Wyniki wyszukiwania - BazTech

1

Dynamic mechanical analysis and thermal analysis of untreated Coccinia indica fiber composites

Balu S., Sampath P. S., Bhuvaneshwaran M., Chandrasekar G., Karthik A., Sagadevan Suresh

Polimery

|

2020

|

T. 65, nr 5

357--362

EN

A natural fiber reinforced polymer matrix composites (FRCs) was prepared by the compression molding method. The natural fiber named Coccinia indica (CI) was employed to fabricate FRCs. The impact of fiber length on storage modulus, loss modulus and loss of weight in the FRCs were determined using dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA). The results revealed that a fiber length of 40 mm shows better storage modulus and nominal loss modulus owing to the higher interfacial bonding between fiber and matrix. In other investigated fiber lengths, the storage modulus is poor and loss modulus is high, which is due to inefficient stress transfer.

PL

Metodą wytłaczania przygotowano próbki kompozytów (FRC) na osnowie polimerowej wzmocnionej włóknami naturalnymi Coccinia indica (CI). Wpływ długości zastosowanych włókien na moduł zachowawczy, moduł stratności i ubytek masy badanych FRC oceniano za pomocą dynamicznej analizy mechanicznej (DMA) i analizy termograwimetrycznej (TGA). Stwierdzono, że kompozyty z udziałem włókien o długości 40 mm wykazują korzystniejszy moduł zachowawczy i nominalny moduł stratności, dzięki lepszemu wiązaniu międzyfazowemu włókna z osnową. W wypadku kompozytów z zawartością włókien o innych długościach moduł zachowawczy jest mały, a moduł stratności duży, co wynika z nieefektywnego przenoszenia naprężeń.

2

Study on the State of Internal Stress and Strain of TATB-based Polymer Bonded Explosive Using Strain Markers and Cone-Beam Computed Tomography

Dai B., Lan L.-G., Zhang W.-B., Tian Y.

Central European Journal of Energetic Materials

|

2017

|

Vol. 14, no. 3

688--707

EN

Precise measurement of the inner structural strain of polymer bonded explosive (PBXs) granules during compression molding is highly desirable in order to investigate the inner stress distribution field and its underlying generation mechanism, with the aim of improving the stress distribution uniformity. In this contribution, TATB-based (1,3,5-triamino-2,4,6-trinitrobenzene) PBX granules were formulated and the stress-strain state of the PBX granules during the warm molding process was analyzed. Strain markers were implanted at different locations and the deformation characteristics and regularity of the embedded spherical strain markers were obtained by X-ray micro-tomography. Thus the local strain states at different locations could be obtained, and the local stress state could be deduced. The results showed that axisymmetric deformation occurred in all of the strain markers, where the flat strain ellipsoids were mainly compressed uni-axially. In the central region, the stress was mainly in an axial direction, and the shear force was small. Not only axial stresses, but also large shear stresses in the surrounding region of the cylindrical grains were present. The stress gradient in the central region was greater than that in the surrounding region. The stress was greater in the surrounding region because this region was squeezed by the mold. The maximum strain degree was 44.8% larger than the minimum strain degree. The local stress increment in each region was quantified. The stress increments of the three axes were in the range 14.2-19.5 MPa. This study examined the feasibility of evaluating the inner stress–strain state of PBX granules in a quantitative manner, which is significant in determining the inner strain and stress distribution in PBX granules during the molding process.

3

Influence of compounding processes and fibre length on the mechanical properties of abaca fibre-polypropylene composites

Bledzki A. K., Faruk O., Mamun A. A.

Polimery

|

2008

|

T. 53, nr 2

120-125

EN

Abaca fibre reinforced polypropylene composites containing 30 wt.% of fibre content have been prepared with different fibre lengths (5, 25 and 40mm), and the structure and mechanical properties have been evaluated. Influence of compounding processes (mixer-injection molding, mixer-compression molding and direct compression molding process) on the structure, tensile, flexural and Charpy impact properties were investigated. It is observed that, with the increasing fibre length (5mm to 40mm), the tensile and flexural properties are showing an increasing tendency but not significantly. Due to the addition of coupling agent, maleated polypropylene (MAH-PP), the tensile and flexural properties increased around 50% of maximum. Among three different processes compared, the mixer-injection molding process showed better mechanical performance (tensile strength is around 90% higher) than the other processes, except notched Charpy impact strength. Compression molding (direct) process showed higher (around 170%) notched Charpy impact strength, in comparison to other processes and with MAH-PP, it was increased 50% nearly. The mixer-injection molding process exhibited significantly higher odour concentration of the composites compared to the other processes.

PL

Przygotowano kompozyty polipropylenu (PP) wzmocnionego włóknami manila (30% mas.) o trzech różnych długościach (5, 25 lub 40mm) stosując trzy sposoby łączenia składników (mieszanie-wtryskiwanie, mieszanie-wytłaczanie, bezpośrednie wytłaczanie). Oceniano także wpływ na strukturę i właściwości kompozytów użycia jako kompatybilizatora kopolimeru bezwodnik maleinowy-polipropylen. Za pomocą skaningowego mikroskopu elektronowego (SEM) badano morfologię otrzymanych kompozytów (rys. 1-3). Wyznaczono także ich właściwości mechaniczne (moduł sprężystości i wytrzymałość na rozciąganie, moduł sprężystości i wytrzymałość na zginanie, udarność Charpy'ego oraz współczynnik tłumienia) badając ich zależność od długości włókien (rys. 4 i 5), sposobu łączenia składników i dodatku kompatybilizatora (rys. 6-9). Stwierdzono, że właściwości mechaniczne przy rozciąganiu i przy zginaniu nieznacznie maleją ze wzrostem długości włókien, rosną natomiast istotnie na skutek zastosowania kompatybilizatora. Spośród trzech badanych metod łączenia składników najlepszą, zapewniającą znaczny wzrost właściwości mechanicznych (z wyjątkiem udarności Charpy'ego), jest mieszanie-wtryskiwanie. Oceniono również za pomocą olfaktometru, że odór zależy od sposobu łączenia składników i jest większy w przypadku próbek otrzymanych metodą mieszanie-wtryskiwanie.

4

Rheological parameters of molding thermoplastic composites high-filled with wood particIes

Stavrov V. P., Spiglazov A. V., Sviridenok A. I.

International Journal of Applied Mechanics and Engineering

|

2007

|

Vol. 12, no 2

527-536

EN

Viscoplastic properties and the friction coefficient of preplasticized composites have been studied at rubbing against a forming surface as a function of filling degree, particIe size, temperature of the melt and lubricant of the forming surface. The composites under study are based on a secondary polypropylene and wood sawdust of various fractions. The pressing force and thickness of the fiat disc-like components were found to be interrelated with the viscoplastic properties of the compositions and conditions at the interface with the forming surface.

5

Recykling elastomerów uretanowych metoda spiekania reaktywnego

Błędzki A. K., Pawlaczyk A., Kardasz D.

Polimery

|

1998

|

T. 43, nr 7-8

479-488

PL

Przedmiotem pracy było określenie możliwości recyklingu elastomerów uretanowych (EUR) metodą spiekania reaktywnego. Zsyntetyzowano cztery serie danych EUR różniące się udziałem segmentów sztywnych w makrocząsteczce (tabela l), zmielono je, a następnie spiekano. Zbadano wpływ budowy chemicznej wyjściowych EUR i warunków spiekania (temp. 210-250°C, czas 90 s lub 210 s) na ciężar właściwy, twardość, udarność, odbojność i właściwości wytrzymałościo-e podczas rozciągania otrzymanych recyklatów. Za optymalne warunki spiekania EUR uznano temp. 230°C i czas 210 s.

EN

Four series of cast urethane elastomers (EUR) were synthesized, differing in the shares of soft segments in the macromolecules (Table 1). The EUR were ground and compression molded. A study was made on the effect of the chemical structure of the starting EUR and compression molding con-ditions (210-250°C, time 90 s or 210 s) on the specific gravity, hardness, impact resistance, resilience and tensile properties on elongation of the re-sulting recyclates. The temperature of 230°C and the time of 210 s were found to be optimum EUR compression molding parameters.