EN
The results of testing the strength properties of experimental ceramic materials containing spending moulding sand after initial mechanical reclamation as a material for subsequent layers of the stucco composition were presented. Tests were carried out on spent moulding sands from various foundry technologies, i.e. sand with furfuryl resin and sand with hydrated sodium silicate. The spent, agglomerated moulding sand has undergone a crushing process. Next, the required granular fractions used for individual layers of the stucco material were separated. Ceramic samples, in which the spent moulding sand was a substitute for fresh silica sand in successive layers of the stucco composition, were prepared. As a reference material, identical ceramic samples were used but with all layers made from the fresh silica sand. Samples prepared in this way were used to determine the bending strength of ceramic materials in the temperature range from 20 to 900ºC. The obtained values of the bending strength have demonstrated that spent moulding sand can be used in investment casting with no adverse effect on the strength of ceramic materials.
PL
W pracy przedstawiono wyniki badań właściwości reologicznych mas lejnych z ZrSiO4, przeznaczonych do wytwarzania ceramicznych form odlewniczych, mających zastosowanie w procesie odlewania precyzyjnego elementów silników lotniczych z nadstopów niklu. Stężenie fazy stałej w ceramicznych masach lejnych wynosiło 75% wag. W celu zmodyfikowania właściwości reologicznych mas lejnych, zastosowano cztery komercyjnie dostępne środki upłynniające: DISPEX N-40, DURAMAX, POLIKOL oraz THS, jako wodne roztwory 10%, których ilość wynosiła 0,25% wagowych w stosunku do proszku. Masy lejne przygotowano w mieszadłach mechanicznych przy szybkości 300 obr./min przez 3 h. Proszek ZrSiO4 scharakteryzowano pod względem wielkości cząstek (metodą dyfrakcji laserowej), morfologii powierzchni (SEM), a także składu chemicznego (XRF). Właściwości reologiczne mas lejnych określono w odniesieniu do lepkości dynamicznej w warunkach laboratoryjnych w temperaturze 21 ºC. Otrzymane wyniki dowodzą, że masa lejna na bazie krzemianu cyrkonu charakteryzuje się zróżnicowaną zdolnością do upłynniania. Mieszanki poddane działaniu środków upłynniających znacząco kontrastują pod względem wielkości lepkości dynamicznej z masą lejną, do której nie dodano upłynniacza. Krzemian cyrkonu wykazuje obiecujące właściwości, stanowiące podstawę do udoskonalania technologii otrzymywania form przeznaczonych do otrzymania części silników lotniczych.
XX
This research concerns properties of ceramic slurries prepared from ZrSiO4 applied for the “prime coat” fabrication in ceramic shell moulds in the investment casting process. The solid phase content was 75% by weight. Modification of the slurry rheological properties was based on addition of four deflocculants such as DISPEX N-40, DURAMAX, POLIKOL and THS as a 10 wt% water solution in an amount of 0.25 wt% with respect to the powder. The ceramic slurries were prepared in a mechanical mixer with a speed equal to 300 RPM within 3 hours. The morphology and chemical properties of ZrSiO4 powder were characterized by SEM and XRF. The powder grain size distribution was determined by laser diffraction. The rheological properties like dynamic viscosity were studied in an air-conditioned lab at 21 °C. The obtained results for the ZrSiO4 based ceramic slurries indicate that the application of deflocculants can decrease or increase dynamic viscosity significantly, when compared to the slurry containing only water).The addition of deflocculants to ZrSiO4 based ceramic slurries is very useful to modify viscosity of them in industrial conditions.
PL
W artykule przedstawiono wyniki badań podstawowych właściwości lejnych mas formierskich na bazie węglika krzemu oraz wodnej zawiesiny spoiwa nanokompozytowego, zawierającego koloidalny tlenek glinu, przeznaczonych do wytwarzania ceramicznych form odlewniczych. W celu zbadania właściwości mas lejnych porównano wpływ rodzaju trzech różnych polimerów pełniących rolę spoiwa modyfikującego, tj. poli(alkohol winylowy) o ciężarze cząsteczkowym 47000 g/mol i stopniu hydrolizy 88%, poli(glikol etylenowy) o ciężarze cząsteczkowym 1500 g/mol, oraz dyspersja poliakrylowa. Zawartość fazy stałej węglika krzemu wynosiła 65% wag. Mieszanki formierskie przygotowywano w klimatyzowanym laboratorium w temperaturze 22 °C przy użyciu mieszadła mechanicznego. Czas eksperymentu wynosił 96 h, przy czym pierwsze badania przeprowadzono po upływie doby, co miało na celu lepszą homogenizacjię mieszaniny. W trakcie trwania doświadczenia co 24 h dokonywano pomiarów lepkości względnej za pomocą kubka Zahna 4#), gęstości, pH oraz adhezji zawiesiny do powierzchni mosiężnej płyty. Dodatkowo scharakteryzowano węglik krzemu pełniący rolę proszku formierskiego. Wykonano obserwacje mikroskopowe (SEM), określenie wielkości cząstek oraz badanie składu chemicznego. Udowodniono, że zastosowanie dodatkowych spoiw modyfikujących znacząco poprawia właściwości technologiczne uzyskanych mas formierskich, co sprzyja ich przyszłościowemu zastosowaniu w odlewnictwie precyzyjnym w skali przemysłowej.
EN
In this work technological properties of ceramic slurries for ceramic shell moulds fabrication were characterized. The slurries were based on silicon carbide powder and nanocomposite binder with colloidal aluminium oxide particles. For modification of rheological properties of the slurries, three binders were added: poly(vinyl alcohol)l with a molecular weight of 47 000 g/mole and 88% of hydrolysis degree, poly(ethylene glycol) with a molecular weight of 1500 g/mole, and a polyacrylic dispersion. The content of silicon carbide solid phase was 65 wt.%. The ceramic slurries were fabricated in an air-condition lab in a reactor equipped with a mechanical mixer. The total time of experiment was 96 h. The first measurement was performed after 24 hours from beginning of the test in order to use the slurries of better homogenization. Relative viscosity by Zahn Cup 5#, density, pH and adhesion were measured every day during the experiment. The silicon carbide powder was additionally characterized for its microstructure (SEM), grain size and chemical composition. It has been proven that the addition of new binders increased the technological properties of the investigated ceramic slurries which was conducive to their future use in the foundry industry.
PL
Węglik krzemu jest używany w wielu dziedzinach nauki i techniki. Charakteryzuje się bardzo dobrymi właściwościami: dużą twardością, odpornością na szoki termicznie czy odpornością na utlenianie. W porównaniu z dotychczas stosowanymi proszkami na formy ceramiczne wykazuję największą przewodność cieplną, co znacząco może skrócić czas uzyskania odlewu, a co za tym idzie zmniejszyć koszty produkcji gotowych części. Głównym celem podjęcia pracy było zastosowanie nowego proszku do wytwarzania form ceramicznych oraz sprawdzenie przydatności nowo opracowanych spoiw i materiałów na formy ceramiczne. W artykule zaprezentowano wyniki badań ceramicznych mas lejnych na bazie węglika krzemu oraz spoiwa, którym był nanokompozyt zawierający koloidalny tlenek glinu. Dodatkowo w celu modyfikacji właściwości technologicznych porównano działanie trzech spoiw dodawanych w ilości 6% masowych w odniesieniu do proszku, którymi były: glikol poli(etylenowy), poli(alkohol winylowy) oraz dyspersja poli(akrylowa). Zawartość fazy stałej proszku SiC wynosiła 65% masowych. Mieszaniny formierskie otrzymywano w reaktorze zaopatrzonym w mieszadło mechaniczne. Czas mieszania wynosił 96 h w temperaturze 21°C. W trakcie trwania eksperymentu dokonywano pomiarów lepkości względnej, pH oraz gęstości. Ponadto co 24 h wykonywano badanie adhezji do powierzchni z użyciem płyty mosiężnej oraz badanie lepkości dynamicznej po zakończeniu prób. W celu scharakteryzowania proszku formierskiego jakim był węglik krzemu wykonano badania za pomocą SEM, pomiary wielkości ziarna oraz badanie składu chemicznego. Udowodniono, iż zastosowanie dodatkowych spoiw wypełniających znacząco poprawia właściwości technologiczne uzyskanych mas formierskich, co sprzyja ich przyszłościowemu zastosowaniu w przemyśle odlewniczym.
EN
Silicon carbide (SiC) is widely used in science and industry. It exhibits advantageous properties like: high strength, hardness and resistance to thermal shocks and oxidation. It is also characterized by thermal resistance and stability. It characterized by very high thermal and electrical conductivity. In comparison with other ceramic powders like: aluminium oxides, zirconium oxides or mullite, SiC exhibits the highest thermal conductivity. Therefore SiC is potentially useful for fabrication ceramic shell moulds in investment casting process. SiC gives possibilities to control macro- and microstructure parameters (like grain size or interdendritic distance) in cast materials, because it exhibit high thermal conductivity. The aim of the study was to investigate the effect of adding three different binders on the technological properties of ceramic slurries used in manufacturing SiC shell moulds for investment casting of aircraft turbine engine parts. In this work technological properties of ceramic slurries based on silicon carbide were characterized. Main binder was substance with nanoparticles of aluminium oxide. Additionally to modify parameters three binders were used: poly(ethylene) glycol, poly(vinyl alcohol) and polyacrylic dispersion. State phase was 65 wt %. The time of mixed ceramic slurries was 96 h in conditioned lab. During the experiment properties such as viscosity, pH and density were investigated. Additionally adhesion to surface test and dynamic viscosity were done. To characterize silicon carbide SEM, grain size and chemical composition were measured. Silicon carbide based ceramic slurries had very promising properties and there are very perspective for future application.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.