Chemical/electrochemical methods for the preparation of graphite multiintercalation compounds

Skowroński J. M., Urbaniak J.

Karbo

|

2005

|

Nr 4

238-243

EN

In this work, the process of the subsequent intercalation of HSO4H2SO4 into CrO3-GIC examined. CrO3GICICs are prepared with two different chemical methods: this is, intercalation from the CrO3/CH3COOH solution according to the Platzcr and de la Martiniere procedure and intercalation of CrO3 from Cr03/HCl solution. Furthermore, the preparation of graphite multiintercalation compound consisted with two different intercalates CrO3 and ZnCl2 from the mixture of graph ite/CrO32 HC1 was performed. The intercalation process of both intercalates CrO3 and ZnCl2 into graphite has been confirmed by cyclic voltammetric technique. Upon the successive intercalation of HSO4/H2S04 the anodic and cathodic effects characteristic for the presence of ZnCl2 and CrO3 have been served in the voltammogram. This suggests the formation of quaternary CrO3/ZnCI2-H2SO4-GIC.

PL

Przedstawiono proces biinterkalacji Hsub>2S04 zachodzący w CrO3IZG. Interkalacja CrO3 w grafit była prowadzona z dwóch mieszanin: grafit/Cr03/HCl oraz grafit/CrO3CH3COOH. Ponadto przeprowadzono próbę jednoczesnej interkalacji dwóch interkalatów CrO3 oraz ZnCl2 celem otrzymania układu multiinterkalacyjnego. Aby stwierdzić czy zaszedł proces interkalacji CrO3 oraz ZnCl2 w grafit, produkt reakcji był badany metodą cyklicznej woltamperometrii w 95 % H2SO4. Na podstawie otrzymanych krzywych woltamperometrycznych stwierdzono obecność obu interkalatów (CrO3 oraz ZnCL2 w matrycy grafitowej. Ponadto, w wyniku anodowego utleniania CrOI3ZnCI2-IZG w 95% H2SO4 otrzymano układ poczwórny CrO3/ZnCl2H2SO4- grafit.

2

Examination of building ceramics with Cr(OH)3 and CrO3 admixtures

Stefanowicz T., Osińska M., Nowak M.

Polish Journal of Applied Chemistry

|

2003

|

Vol. 47, nr 1

23--30

EN

Two series of ceramic test-bricks were prepared - the first with admixtures of 1%, 2%, 3% and 10% of chromium hydroxide Cr(OH)3, and the second - with similar percentage of admixtures of chromium trioxide CrO3. The test-bricks were burned-out in the tunnel stove at a temperature of 960oC and examined for physical and mechanical properties as well as for chromium leaching in distilled water. It was determined that during the burning of ceramics with Cr(OH)3 admixtures, Cr(III) was oxidized to Cr(VI), while during the burning of ceramics with CrO3 admixtures Cr(VI) was not reduced to Cr(III), proving the exclusively oxidizing character of the thermal conversion of chromium in the ceramic firing stove. Leachability of Cr(VI) from ceramics prepared with Cr(OH)3 and particularly CrO3 admixtures greatly exceeded the level permissible by Standards. The admixtures of Cr(OH)3 as well as of CrO3 decreased the compressive strength of ceramics: in the case of Cr(OH)3 when the admixture was greater than 2% and in the case of CrO3 - when the admixture was 1%, with additional loss of freeze resistance. It was proved that the utilization of waste chromium hydroxide and especially of chromium trioxide by admixing any of them to building ceramics should not be accepted.

PL

Przygotowano dwa rodzaje kształtek ceramicznych z domieszkami w jednym przypadku wodorotlenku chromu Cr(OH)3 i w drugim trójtlenku chromu CrO3, w ilościach 1,2,3 i 10%. Po wypaleniu kształtek w piecu tunelowym w temperaturze 960C badano ich cechy fizykochemiczne oraz wymywalność chromu w wodzie destylowanej. Stwierdzono, że na skutek wypalania Cr(III) wprowadzony do ceramiki w postaci Cr(OH)3 uleniał się do Cr(VI) natomiast Cr(VI) wprowadzony do ceramiki w postaci CrO3 nie ulegał redukcji do Cr(III), co wskazuje na wyłącznie utleniający charakter przemiany termicznej chromu w piecu do wypalania ceramiki. Wymywalność Cr(VI) z ceramiki z domieszkami Cr(OH)3, a zwłaszcza z domieszkami CrO3 wielokrotnie przekraczała dopuszczalne normy. Domieszki Cr(OH)3 obniżay wytrzymałość ceramiki na ściskanie powyżej domieszki 2%, a domieszki CrO3 - ju począwszy od domieszki 1%, czemu towarzyszyła utrata mrozoodpornoci. Wykazano, ze utylizacja odpadowego wodorotlenku chromu, a szczególnie trójtlenku chromu przez wprowadzanie ich do ceramiki budowlanej nie powinna by dopuszczona.

3

Exfoliation of CrO3-GIC as a route to novel graphite composites

Skowroński J. M., Walkowiak M.

Karbo

|

2001

|

Nr 11

400-403

EN

Intercalation compound of graphite with chromium trioxide was used as a precursor for obtaining of a novel type of graphite composites. Heating it at temperature of up to 800°C in air resulted in obtaining of composite material of expanded graphite/Cr(2)O(3) type. Whereas further treatment of this composite at the temperature of 1000°C in the stream of hydrogen with argon lead the transformation of Cr(2)O(3) into chromium carbide and origination of a composite of expanded graphite/Cr(3)C(2) type.

PL

Interkalacyjny związek grafitu z trójtlenkiem chromu został użyty jako prekursor w procesie otrzymywania nowego typu kompozytów grafitowych. Ogrzewając go do temperatury 800°C w powietrzu otrzymano materiał kompozytowy typu ekspandowany grafit/Cr(2)O(3), natomiast dalsze ogrzewanie tego kompozytu w temperaturze 1000°C w strumieniu wodoru z argonem spowodowało redukcję Cr(2)O(3) do węglika chromu i powstanie kompozytu typu ekspandowany grafit/Cr(3)C(2).