Rheological investigations of a magnetorheological elastomer

Skalski P.

Zeszyty Naukowe Instytutu Pojazdów / Politechnika Warszawska

2016

z. 5/109

99--108

Magneothrological elastomers due to controlled mechanical parameters in an active magnetic field are interesting for researchers and engineers in applications in the automotive industry. In this paper a magnetorheological elastomer based on the natural rubber matrix with carbonyl iron powder was studied. A material sample was fabricated without applying a magnetic field. Its microstructure was observed using a scanning electron microscope. The rheology of the material was investigated with and without an applied magnetic field using the ARES rheometer. Results of investigations were presented and discussed.

Elastomery magnetoreologiczne ze względu na swoje kontrolowane parametry mechaniczne w obecności pola magnetycznego stają się obiektem zainteresowań badaczy oraz inżynierów do aplikacji w przemyśle samochodowym. Próbka materiału elastomeru magnetoreologicznego została przygotowana bez obecnego pola 108 magnetycznego. Struktura elastomeru została zobrazowana na skaningowym mikroskopie elektronowym. Reologia materiału została przeprowadzona na reometrze ARES z obecnym polu magnetycznym oraz bez pola magnetycznego. Wyniki badań zostały przedstawione i poddane dyskusji. Słowa kluczowe: elastomer magnetoreologiczny, guma naturalna, pył karbonylkowy, reologia, badania.

Magnetomechanical properties of magnetorheological composites

Małecki P., Szewczyk A., Pigłowski J.

Composites Theory and Practice

2013

R. 13, nr 1

47-51

According to Takagi's definition, an intelligent material is able to react to external stimulus by a significant change in its properties in order to make a proper and successful response to the stimulus. The rheological behaviour of magnetorheological composites (MRC) can be controlled continuously, rapidly and reversibly by an applied magnetic field. In this paper, an acrylic copolymer with carbonyl iron powder (CIP) is tested in conditions of mechanical and magnetic stimulations. Chitosan-coated magnetic particles are made in order to change the hydrophilic surface character of CIP to hydrophobic and as a result, obtain better compatibility between the particles and the matrix. The test samples are subjected to cyclic shearing with a constant frequency of 1 Hz. The change in the magnetomechanical properties is expressed by the relative change in hysteresis loop area δW and stress amplitude δ τ. An increasing content of carbonyl iron in the composites and the strength of magnetic field H causes an increase in the hysteresis loops area. Material containing modified particles has a significantly bigger hysteresis loop area than samples filled with unmodified carbonyl iron powder. Based on this knowledge, it can be concluded that this sample can dissipate much more mechanical energy.

Według definicji Takagiego, materiał inteligentny to taki, który jest zdolny do reagowania na bodźce zewnętrzne przez zmianę swych właściwości dla pożądanego i skutecznego odpowiedzenia na te bodźce. Reologiczne właściwości kompozytów magnetoreologicznych mogą być kontrolowane w sposób ciągły, szybki i powtarzalny poprzez zastosowanie zewnętrznego pola magnetycznego. W pracy badano kompozyty kopolimeru akrylowego i proszku żelaza karbonylkowego w warunkach stymulacji mechanicznej i magnetycznej. Przeprowadzono modyfikację powierzchni cząstek magnetycznych w celu zmiany jej charakteru z hydrofilowego na hydrofobowy oraz uzyskaniu lepszej kompatybilności między cząstkami a matrycą. Efekt modyfikacji potwierdza analiza FTIR. Próbki badano w warunkach cyklicznego ścinania ze stałą częstotliwością 1 Hz. Zmianę właściwości magnetomechanicznych wyraża się poprzez zmianę pola pętli histerezy δW i amplitudy naprężenia δ τ . Wraz ze zwiększeniem zawartości żelaza karbonylkowego w kompozycie i natężenia pola magnetycznego następuje zwiększenie pola pętli histerezy. Kompozyty zawierające 31% obj. cząstek magnetycznych modyfikowanych chitozanem wykazują 4-krotnie większą pętle histerezy niż odpowiednia próbka z żelazem bez modyfikacji. W warunkach badania, przy odkształceniu 25 • 10-3 i polu H = 100 kA/m pole pętli wynosi 100 J/m3, gdzie dla próbki z modyfikowanymi cząstkami osiąga wartość 430 J/m3. Oznacza to, że materiał lepiej tłumi drgania, tj. rozprasza energię mechaniczną. Efekt ten związany jest ze wzrostem kompatybilności między cząstkami magnetycznymi a matrycą polimerową.