Influence of Modified Cationic Starch in a Mixed Poly(Vinyl Alcohol)/Cationic Starch Solution on the Electrospinning Process and Web Structure

Šateikė Jurgita, Milašius Rimvydas

Autex Research Journal

|

2020

|

Vol. 20, no. 1

69--72

EN

Nanofibers were electrospun from bicomponent poly(vinyl alcohol) (PVA) and modified cationic starch (CS) mixed solution PVA/CS with different mass ratios (75/25, 50/50 and 35/65) at a total concentration of 12 wt% for all polymer compositions. For comparison, pure PVA solution was used. Electrospinning technique Nanospider (Elmarco, Czech Republic) with a rotating electrode with tines was used to obtain nanofibrous web. The influence of prepared polymer solution compositions on the structure and morphology of nanofibers and webs were investigated. Analyzing the structure and morphology of the formed nanofiber webs, it was noticed that the fineness nanofibers were formed from the PVA/CS solution with a mass ratio of 50/50. This ratio of solution also lets us to obtain the nanofibrous web with less sticked nanofibers on spunbond. The increase in the CS ratio by more than 50/50 had a negative influence on the diameter of nanofibers and the structure of nanofibrous web.

2

Przemysłowa skrobia kationowa jako flokulant w technologii oczyszczania wody

Ziółkowska D., Shyichuk A., Organiściak A.

Przemysł Chemiczny

|

2013

|

T. 92, nr 10

1914-1917

PL

Skrobia kationowa jest produktem w pełni biodegradowalnym i potencjalnie może zastąpić flokulanty syntetyczne w technologii oczyszczania wody. Zbadano właściwości flokulacyjne ziemniaczanej skrobi kationowej Borcet SZ 2000 (charakteryzującej się stopniem podstawienia 0,18–0,20) w obecności handlowych koagulantów: PIX-123 (siarczan(VI) żelaza(III)) oraz PAX-XL19 (polichlorek glinu). Stwierdzono, że efektywność flokulacyjna skrobi kationowej wyraźnie wzrasta w obecności jonów Fe3+ i Al3+. Dla modelowej zawiesiny kaolinu (4 g/dm3) określono optymalne dawki koagulantów oraz flokulanta wynoszące 0,05% i 0,225% (PIX+Borcet) oraz 0,005% i 0,225% (PAX+Borcet) w stosunku do masy kaolinu. Wykazano, że przedawkowanie koagulantów może prowadzić do obniżenia wydajności procesu sedymentacji zawiesiny.

EN

Cationic starch was added to a kaolin suspension (4 g/L) flocculated with Fe2(SO4)3 and Al polychlorides as com. coagulants. The flocculation effectiveness of the starch increased markedly in presence of Fe3+ and Al3+ ions.

3

Formation of Poly(Vinyl Alcohol)/Cationic Starch Blend Nanofibres via the Electrospinning Technique: The Influence of Different Factors

Sukyte J., Adomaviciute E., Milasius R., Bendoraitiene J., Danilovas P. P.

Fibres & Textiles in Eastern Europe

|

2012

|

Vol. 20, no. 3 (92)

16--20

EN

This paper describes the formation of bicomponent nanofibres from poly(vinyl alcohol) (PVA) and modified cationic starch (CS) mixed solutions (PVA/CS mass ratio 3/1) with different total concentrations of solids in water (8, 10 and 12 wt.%) via the electrospinning technique using two types of rotating electrodes (a plain cylindrical electrode and an electrode with tines). The best results were obtained using a PVA/CS solution with a solid concentration of 8 wt.%. The viscosity of 12 wt.% spinning solution was significantly higher compared to that with a concentration of 8 wt.%. These differences in viscosity had a significant influence on the process of electrospinning, as thinner nanofibres were produced from the less viscous solution. In comparison with the cylindrical electrode, the electrode with tines showed a better performance, where the diameter distribution of nanofibres and the electrospinning process were improved. The purpose of the second part of the experiment was to investigate the influence of different amounts of ethanol in the 8 wt.% PVA/CS solution on the electrospinning process and the properties of nanofibres. The results showed that 3 wt.% of ethanol in the spinning solution influenced the diameter of nanofibres in comparison with 9 wt.% of ethanol (the diameter of nanofibres significantly increased in this case).

PL

Artykuł przedstawia formowanie włókien przy zastosowaniu dwóch rodzajów elektrod - cylindrycznej i żłobkowanej. Najlepsze wyniki uzyskano przy przędzeniu włókien z roztworu 8 wt.%. Różnice w lepkości spowodowane stężeniem odgrywają znaczną rolę przy produkcji nanowłókien, przy czym cieńsze naowłókna otrzymywane są z roztworów o mniejszej lepkości. Stwierdzono, że proces przebiega lepiej i uzyskuje się korzystniejszy rozkład średnic przy zastosowaniu elektrody żłobkowanej. Druga część badań polegała na ocenie wpływu zawartości etanolu na przebieg procesu i właściwości uzyskiwanych włókien. Stwierdzono znaczny wzrost średnicy nanowłókien przy stosowaniu 9 wt% zawartości etanolu w roztworze przędzalniczym w stosunku do roztworu 3 wt.%.

4

Wpływ skrobi na właściwości optyczne i starzenie papierów białych

Wysocka-Robak A.

Przegląd Papierniczy

|

2011

|

R. 67, nr 10

632-634

PL

Celem niniejszej pracy było określenie wpływu zaklejania powierzchniowego papieru roztworem skrobiowym na trwałość jego właściwości optycznych. Papier zaklejany w masie zawierał różne dodatki skrobi kationowej. Badania wykonano dla papierów niepoddanych oraz poddanych procesowi przyspieszonego starzenia. Badania wykazały, że preparaty skrobiowe stosowane do zaklejania papieru zarówno w masie, jak i zaklejania powierzchniowego, powodują zmianę barwy tych papierów w kierunku żółtym i przyczyniają się do większego ich żółknięcia w wyniku starzenia.

EN

The purpose of this study was to determine the effect of paper surface sizing with starch solution on fastness of paper optical properties. Stuff sized paper contained different dosages of cationic starch. The tests were made for samples treated and untreated with accelerated ageing. The tests showed that the starch products used both in stuff and surface sizing changed the colour of those papers towards yellow hues and increased their yellowing as a result of ageing.

5

Flocculation abilities of industrial cationic starches

Ziółkowska D., Shyichuk A.

Polimery

|

2011

|

T. 56, nr 3

244-246

EN

Flocculation abilities of five industrial cationic starches were investigated. The research was performed on suspensions of kaolin, bentonite and natural clay. Time dependence of turbidity was determined using the nephelometric method. It was found that modified cationic starches are quite good flocculants for aluminosilicate suspensions, especially for natural clay. The highest flocculation efficiency showed the potato starch BORCET SZ 2000 characterized with the highest substitution degree.

PL

Określono właściwości flokulacyjne skrobi kationowych różniących się pochodzeniem oraz stopniem podstawienia (tabela 1). Badania przeprowadzono w zawiesinach glinokrzemianów: kaolinu, bentonitu oraz naturalnej gliny. Zmiany zmętnienia w czasie oznaczano metodą nefelometryczną. Stwierdzono, że zmodyfikowane skrobie kationowe mogą pełnić rolę flokulantów przyspieszających sedymentację glinokrzemianów, a w szczególności naturalnej gliny. Klarowanie zawiesiny zachodzi tym efektywniej im większy jest stopień podstawienia skrobi (rys. 1). Najlepszą efektywność zaobserwowano stosując BORCET SZ 2000. W porównaniu z flokulantami syntetycznymi, skrobie kationowe zapewniają nieco mniejszą wydajność procesu (tabela 2), jednak posiadają wiele zalet, takich jak: nietoksyczność, zdolność do biodegradacji oraz niska cena.

6

Flokulacyjna efektywność kationowej skrobi ziemniaczanej w obecności koagulantów

Ziółkowska D., Shyichuk A., Cysewski P., Organiściak A.

Chemik

|

2011

|

Vol. 65, nr 4

309-314

PL

W pracy przedstawiono wyniki badania flokulacyjnych właściwości kationizowanej skrobi ziemniaczanej w obecności koagulantów żelazowego i glinowego. Wydajność sedymentacji modelowych zawiesin kaolinu określano metodą nefelomeryczną. Stwierdzono, że modyfikowana skrobia użyta w kompozycji z koagulantem znacznie wydajniej przyspiesza klarowanie zawiesiny mineralnej, niż flokulant czy koagulant stosowane pojedynczo. Przedawkowanie koagulanta (zarówno żelazowego jak glinowego) prowadzi do obniżenia wydajności flokulacyjnej kationizowanej skrobi.

EN

The work contains experimental data on flocculation abilities of cationized potato starch applied together with ferric and aluminum coagulants. The sedimentation efficiency for model kaolin suspensions has been determined with nephelometric method. It has been stated that modified starch used together with coagulant accelerates much more effectively the clarification of mineral suspension comparing to the flocculant or the coagulant used separately. Meantime, overdosage of the coagulant (both ferric and aluminum one) leads to decrease of flocculation efficiency of cationized starch.

7

Methods of Forming Nanofibres from Bicomponent PVA/Cationic Starch Solution

Adomavičiūtė E., Milašius R., Žemaitaitis A., Bendoraitienė J., Leskovšek M., Demšar A.

Fibres & Textiles in Eastern Europe

|

2009

|

Vol. 17, no. 3 (74)

29--33

EN

In this study nanofibres were manufactured from bicomponent PVA/cationic starch (CS) polymers solutions using the electrospinning method. The effect of the starch derivative solution preparation procedure and weight ratio of bicomponent polymer solution on the morphology of nanofibres was investigated. Three types of polymer solutions were prepared: PVA/CS and PVA/homogenizated (hCS), both in water, and PVA/hCS in a mixture of ethanol/water. It was found that the homogenisation procedure for CS improves the spinability of the bicomponent solution. The use of ethanol in the solution allows to form nanofibres, even from one consisting of 25% hCS. It was estimated that a solution composition of PVA/hCS (85/15w/w) in a mixture of ethanol/water is optimal to produce nanofibers by electrospinning. Analysing the morphology of webs formed, it was estimated that more stick nanofibres were formed from the PVA/hCS solution than from the PVA/CS one. The use of a ethanol/water mixture in PVA/hCS causes the formation of thicker nanofibres.

PL

Przedstawiono wyniki badań oceny aktywności przeciwdrobnoustrojowej (APD) bioaktywnych pneumotermicznych włóknin filtracyjnych (WPTF) stosowanych do produkcji półmasek ochronnych. W badaniach stosowano włókniny PP zawierające w swoim składzie związek biologicznie aktywny jony Ag/AgCl na różnych nośnikach: ZnO, TiO, BaSO4. Zbadano wpływ różnych nośników oraz ładunku elektrycznego na APD włóknin wobec czterech gatunków bakterii i grzybów. WPTF z dodatkiem Ag/AgCl na nośnikach charakteryzowały się wysoką APD wobec bakterii E. coli, S. aureus oraz grzybów C. albicans, A. niger. Stwierdzono, iż APD Ag/AgCl zależy w dużym stopniu od nośnika substancji aktywnej. Zastosowanie jednocześnie dwóch rodzajów nośników TiO oraz ZnO jak również TiO2 oraz BaSO4 znacznie podwyższyło APD włóknin, w porównaniu z włókninami, w których stosowany był jeden nośnik. Stwierdzono również wyższą APD przy obecności ładunku elektrostatycznego na włóknach. Badania mikroskopowe wykazały prawidłowe rozmieszczenie substancji aktywnej na powierzchni oraz tuż pod powierzchnią włókien, a badania filtracji aerozolu mgły olejowej potwierdziły, iż obecność biocydu nie zmienia właściwości filtracyjnych włókniny. Wykazano skuteczność bójczą zarówno wobec bakterii jak i grzybów po 8 godzinach kontaktu z włókniną. Wysokie efekty APD uzyskano po 24 godzinach, co wskazuje iż mechanizm działania srebra na komórki drobnoustrojów jest długotrwały.