Carbon modified TiO2 photocatalysts for water purification

Morawski A. W., Janus M., Tryba B., Toyoda M., Tsumura T., Inagaki M.

Polish Journal of Chemical Technology

2009

Vol. 11, nr 2

46-50

Carbon can form different structures with TiO2: carbon-doped TiO2, carbon coated TiO2 and composites of TiO2 and carbon. The presence of carbon layer on the surface of TiO2 as well as the presence of porous carbon in the composites with TiO2 can increase the concentration of organic pollutants on the surface of TiO2, facilitating the contact of the reactive species with the organic molecules. Carbon-doped TiO2 can extend the absorption of the light to the visible region by the narrowing of the band gap and makes the photocatalysts active under visible light irradiation. TiO2 loaded carbon can also work as a photocatalyst, on which the molecules are adsorbed in the pores of carbon and then they undergo the photocatalytic decomposition with UV irradiation. Enhanced photocatalytic activity for the destruction of some organic compounds in water was noticed on the carbon coated TiO2 and TiO2 loaded activated carbon, mostly because of the adsorptive role of carbon. However, in carbon-doped TiO2, the role of carbon is somewhat different, the replacement of carbon atom with Ti or oxygen and formation of oxygen vacancies are responsible for extending its photocatalytic activity towards the visible range.

Photocatalytic activity and surface properties of carbon-doped titanium dioxide

Górska P., Zaleska A., Suska A., Hupka J.

Physicochemical Problems of Mineral Processing

2009

Vol. 43

21-30

Carbon-doped TiO2 was prepared by hydrolysis of titanium (IV) isopropoxide and calcina tion at 350stC for 2h in air. Phenol (0.21 mM) was successfully degraded in the aqueous suspension of the powder, under visible light (λ>400 nm). Characteristics of obtained photocatalyst by BET method and UV-Vis diffuse reflectance spectroscopy showed about 127 m2/g of specific surface area, absorption of light in the visible region and 3.35 eV of band gap energy. Photocatalytic activity and selected properties of five samples prepared independently were investigated.

TiO2 domieszkowany węglem otrzymano poprzez hydrolizę izopropanolanu tytanu(IV) i alcynację w 350st C w atmosferze powietrza przez 2h. Przeprowadzone badania wykazały, Se fenol (0.21 mM) jest efektywnie degradowany w fazie wodnej, w obecności otrzymanego fotokatalizatora oraz światła z zakre su widzialnego (λ>400 nm). Pole powierzchni właściwej otrzymanego C-TiO2 wynosiło około 127 m2/g, fotokatalizator absorbuje światło z zakresu widzialnego a przerwa energetyczna Eg wynosi 3,35 eV. W pracy przebadano aktywność oraz wybrane właściwości dla pięciu niezaleSnie otrzymanych próbek.