Experimental determination of springback characteristics in a three-point bending test of the aluminium alloy sheet with aluminium cladding

Kut Stanisław, Pasowicz Grzegorz, Stachowicz Feliks

Acta Mechanica et Automatica

2024

Vol. 18, no. 2

307--313

The springback phenomenon that occurs during cold forming is the main problem that affects the dimensional accuracy of bent products. This article presents the results of the analysis of the springback phenomenon occurring during a three-point air bending of 0.5 mm, 0.8 mm, 1.0 mm and 2.0 mm thick AW-2024 aluminium alloy sheet, AW-1050A aluminium clad. For sheets with a thickness of 1.0 mm and 2.0 mm, the influence of heat treatment and natural ageing time of sheets on the value of the springback coefficient was also tested. The springback characteristics were determined by defining the dependence of the springback coefficient on the bending deflection of the band. The experimental results obtained indicate a linear dependence of the value of the springback coefficient on the relative deflection w/fg index (w – distance between supports, fg – deflection under load), both in the case of the influence of the sheet thickness and the ageing time of the sheets.

Steel clad plates hydrogen degradation evaluation using ultrasonic defectoscopy method

Szwed M., Lublińska K., Gloc M., Manaj W., Kurzydłowski K. J.

Advances in Manufacturing Science and Technology

2009

Vol. 33, nr 4

51-57

This paper presents results of hydrogen degradation tests of steel clad plates by the ultrasonic defectoscopy. The subject of the tests were samples of low-alloy steel 12CrMo4-5 coated with austenitic steel X2CrNi19-11 using explosive cladding method. The samples were subjected to a thermocycling process within the temperature range from 25 to 450 degrees centigrade in the gaseous hydrogen atmosphere. Detailed microstructural and microanalytical tests of the areas indicated by the ultrasonic defectoscopy were carried out to verify the results of the ultrasonic tests. The structural observations were carried out by light microscopy, scanning electron microscopy (SEM). X-ray microanalysis of chemical composition (EDS) was also performed. The results show that with properly selected measurement settings, the ultrasonic defectoscopy allows to detect early stages of hydrogen degradation in clad plates.

W pracy przedstawiono wyniki badań degradacji wodorowej blach platerowanych metodami defektoskopii ultradźwiękowej. Przedmiotem badań jest blacha ze stali niskostopowej 13CrMo4-5 platerowana metodą wybuchową austenityczną stalą X2CrNi19-11. Wykonano cykliczną obróbkę cieplną w zakresie temperatury od 25 do 450 stopni Celsjusza w atmosferze wodoru. Weryfikację wyników badań ultradźwiękowych dokonano przez obserwację mikrostruktury stali w obszarach wytypowanych za pomocą badań ultradźwiękowych. Stosowano metody mikroskopii świetlnej, elektronowej mikroskopii skaningowej oraz mikroanalizę rentgenowską (EDS). Stwierdzono, że dobór parametrów pomiarowych metodą defektoskopii ultradźwiękowej umożliwia wykrywanie wczesnych etapów degradacji wodorowej mikrostruktury stali blach platerowanych.