierających cyrkon osadzonych na podłożu cynkowym z kąpieli opartej na H2ZrF6 jako źródle cyrkonu oraz 3-aminopropylotrietoksysilanie. Zbadano wpływ warunków osadzania powłok (temperatura kąpieli, czas osadzania) na ich odporność korozyjną. Za pomocą pomiarów polaryzacyjnych stałoprądowych w 0,5 M NaCl i testów w komorze solnej wykazano, że otrzymane powłoki wyraźnie podnoszą odporność na korozję stali ocynkowanej galwanicznie, a wydłużenie czasu osadzania powłok poprawia ich właściwości ochronne. Najniższe wartości gęstości prądu korozji zmierzono dla próbek z powłokami osadzonymi przez 20÷60 s z kąpieli o temperaturze 25°C.

EN

This paper presents the results of research on Zr-containing conversion coatings. The coatings were deposited on zinc substrate from the solution contained H2ZrF6 as a source of Zr and 3-aminopropyltriethoxysilane. The effect of deposition conditions (bathe temperature and immersion time) on their corrosion resistance (DC polarization measurements in 0.5 M NaCl, salt spray test) was investigated. Coatings deposited from the proposed bath increase the corrosion resistance of zinc electrogalvanized steel and the resistance is affected by the increase in deposition time. The lowest corrosion current density values were recorded for the coatings deposited at T = 25°C in t = 20÷60 s.

9

Badania morfologii i składu konwersyjnych powłok bezchromowych otrzymanych z kąpieli na bazie H2ZrF6 modyfikowanej dodatkiem 3-aminopropylotrietoksysilanu

Winiarski J.

Ochrona przed Korozją

|

2012

|

nr 11

536-540

PL

Otrzymano powłoki konwersyjne oparte na cyrkonie. Powłoki osadzono na podłożu cynkowym z kąpieli zawierającej m. in. H2ZrF6 oraz 3-aminopropylotrietoksysilan. Wyniki badań mikroskopowych wykazały, że są one homogeniczne, mają strukturę porowatą, a wzrost czasu osadzania w zakresie od 20 s do 180 s nie powoduje zmian w morfologii. Metodą XPS określono skład pierwiastkowy (obok Zr występują: O, C, Zn, F, Si, N) oraz związki chemiczne, z których zbudowane są otrzymane powłoki.

EN

The Zr-containing conversion coatings were obtained. The coatings were deposited on zinc coated steel from the solution contained i.e. H2ZrF6 and 3-aminopropyltriethoxysilane. The results of microscopic analysis showed that the coatings are homogeneous and rather porous, and the morphology is not affected by the deposition time which was changed in the range of 20 s - 180 s. By means of X-ray photoelectron spectroscopy the chemical composition was determined (Zr, O, C, Zn, F, Si, N) and the film-forming compounds were proposed.

10

Właściwości ochronne powłok otrzymywanych z roztworów na bazie silanów oraz związków tytanu(IV)

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2011

|

nr 7

446-448

PL

Dotychczasowe wyniki badań powłok konwersyjnych zawierających tytan stały się podstawą do zbadania właściwości powłok otrzymywanych z roztworów na bazie związków tytanu oraz organicznych związków krzemu. W trakcie przeprowadzonych badań osadzono na podłożu cynkowym powłoki z wodnych roztworów zawierających chlorek tytanu(IV) oraz tetraetyloortokrzemian (TEOS). Zbadano wpływ czasu osadzania powłok na ich morfologię (SEM), skład chemiczny (EDS) oraz odporność na korozję (pomiary polaryzacyjne, testy w komorze solnej).

EN

Recent studies on titanium containing conversion coatings were the basis to investigate the properties of the coatings obtained from baths consisted of titanium and silicon organic compounds. During experiment the coatings from solution containing titanium tetrachloride and tetraethoxysilane (TEOS) were deposited on zinc coated steel. The dependence between their morphology (SEM), chemical composition (EDS), corrosion resistance (polarization measurements, salt spray test) and deposition time was investigated.

11

Elektrochemiczne utlenianie aluminium metodą jarzeniową

Nieużyła Ł., Nawrat G., Michalska J.

Ochrona przed Korozją

|

2011

|

nr 4-5

243-245

PL

W pracy przedstawiono wyniki badań dotyczących wytwarzania powłok konwersyjnych na aluminium przy zastosowaniu metody jarzeniowej. Przeprowadzono badania wpływu parametrów prowadzenia procesu na skład chemiczny powłoki i jej właściwości ochronne. Przedstawiono morfologię otrzymanych powłok, określono ich chropowatość oraz odporność korozyjną. Stwierdzono, że napięcie stosowane w procesie jest parametrem, który znacząco wpływa na właściwości i skład otrzymywanych powłok.

EN

The results of investigations concerning to formation the conversion coatings on aluminum by micro-arc oxidation have been presented in the article. The studies of influence the process parameters on chemical composition and protection properties of the coatings were carried out. The coatings morphology was presented and their roughness and corrosion resistance were determined. It was found that applied voltage significantly affect on composition and properties of the coatings.

12

Physico-mechanical properties of Ti-containing chromium-free conversion coatings on zinc coated steel

Winiarski J., Szczygieł B.

Challenges of Modern Technology

|

2011

|

Vol. 2, no. 4

27--30

EN

This work aims at physico-mechanical properties of the Ti-containing chromium-free conversion coatings on zinc coated steel. The wear resistance of the whole conversion coating/zinc coating system depends on the deposition time of these coatings. As the duration of the deposition of conversion coatings containing titanium increases, the wear resistance of the samples decreases. The reason for this deterioration in wear resistance is likely worse adhesion of these coatings obtained at longer deposition times. The best adhesion to the zinc substrate posses coatings deposited for 20 s.

13

Wpływ chemicznej obróbki wstępnej stopów aluminium serii 2000 na właściwości ochronne powłok organicznych

Zych A., Kwiatkowski L.

Rudy i Metale Nieżelazne

|

2010

|

R. 55, nr 7

518-522

PL

Celem artykułu było zbadanie wpływu rodzaju powłoki konwersyjnej wytworzonej na stopie aluminium AA2024-T3 na właściwości ochronne powłoki organicznej, w porównaniu z powłoką chromianową zawierającą Cr(VI). Uwzględniono powłokę otrzymaną w procesie zol-żel oraz amorficzną powłokę fosforanowo-tlenkową. Właściwości ochronne układów powłokowych badano w obojętnej mgle solnej oraz za pomocą metod elektrochemicznych, metodą potencjodynamiczną i elektrochemicznej spektroskopii impedancyjnej. Pomimo że istnieją różnice we właściwościach ochronnych pomiędzy obróbką zol-żel i chromianowaniem, to pierwsza z metod jest bardziej skuteczna od innych alternatywnych w stosunku do chromianowania procesów chemicznych. Dobór odpowiedniego inhibitora uczestniczącego w procesie zol-żel jest istotnym krokiem w projektowaniu systemu ochronnego.

EN

The aim of this work is to investigate the effect of a type of conversion layer formed on AA2024-T3, on the protective properties of an organic coating in comparison with chromating. Amorphous phosphating and sol gel process were taken into consideration. Protective properties of the systems were assessed by means of neutral salt spray test (NSS) and electrochemical impedance spectroscopy (EIS). Although there is still a difference between sol-gel pre-treatment and chromating in terms of protective properties of the resulted coatings it seen that the former method is much more efficient than other chemical processes. A choice of the effective inhibitor included in a sol-gel pre-treatment is a crucial step in the design of protective system.

14

Wybrane metody wytwarzania powłok ochronnych na magnezie i jego stopach

Stankiewicz A., Laszczyńska A., Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2010

|

nr 4-5

286-292

PL

Magnez oraz jego stopy należą do najlżejszych materiałów konstrukcyjnych. Dzięki doskonałym właściwościom fizycznym i mechanicznym są coraz powszechniej stosowane w przemyśle lotniczym, samochodowym oraz w elektronice. Magnez jest metalem reaktywnym i bardzo podatnym na korozję, szczególnie w środowiskach zawierających jony chlorkowe, co ogranicza obszar zastosowań stopów magnezu. Z tego względu konieczne jest zabezpieczanie powierzchni elementów magnezowych poprzez nakładanie dodatkowych powłok malarskich, powłok konwersyjnych czy powłok elektrochemicznych lub stosowanie procesów anodowania oraz osadzania powłok z fazy gazowej. W artykule opisano i porównano najczęściej stosowane metody modyfikacji powierzchni stopów magnezu.

EN

Magnesium and its alloys, which are the lightest structural metal materials with excellent physical and mechanical properties are being used in a wide range of structural applications in industries as aerospace, automotive, computer and electronic. Unfortunately, magnesium is a very active metal and easy to be corroded, particularly in chloride environment. This has hindered its widespread use in many fields. Common processes used to enhance corrosion resistance include paints, conversion coatings, anodizing, vapor deposition, electrochemical plating. This review details the state of the art in coating and surface modification technologies for magnesium-based substrates.

15

Wpływ modyfikacji powierzchni stopu AZ91D na morfologię i odporność korozyjną - badania rozpoznawcze

Winiarski J., Stankiewicz A., Baraniecki T., Szczepaniak A., Szczygieł B.

Ochrona przed Korozją

|

2010

|

nr 11

633-636

PL

Magnez i jego stopy są doskonałymi materiałami konstrukcyjnymi dla zastosowań, w których ważne jest obniżenie masy produktu. Niestety magnez jest metalem bardzo podatnym na korozję. Celem tej pracy była poprawa właściwościpowierzchniowych stopu AZ91D, dzięki obróbce laserowej oraz osadzeniu powłoki konwersyjnej i powłoki Ni-P. Zbadano odporność na korozję i morfologię powierzchni po zastosowanych modyfi kacjach. Zaobserwowano korzystny wpływ obróbki laserowej na mikrostrukturę warstwy wierzchniej i na odporność korozyjną. Właściwości antykorozyjne poprawia także otrzymana powłoka konwersyjna.

EN

Magnesium and its alloys are an ideal material for applications where weight reduction is of signifi cant concern. Unfortunately, magnesium is highly susceptible to corrosion. The aim of this work was to improve the surface properties of AZ91D alloy by laser treatment, conversion and Ni-P coatings. The corrosion behavior and morphology of surface were studied. The beneficial influence of microstructure of surface and improvement of corrosion resistance were observed. Anticorrosive properties were enhanced by deposition of conversion coatings, also.

16

Odporność na korozję powłok konwersyjnych otrzymywanych z roztworów zawierających związki Ti(III)

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2010

|

nr 3

133-136

PL

Od wielu lat prowadzone są badania nad rozwojem nowych technologii otrzymywania powłok konwersyjnych pozbawionych Cr(VI). Wśród doniesień literaturowych można znaleźć prace poświęcone badaniom nad wytwarzaniem powłok konwersyjnych z roztworów zawierających związki molibdenu, wolframu, związki metali ziem rzadkich, związki tytanu lub cyrkonu, a także krzemiany. W przeprowadzonych badaniach określono właściwości elektrochemiczne (metody polaryzacyjne), topografię i skład (SEM, EDS) oraz odporność na korozję (komora solna) powłok konwersyjnych na podłożu cynkowym otrzymanych przez obróbkę w wodnym roztworze o składzie (gźdm-3): TiCl3 - 5; H2SiF6 - 10; H2O2 - 6; C2H2O4 --1. Najwyższe wartości oporu polaryzacji (Rp) wykazały powłoki wytworzone w następujących warunkach: pH = 2,5; T = 25 oraz 50°C; t =1 min. Powierzchnia próbek była pozbawiona spękań. Badane powłoki miały jasnoniebieską barwę o intensywności rosnącej z czasem wytwarzania powłoki. Wyniki analizy składu pierwiastkowego (EDS) potwierdziły obecność Ti i Si. Testy w komorze solnej wskazały na potencjalne możliwości zastosowania uzyskanych powłok konwersyjnych do ochrony cynku przed korozją. Ich odporność na korozję jest jednak mniejsza niż dla powłok chromianowych. Z tego względu konieczne są dalsze prace nad optymalizacją składu kąpieli oraz warunków otrzymywania powłok.

EN

The toxicity and carcinogenic nature of the hexavalent chromium compounds is well known. These concerns led to development of other non-toxic processes with comparable corrosion resistance. Recently new alternative types of conversion coatings were investigated that are formed by treatment in solutions containing molybdates, tungstates, rare earth compounds, titanium or zirconium compounds and silicates. This paper aims at electrochemical properties, topography, composition and corrosion resistance of the zinc conversion coatings obtained from the solution containing (gźdm-3): TiCl3 - 5; H2SiF6 - 10; H2O2 - 6; C2H2O4 - 1. The highest values of polarization resistance (Rp) have been measured for the samples obtained at pH 2,5; T = 25 and 50°C; t = 1 min. The obtained coatings were crack-free and had bright blue iridescent colour. The EDS analysis of the coatings reveals the presence of Ti and Si. The results of the salt spray test show that the investigated coatings could be used for the protection of zinc electro-galvanized steel, but their protection ability is worse than that for chromated zinc.

17

Bezchromowe powłoki konwersyjne na cynkowych podłożach stopowych - badania rozpoznawcze

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2009

|

nr 4-5

174-176

PL

Otrzymano warstwy konwersyjne z roztworów soli molibdenu Na2MoO4 z dodatkiem cytrynianu sodu jako czynnika kompleksującego. Jako podłoża użyto stali węglowej St3s z elektrolitycznie osadzoną powłoką cynkowo-niklową. Badano wpływ pH oraz temperatury kąpieli na przebieg procesu i właściwości osadzonych powłok. Jako punkt odniesienia dla właściwości powstałych warstw użyto próbek chromianowanych. Badania polaryzacyjne wykazały, że wzrost temperatury kąpieli powoduje zmniejszenie odporności korozyjnej powłok w środowisku 0,5 M NaCl (wzrost prądów korozyjnych, spadek oporu polaryzacyjnego). Najlepsze warstwy zawierające molibden uzyskano w temperaturze 25 i 40°C. Powłoki są jednorodne i pozbawione spękań.

EN

Molybdate conversion layers have been obtained on the Zn-Ni alloy electrogalvanised steel from a solution containing sodium molybdate(VI) and sodium citrate, acidifi ed with phosphoric acid. The layers were deposited at different bath temperatures and different pH values. Chromated samples were used as the reference in order to compare the corrosion resistance properties. The increasing bath's temperature causes decreasing corrosion resistance (bigger corrosion curents, smaller polarization resistance) in 0,5 M NaCl environment. The best molybdate layers were obtained in temperature 25-40°C. These layers are homogeneous and free of cracks.

18

Warstwy molibdenianowe na powłokach stopowych Zn-Ni jako alternatywa warstw chromianowych

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2008

|

nr 4-5

124-126

PL

Na podłożu ze stali węglowej St3s z elektrolityczną powłoką cynkowoniklową otrzymano warstwy konwersyjne z roztworów zawierających molibdenian sodu. Parametrami zmiennymi w procesie osadzania warstw konwersyjnych były: rodzaj kwasu nieorganicznego użytego do zakwaszania kąpieli, pH roztworu, temperatura kąpieli i czas zanurzania. Dla oceny właściwości korozyjnych stosowano porównawczo próbki chromianowane. Wykazano, że wzrost temperatury kąpieli do osadzania warstw molbdenianowych powoduje zmniejszenie odporności korozyjnej powłok w środowisku Na2SO4 (większe prądy korozyjne, mniejszy opór polaryzacji). Najlepsze, jednorodne i pozbawione spękań, warstwy zawierające molibden uzyskano w temperaturze 20°C.

EN

Molybdate conversion layers have been obtained on the Zn-Ni alloy electrogalvanised steel from a solution containing sodium molybdate (VI) acidified with phosphoric acid or nitric acid. The layers were deposited at different bath temperatures and different kind of inorganic acids. Chromated samples were used as the reference in order to compare the corrosion resistance properties. Increasing bath's temperature decreases corrosion resistance (bigger corrosion curents, smaller polarisation resistance) in Na2SO4 environment. The best molybdate layers were obtained in temperature T = 23°C. These layers are homogeneous and free of cracks.

19

Właściwości ochronne powłok antykorozyjnych - porównanie wyników badań terenowych i przyspieszonych

Zubielewicz M., Kamińska-Tarnawska E.

Ochrona przed Korozją

|

2006

|

nr 5

155-159

PL

W 2004 roku przeprowadzono badania laboratoryjne właściwości powłok pigmentowanych fosforanem cynku i modyfi kowanym zasadowym fosforanem cynku, nałożonych na podłoża fosforanowane amorfi cznie i krystalicznieW celach porównawczych przebadano powłoki bez pigmentu antykorozyjnego oraz powłoki nałożone na podłoże niefosforanowane. Badania przyspieszone obejmowały oznaczanie nasiąkliwości, przepuszczalności pary wodnej, adhezji oraz właściwości antykorozyjnych, w komorze solnej i metodą elektrochemicznej spektroskopii impedancyjnej (EIS). W niniejszej publikacji omówiono wyniki 2-letnich badań powłok na stacji terenowej w Gliwicach i porównano je z wynikami badań przyspieszonych w komorze solnej. Stwierdzono dobrą korelację między wynikami uzyskanymi w warunkach naturalnych i przyspieszonych oraz synergicznie oddziaływanie pigmentów fosforanowych z powłoką konwersyjną.

EN

In 2004 laboratory investigations were carried out on the properties of coatings pigmented with zinc phosphate and modified basic zinc phosphate, applied on amorphous and crystalline phosphated steel surfaces. Both coatings without anticorrosive pigments and coatings applied on non-phosphated substrate were tested and compared. The accelerated tests were performed to determine the water absorption, water permeability, adhesion and anti-corrosive properties of the coatings in a salt spray test and EIS. The results of 2 year long studies of the coatings at a fi eld station in Gliwice have been presented in this publication. These results were afterwards compared with the results obtained in the accelerated tests in a salt spray chamber. A good correlation between the obtained results in the natural weathering tests and those in the accelerated tests was observed. Correspondingly, the synergism between the phosphate pigments and the conversion coating was also noted.