Case studies of steel and their welded joint failures caused by liquid metal embrittlement LME

Bernasovský P., Brziak P.

Przegląd Spawalnictwa

2015

R. 87, nr 2

37--40

Liquid metal embrittlement (LME) is a phenomenon, where liquid (molten) metal is mostly intergranulary (but not only) penetrated into solid metal and causes its brit- tle fracture. The LME is usually related to low melting metals (zink, tin, cadmium), which are in the contact with higher molten ones (steels, Ni alloys). Cases of LME as a Cu penetration into pipeline welded joint of 15G2S steel, a hot temperature corrosion in the cement works shell plate made of AISI 310 stainless steel attacted by Ni3S2 (Ts = 644 °C) and a vanadium corrosion in the boiler vessel (10CrMo9-10 steel) due to V2O5 + Na2SO4 eutecticum (~600 °C) are concerned.

Kruchość stali wywołana obecnością cieczy metalicznej (ang. LME – liquid metal embrittlement) zachodzi podczas oddziaływania i w konsekwencji penetrowania granic ziaren (stali oraz stopów Ni) niskotopliwych metalami (cu, Zn, Col Sn), w warunkach działania naprężeń rozciągających. W artykule przeanalizowano przypadki LME wynikające z penetrowania Cu złączy spawanych rurociągów ze stali 15G29 oraz wysokotemperaturowej erozji płyt ze stali 310 wg ALSI wywołanej działaniem Ni3S2 (Ts-644 °C) oraz erozji kotła ze stali 10CrMo9-10 wywołanym oddziaływaniem w wysokiej temperaturze V2O5 + Na2SO4.