The Influence of Lamellar Graphite Cast Iron Annealing on Hardness and Structure

Roučka J., Prochazka J., Kana V., Krutis V., Nedelova K.

Archives of Foundry Engineering

2019

iss. 4

105--112

An analysis has been carried out of the influence of annealing time at the preheating temperature of 650 °C on the change in hardness and alloy structure of lamellar graphite cast iron in the working as well as in the laboratory conditions. This preheat temperature is common during reclaiming welding of castings with complex shapes. The changes in unalloyed cast iron EN-GJL 200 to EN-GJL 300 according to ISO 1690 standard and cast iron with low amount of elements such as Sn, Cu, Cr, and Mo and their combinations were assessed. It was found that the cast iron of higher strength grades has better hardness and structural stability. Cast iron alloyed with chromium or its combinations has the highest stability. In unalloyed cast iron, a partial degradation of pearlite occurs; in alloyed cast iron the structural changes are not conclusive.

Fraktalny opis zmian twardości żeliwa wykazującego na przekroju odlewu gradient udziału składników struktury

Chmiela J., Cybo J., Słota D.

Krzepnięcie Metali i Stopów

1998

nr 36

63--69

W pracy przedstawiono fraktalny opis zmian twardości żeliwa charakteryzującego się złożoną morfologią i gradientem udziału składników osnowy. Wyniki skonfrontowano z krzywą analitycznego opisu zmian HB(R), uzyskując identyczne rozwiązanie.