Ceramic failure, at stresses lower than those when KIc is reached, might be an effect of subcritical crack propagation. It occurs when the material is in service in the presence of water (even water vapour) for a long time. If this phenomenon leads to limiting its useful life, it is important to predict the lifetime of a ceramic component under specific conditions. Dynamic tests are suitable to determine subcritical crack growth parameters. Calculations are made to determine material behaviour under static loading on the basis of strength data. The paper presents the results for zirconia-alumina composites with 5, 15 and 50 vol.% inclusions to compare materials with different types of microstructures. Pure zirconia sintered bodies were used as the reference material.
PL
Zniszczenie materiałów ceramicznych, przy obciążeniach niższych niż te, gdy osiągane jest KIc, może być efektem pękania podkrytycznego. Ma to miejsce, gdy materiał używany jest w obecności wody (również w postaci pary wodnej) przez długi czas. Jeśli to zjawisko prowadzi do ograniczenia czasu użytkowania, istotne jest, aby przewidzieć czas przeżycia elementu ceramicznego działającego w danych warunkach. Odpowiednie do wyznaczania parametrów pękania podkrytycznego są testy dynamiczne. Obliczenia wykonywane są w celu przewidzenia zachowania materiału pod stałymi obciążeniami na podstawie wyników wytrzymałości. Praca przedstawia wyniki dla kompozytów tlenek cyrkonu-tlenek glinu z 5, 15 oraz 50 obj.% wtrąceń w celu porównania materiałów o różnych typach mikrostruktur. Spieki z czystego dwutlenku cyrkonu zostały zbadane jako materiał odniesienia.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.