Impact testing of carbon fiber-epoxy resin composite with graphene

Wiśniewski A., Sałacińska A., Wilk J.

Prace Instytutu Lotnictwa

2016

Nr 4 (245)

271--279

The article presents the state of knowledge in the field of dynamic tests with the use of Drop Tower devices of the impact energy of a spherical pivot 18 J. Developed structures of composite samples were presented, with dimensions of 150x100 mm, consist of unidirectional prepreg MTM46/HTS (12K)-150-35% RW and adhesive film with and without addition of graphene plane. The impact strength of these composites panels were investigated according to ASTM D7136/7136M-15 method. Relationship between impact force versus time during impact test was presented. Relationship between deformation and impact energy in the time of the test was also consulted. The type and degree of samples destruction were observed by the microscope. The effect of graphene addition on the properties of carbon fiber-epoxy resin composites were determined.

W artykule przedstawiono stan wiedzy w zakresie badań dynamicznych z zastosowaniem urządzenia Drop Tower o energii uderzenia trzpienia kulistego 18 J. Przedstawiono opracowane konstrukcje wykonanych płyt kompozytowych z użyciem preimpregnatu jednokierunkowego MTM46/HTS(12K)-150-35% RW o wymiarach 150x100 mm z klejem błonkowym i płyt kompozytowych z grafenem na nośniku z kleju błonkowego. Wykonano badania wytrzymałości tych płyt na uderzenie według normy ASTM D7136/7136M-15. Przedstawiono wykresy zależności siły od czasu podczas uderzenia próbek oraz zależności głębokości deformacji i energii uderzenia od czasu w próbie uderzenia. Oceniono sposób i stopień zniszczenia próbek z zastosowaniem mikroskopu. Określono wpływ grafenu na właściwości kompozytu węglowo-epoksydowego.

Compression after impact testing ofcarbon-epoxy resin composites samples with graphene

Wiśniewski A., Sałacińska A.

Prace Instytutu Lotnictwa

2016

Nr 4 (245)

280--286

The article presents compression after impact test of composite samples with graphene. In the presented research, graphene (in the form of a planes of (dimensions) 90x 100 mm on adhesive film as a media agent were applied. Fabricated composite structures made of unidirectional prepreg MTM46/HTS(12K)-150-35%RW with dimensions of 150*100 mm with adhesive films and composite panels with graphene on adhesive films were presented. For samples with and without grapheme, the results of a Compression After Impact (CAI) test with compression speed of 0.005 mm/s were shown. The relationship of force versus displacement for samples with an adhesive film and graphene on an adhesive film were investigated. Studies on residual compressive strength show large differences in compressive strength for samples with graphene and without graphene. It was determined that the obtained differences are due to various locations of destruction. The destruction of the sample was not concentrated at the place of impact, but in the place where the border of the adhesive film flashed. It was found that at the upper edge of the sample partial propagation of destruction caused by the impactor occurred.

W artykule przedstawiono badania wytrzymałości resztkowej kompozytów węglowo-epoksydowych z grafenem. W pracy zastosowano płaszczyzny grafenu o wymiarach 90x 100 mm na kleju błonkowym jako na nośniku. Przedstawiono opracowane konstrukcje wykonanych płyt kompozytowych z użyciem preimpregnatu jednokierunkowego MTM46/HTS(12K)-150-35%RW o wymiarach 150x100 mm z klejem błonkowym i płyt kompozytowych z grafenem na nośniku z kleju błonkowego. Dla próbek z grafenem i bez grafenu pokazano wyniki badań statycznych wytrzymałości resztkowej próbek po uderzeniu CAI (Compression After Impact) o prędkości ściskania próbki 0,005 mm/s. Przedstawiono wykresy zależności siły od przemieszczenia dla próbek z klejem błonkowym i z grafenem na nośniku z kleju błonkowego. Badania resztkowej wytrzymałości na ściskanie wykazały duże rozbieżności wytrzymałości na ściskanie dla próbek z grafenem i bez grafenu. Określono, że otrzymane rozbieżności wynikają z miejsca zniszczenia próbek, a zniszczenie koncentrowało się nie w miejscu uderzenia próbki, ale w miejscu, gdzie przebiegała granica kleju błonkowego. Stwierdzono, że przy górnej krawędzi próbki wystąpiła częściowa propagacja zniszczenia powstałego po uderzeniu bijaka.