Cold Cracking Susceptibility of Joints made of Ferritic-‑Austenitic Duplex Steel 2205 during Underwater Wet Welding

Prokop K., Rogalski G.

Biuletyn Instytutu Spawalnictwa w Gliwicach

2016

Vol. 60, No. 2

35--42

The underwater welding of ferritic-austenitic duplex steels is arousing growing interest inspired by the urgent need for developing welding technologies used for repairing underwater pipelines transporting oil. The tests involved underwater welding using covered electrodes (process 111). The research also involved Tekken technological tests performed under water at a depth of 0.5 m and in air as well as macro and microscopic metallographic tests, ferrite content measurements and hardness measurements of joints. The test results obtained revealed that the underwater welding of duplex steels could lead to cold crack formation. In the case considered above, cold crack susceptibility was attributed to arc burning instability.

Spawanie pod wodą stali ferrytyczno-austenitycznych typu dupleks budzi coraz szersze zainteresowanie. Wynika to z pilnej potrzeby opracowania spawalniczych technologii naprawczych rurociągów do transportu ropy naftowej eksploatowanych pod wodą. Do badań wykorzystano metodę mokrą przy zastosowaniu spawania elektrodami otulonymi (proces 111). Wykonano technologiczne próby Tekken pod wodą na głębokości 0,5 m oraz na powietrzu. Przeprowadzono badania metalograficzne makroskopowe i mikroskopowe, pomiary zawartości ferrytu oraz pomiary twardości złączy. Uzyskane wyniki badań wykazały, że spawanie stali dupleks pod wodą może prowadzić do formowania się pęknięć zimnych. W rozpatrywanym przypadku związane jest to z niestabilnością jarzenia się łuku.