The influence of chromium compounds on boron carbide sintering

Rutkowski P., Stobierski L., Bućko M.

Composites Theory and Practice

2013

R. 13, nr 4

245--249

The paper concerns the activated sintering of boron carbide based materials. The work shows the influence of introduced Cr3C2, CrSi2, Cr3Si modifiers on the sintering of commercial boron carbide. A high-temperature graphite dilatometer was used in order to investigate boron carbide sintering with various additives. The shift of the onset and endset sintering temperature of different sample compositions was determined. The influence of chromium compounds on sintering was explained by XRD phase analysis. The phase changes in the sinters vs. increasing volume fraction of the additives were made. The same analyses were made on samples heat-treated close to the onset sintering temperature.

Artykuł dotyczy aktywowanego spiekania materiałów na osnowie węglika boru. W pracy przedstawiono wpływ dodatku wprowadzonych modyfikatorów w postaci Cr3C2, CrSi2orazCr3Si na spiekanie komercyjnego węglika boru. Do badań użyto wysokotemperaturowego grafitowego dylatometru w celu prześledzenia przebiegu procesu spiekania węglika boru ze zmienną zwartością różnych dodatków. W ramach badań dylatometrycznych określono przesunięcie temperatury początku i końca spiekania dla różnych przygotowanych składów materiałowych. Wpływ dodatków związków na bazie chromu na spiekanie badanych tworzyw wyjaśniono przy użyciu analizy XRD. Przeprowadzono analizę zmian fazowych spieków w funkcji wzrastającego udziału objętościowego dodatków. Te same badania wykonano również dla wybranych składów wygrzewanych w temperaturach bliskich temperaturze początku spiekania. Przeprowadzono obserwacje mikrostrukturalne SEM.

Mechanical properties of hot-pressed boron carbide materials

Rutkowski P.

Composites Theory and Practice

2013

R. 13, nr 1

33-39

In the paper, a research study is presented that was carried out for the purpose of obtaining composite materials based on a commercial micron boron carbide. A hot pressing process was performed to produce all the necessary materials. Chromium carbides, chromium silicides, and chromium boride were used as sintering activators, and as the phases generating thermal stresses (to improve fracture toughness). Some additives were introduced, their amounts not exceeding 5% of the total volume of the sample. In the case where large amounts of the introduced phases were applied, the sintering temperature was reduced by 120°C as regards the boron carbide sintered with carbon. The phase composition and the structure of the sinters produced were analyzed. The microstructure of polished and chemically etched (in molten salts) samples was investigated using scanning electron microscopy. The elastic properties, hardness, bending strength, and fracture toughness of the products were also determined.

Przeprowadzone w niniejszej pracy badania dotyczą otrzymywania tworzyw kompozytowych na bazie mikronowego komercyjnego węglika boru. Tworzywa otrzymane zostały w procesie prasowania na gorąco. Jako aktywatory spiekania, a zarazem faz generujących naprężenia cieplne w celu podniesienia odporności na kruche pękanie wykorzystano węglik chromu, krzemki chromu oraz borek chromu. Dodatki wprowadzano w ilościach do 5% obj. W przypadku użycia dużych ilości wprowadzonych faz obniżono temperaturę spiekania o 120°C w stosunku do węglika boru spiekanego z dodatkiem węgla. Wytworzone spieki poddano analizie fazowej oraz strukturalnej. Na wypolerowanych i wytrawionych chemicznie (w stopionych solach) próbkach tworzyw dokonano obserwacji mikrostrukturalnych metodą skaningowej mikroskopii elektronowej. Materiał poddano również badaniom w celu wyznaczenia właściwości sprężystych, twardości, wytrzymałości na zginanie oraz odporności na kruche pękanie.