1

Effect of the type of abrasive agent on the properties of cast Co-Cr alloys used in prosthetics

Augustyn-Pieniążek J., Kurtyka P.

Rudy i Metale Nieżelazne Recykling

|

2015

|

R. 60, nr 6

262--268

EN

The study presents the results of abrasion resistance tests carried out on alloys from the cobalt-based family, including Remanium 2001 (CoCrMoW) and Wironit LA (CoCrMo). Tests were performed on the Miller apparatus. The abrasive agent was slurry composed of water and silicon carbide particles of different granulations (SiC > 500 μm and SiC ~45 μm). The study included metallographic examinations, measurements of hardness and weight loss recorded in the tested materials after different times of abrasion amounting to 2, 4, 6, 8, 12 and 16 hours. The surfaces of samples subjected to abrasion were additionally examined by SEM. Alloys were characterized by a dendritic structure typical of cast materials. The results have proved the effect of abrasive particle size on the relative weight loss in Remanium 2001 and Wironit LA alloys. They have also proved that, regardless of the size of abrasive particles, the Wironit LA alloy offers better resistance to abrasion than Remanium 2001. This is due to, among others, the geometric features of the dendrite arms.

PL

W artykule przestawiono wyniki badań odporności na ścieranie stopów z grupy na osnowie kobaltu Remanium 2001 (CoCrMoW) i Wironit LA (CoCrMo), które wykonano na aparacie Millera. Ośrodek ścierający stanowiła zawiesina złożona z wody i węglika krzemu o różniej granulacji (SiC > 500 μm i SiC ~45 μm). W ramach badań wykonano obserwacje metalograficzne, pomiary twardości oraz zarejestrowano ubytki mas badanych materiałów po poszczególnych czasach ścierania tj. 2, 4, 6, 8, 12 i 16 h. Dodatkowo powierzchnie próbek po ścieraniu poddano obserwacji przy wykorzystaniu SEM. Wykazano, że stopy charakteryzowały się strukturą dendrytyczną typową dla materiałów odlewanych. Stwierdzono również istotną rolę wielkości elementów trących na wartości względnych ubytków mas stopu Remanium 2001 oraz Wironit LA. Pokazano również, że stop Wironit, cechuje się większa odpornością na ścieranie od stopu Remanium 2001, niezależnie od wielkości cząstek ścierających. Efekt ten jest związany między innymi z właściwościami geometrycznymi ramion dendrytów.

2

Possibilities of production of the composite coatings reinforced by hard ceramic particles by laser cladding

Bartkowski D., Dudziak B., Piasecki A., Matysiak W.

Journal of Research and Applications in Agricultural Engineering

|

2015

|

Vol. 60, nr 2

17--20

EN

The paper presents research results of metal matrix composite coatings produced on S355 steel using laser cladding. Two powder mixtures Stellite-6/30% B4C and Stellite-6/30% SiC were used. The aim of this study was to determine the applicability of these materials in the production of composite coatings having a microstructure similar to sintered carbides. Applied carbides were characterized by very high hardness (B4C -3800 HV, SiC -2500 HV) and a high melting point (B4C -2763°C, SiO -2730°C).Such parameters are conducive to formation of coatings with composite microstructure. The purpose of analyzed process consisted in complete melting of matrix material, partial melting of reinforcing particles and minimal melting of substrate material. This effect has been achieved to a limited extent.

PL

Przedstawiono wyniki badań kompozytowych warstw powierzchniowych wytwarzanych na stali S355przy użyciu proszkowego napawania laserowego. Zastosowano dwie mieszaniny proszkowe Stellite-6/30%B4C oraz Stellite-6/30%SiC.Celem badań było określenie możliwości zastosowania tego rodzaju materiałów do wytwarzania kompozytowych warstw powierzchniowych o mikrostrukturze zbliżonej do węglików spiekanych. Zastosowane węgliki charakteryzowały się bardzo dużą twardością (B4C -3800 HV, SiC -2500 HV) oraz wysoką temperaturą topnienia (B4C -2763°C, SiC -2730°C). Takie parametry sprzyjają wytworzeniu warstwy o budowie kompozytowej. Celem badanego w pracy procesu było całkowite przetopienie materiału osnowy, częściowe cząstek fazy wzmacniającej oraz minimalne materiału podłoża. Efekt ten został osiągnięty w ograniczonym zakresie.

3

Microstructure and wear resistance of Stellite-6/WC metal matrix composite coatings

Bartkowski D., Kinal G., Dudziak B., Piasecki A., Matysiak W.

Journal of Research and Applications in Agricultural Engineering

|

2015

|

Vol. 60, nr 2

21--25

EN

The paper presents the study results of metal matrix composite coatings formed on S355 and B27 steels by laser cladding with powder technology. Powder mixture consisting of cobalt based alloy and tungsten carbides particles was used. The study consisted of production of the coatings using Trumpf TruDisk laser device equipped with 3-stream nozzle powder feeding system. Composite coatings were produced both on laboratory specimens as well as on agricultural tools. The constant value of feed rate equals 460 mm min-1 and different values of laser beam power (400, 550 and 700 W) have been used. The influence of laser beam power on microstructure, chemical composition and wear resistance on produced coatings have been investigated.

PL

Przedstawiono wyniki badań z kompozytowych warstw powierzchniowych wytwarzanych na stalach S355 i B27 przez napawanie laserowe techniką proszkową. Zastosowano mieszaninę proszkową składającą się z proszku stopu na bazie kobaltu i cząstek węglika wolframu. Badanie polegało na wytworzeniu warstw powierzchniowych przy użyciu urządzenia laserowego Trumpf TruDisk wyposażonego w system trójstrumieniowego podawania proszku. Warstwy powierzchniowe wytwarzano zarówno na próbkach laboratoryjnych jak i na narzędziach rolniczych. Zastosowano stałą wartość posuwu wiązki lasera równą 460 mm min-1 oraz różne wartości mocy wiązki (400, 550 i 700 W). Badano wpływ mocy wiązki lasera na mikrostrukturę, skład chemiczny i odporność na zużycie przez tarcie wytworzonych warstw powierzchniowych.

4

Investigation on Cobalt based alloy modified by Titanium for dental applications

Peter I., Rosso M., Toppi A., Dan I., Ghiban B.

Archives of Materials Science and Engineering

|

2013

|

Vol. 61, nr 2

62--68

EN

Purpose: The main goal of this study is to develop and obtain some competitive products, with high added value. In particular, the attention will be focused on the possibility to obtain a new class of Cobalt based alloy by Ti addition. Design/methodology/approach: Modification of the composition by Ti addition can increase the corrosion resistance, processing and at the same time can improve the alloy biocompatibility. Findings: Addition of these elements has a positive effect on the alloy hardness. Up to 6% of Ti or combining Ti and Zr as alloying elements there are no significant differences as hardness concerns. As corrosion resistance in a simulated oral cavity environment concerns, no significant release of metal ions was observed, the pH value and the weight loss fulfil the conditions required by the Standard ISO 10271/2011. However, the best behaviour was obtained employing CoCrMoTi6 alloy. Research limitations/implications: Based on the up to date achieved outcomes, it appears that a quite homogeneous and good mechanical properties have been obtained modifying the original alloy with 6% of Ti. The future research work will be oriented to get additional and detailed data on the biocompatibility of the alloy. Practical implications: The central issue is the valid transfer to dentistry application. Originality/value: The aim of the paper is to obtain a new class of Co based alloy by the modification of the original chemical composition.

5

Azotowanie kobaltu i jego stopów

Jamrozek J., Konstanty J., Przybyłowicz K.

Rudy i Metale Nieżelazne

|

2004

|

R. 49, nr 1

29-31

PL

Przedstawiono wyniki badań dyfuzyjnych warstw uzyskanych podczas azotowania kobaltu oraz wieloskładnikowego stopu na osnowie kobaltu, w warunkach wyładowania jarzeniowego. Obróbkę prowadzono przez 4 godziny, w temperaturze 520 stopni Celsjusza, w atmosferze N2-33% obj. H2 pod ciśnieniem 3 hPa. Próbki do badań wykonano metodą metalurgii proszków, na drodze prasowania na gorąco proszku Co Extrafine oraz mieszanki proszków Co Extrafine i stopu niklu HMSP 1660-02 (po 50% mas.) Określono wpływ rodzaju materiału poddanego obróbce na strukturę warstwy dyfuzyjnej, jej grubość i mikrotwardość. W pracy wykorzystano stereoskopowy mikroskop Olympus SZ-STU2, z aparatem cyfrowym Camedia C-3030, mikrotwardościomierz Hanemanna oraz dyfraktometr rentgenowski TUR-M62.

EN

Results of the examination of difussive layers obtained by nitriding cobalt and multicomponent cobalt-based alloy in the conditions of glow discharge have been presented. The treatment was conducted for 4 hours at the temperature of 520 degrees centigrade, in the atmosphere of N2-33% vol. H2 under the pressure of 3 hPa. Samples for the examination were made by powder metallurgy methods, by hot pressing of the Co Extrafine powder and of a mixture of powders of Co Extrafine and HSMP 1660-02 nickel alloy (by 50 mass % each). An effect of a type of material subjected to such treatment on a structure of the diffusive layer has been determined as well as its thickness and microhardness. In the examination, Olympus SZ-STU2 stereo microscope fitted with Camedia C-3030 digital camera, Hanemann's microhardness meter, and the TUR-M62 type X-ray difractometer, were used.

6

Wiązanie stopu na bazie kobaltu z materiałem kompozycyjnym na bazie żywic w stomatologii odtwórczej. Badanie in vitro.

Kupka T., Tanasiewicz M., Księżarek S., Malec W., Gibas M.

Rudy i Metale Nieżelazne

|

2002

|

R. 47, nr 9

440-442

PL

Zaprezentowano badania, których celem była ocena in vitro wytrzymałości wiązania w teście na ścianie (SBS) materiału kompozycyjnego na bazie żywic z nowym stopem na bazie kobaltu SI przeznaczonych dla odbudów złożonych w stomatologii zachowawczej z zastosowaniem indywidualnego umocowania wewnątrzkanałowego.

EN

The in vitro study was made aimed to examine shear bound strength (SBS) of a resin-based composite material with a new cobalt-based S1 alloy to be applied for complex restorations in conservative dentistry with a use of individual in-canal anchorage.

7

Badanie efektu Halla w izotropowych i anizotropowych stopach amorficznych na osnowie Co

Kolano R., Jakubczyk E.

Archiwum Nauki o Materiałach

|

1999

|

T. 20, nr 2

113-122

PL

Dla amorficznych stopów Co68Fe4Mo1,5Si13,5B13 i Co71,5Fe2,5Mn2Mo1Si9B13 badano efekt Halla, strukturę domenową oraz właściwości magnetyczne: indukcję magnetyczną nasycenia Bmax, pozostałość magnetyczną Br, koercję Hc i straty magnetyczne Ps. Badania prowadzono dla próbek wygrzewanych w temperaturze poniżej temperatury krystalizacji bez pola magnetycznego i w polu prostopadłym do kierunku odlewania taśmy, tj. dla próbek izotropowych i anizotropowych magnetycznie. Stwierdzono, że wyindukowana anizotropia zmienia strukturę domenową obu stopów oraz istotnie zmniejsza ich pozostałość magnetyczną, koercję i straty magnetyczne, powoduje wzrost rezystywności Halla i zmniejsza wartość indukcji magnetycznej, przy której następuje przejście z zakresu anomalnego do normalnego efektu Halla.

EN

Investigation of the correlation between the Hall effect, the domain structure and such magnetic properties as: saturation induction Bmax, magnetic remanence Br, coercivity Hc, and core losses Ps, were carried out for isotropic and anisotropic amorphous Co68Fe4Mo1,5Si13,5B13 and Co71,5Fe2,5Mn2Mo1Si9B13 alloys. The samples composed from the above alloys were annealed at a temperature below the crystallization temperature without magnetic field and in a magnetic field perpendicular to the ribbon casting direction. The magnetic anisotropy induced by the external transverse field caused changes of the domain structure in both alloys and a significant decrease of magnetic remanence, coercivity and core losses. Moreover, the increase of the Hall resistivity and the decrease of the value of the magnetic induction at a transition from the anomalous to the ordinary. Hall effect occurs was observed for anisotropic ribbons.