Studies into new, environmentally friendly Ag-Cu-Zn-Sn brazing alloys of low silver content

Wierzbicki L. J., Malec W., Stobrawa J., Cwolek B., Juszczyk B.

Archives of Metallurgy and Materials

|

2011

|

Vol. 56, iss. 1

147-158

EN

The paper present selected results of the research conducted for elimination of toxic cadmium from silver based brazing alloys of Ag-Cu-Zn-Cd type. The investigations were conducted with nine new alloys of constant, low silver content (25%) and diversified copper (38.8-46%), zinc (19-32%) and tin (3-10%) contents. Tin was selected as potentially the best cadmium substitute basing on literature review and analysis of equilibrium systems. For examinations and tests a series of ingots in laboratory scale was manufactured, as well as some ingots in pilot scale for the selected, most promising alloys. Complex metallographic examinations of the brazing alloys samples produced in various conditions were made as well as analyses of their phase composition. Also mechanical properties of the samples both in ambient and in elevated temperatures were examined, and physical and technological properties and usability of the alloys were determined. The last stage of the study covered laboratory trials of brazing using the selected alloys. Basing on the results it can be said that there is a possibility to substitute selected cadmium containing silver-based alloys with environmentally friendly alloys of Ag-Cu-Zn-Sn type of relatively low silver content. Low range of melting point was reached, as preliminary assumed. Mechanical properties of the studied alloys strongly depend on temperature, and present limited plasticity in room temperature, while at high temperature (over 500°C) present superplasticity. The examined alloys show good spreadability and the brazing tests confirmed their good reactions both with copper and brass base in a wide temperature range.

PL

W niniejszym artykule przedstawiono wybrane wyniki prac, których celem jest wyeliminowanie toksycznego kadmu ze srebrowych spoiw twardych typu Ag-Cu-Zn-Cd. Badaniami objęto 9 nowych gatunków stopów o stałej, niskiej zawartości srebra (25%) oraz zróżnicowanej zawartości miedzi (38,8-46%), cynku (19-32%) oraz cyny (3-10%). Cyna została wytypowana, na podstawie analizy literaturowej oraz układów równowagowych, jako potencjalnie najlepszy zamiennik kadmu. Wytworzono szereg wlewków w skali laboratoryjnej oraz dla wybranych, najbardziej obiecujących gatunków spoiw, wlewki w skali półtechnicznej przeznaczone do badań i prób. Przeprowadzono kompleksowe badania metalograficzne próbek spoiw wytworzonych w róznych warunkach oraz dokonano analizy skżadu fazowego. Wykonano także badania wżaściwości mechanicznych próbek zarówno w temperaturze otoczenia jak i podwyższonej oraz badania właściwości fizycznych, technologicznych i użytkowych. W ostatnim etapie pracy przeprowadzono laboratoryjne próby lutowanie przy zastosowaniu wybranych spoiw. Uzyskane wyniki badań pozwalają stwierdzić, że możliwe jest zastąpienie wybranych gatunków spoiw srebrowych kadmowych stopami ekologicznymi z grupy Ag-Cu-Zn-Sn o stosunkowo niskiej zawartości srebra. Uzyskano, zakładany we wstępnym etapie prac, niski zakres temperatury topnienia. Właściwości mechaniczne badanych stopów silnie zależą od temperatury, charakteryzują się one ograniczoną plastycznościa w temperaturze pokojowej, by w wysokiej temperaturze (ponad 500°C) wykazywać cechy nadplastyczne. Badane spoiwa charakteryzują się dobrą rozpływnością, a próby lutowania wykazały, że dobrze reagują zarówno z podłożem miedzianym jak i mosiężnych w szerokim zakresie temperatury.

2

Badania podatności do przeróbki plastycznej spoiw twardych z grupy Ag-Cu-Zn-In

Wierzbicki Ł. J., Malec W., Cwolek B., Stobrawa J., Juszczyk B.

Hutnik, Wiadomości Hutnicze

|

2010

|

Vol. 77, nr 8

431-434

PL

W pracy przedstawiono wyniki badań stopów Ag-Cu-Zn-In, zawierających 40 do 50 % Ag, 20 do 40 % Cu, 10 do 25 % Zn i 8 do 10 % In, jako potencjalnych zamienników szeroko zpowszechnionych lutowi kadmowych. Prezentowane wyniki badań obejmują ocenę mikrostruktury oraz właściwości mechanicznych w próbie ściskania w temperaturze otoczenia i podwyższonych, ze szczególnym uwzględnieniem podatności do przeróbki plastycznej.

EN

The paper presents results of testing Ag-Cu-Zn-In alloys containing 40 to 50 % Ag, 20 to 40 % Cu, 10 to 25 % Zn and 8 to 10 % In, as interchangeable for popular cadmium brazing alloys. The study presents estimation of microstructure and mechanical properties in ambient and elevate temperatures in compression test for good plastic workability.

3

Badania mikrostruktury i własności plastycznych spoiwa Ag45Cu27Zn25Sn3

Cwolek B., Ciura L., Malec W., Juszczyk B., Wierzbicki Ł. J.

Hutnik, Wiadomości Hutnicze

|

2010

|

Vol. 77, nr 8

374-377

PL

W pracy przedstawiono wyniki badań niskotemperaturowego spoiwa Ag45Cu27Zn25Sn3 (BAg-36 wg AWS) przeznaczonego do łączenia stali i metali nieżelaznych. Główny nacisk położono na określenie warunków uzyskania możliwie najlepszej podatności do przeróbki plastycznej na gorąco i na zimno. Zaprezentowano wyniki zarówno badań metalograficznych po obróbce cieplnej oraz uzyskane w wyniku sterowania mikrostrukturą zmiany właściwości wytrzymałościowych i plastycznych.

EN

The study presents results of research tests of low-temperature Ag45Cu27Zn25Sn3 brazing alloy (BAG-36 according to AWS) usefull for joining steels and non-ferrous metals. Particular emphasis was placed on determination of conditions ensuring achieving good cold and hot workability. A metallography examination after heat treatment and changes of mechanical properties have been presented.

4

Zastosowanie wyciskania metodą KOBO do produkcji spoiw AgCuTi

Malec W., Marchewka Ł., Księżarek S., Stobrawa J., Ciura L., Cwolek B., Juszczyk B.

Hutnik, Wiadomości Hutnicze

|

2009

|

Vol. 76, nr 8

625-628

PL

Celem badań było sprawdzenie możliwości zastosowania procesu wyciskania metodą KOBO drutów spoiw AgCuTi i określenie wpływu tego procesu na poprawę podatności prasówki do przeróbki plastycznej na zimno. Próby wyciskania drutu ze stopu AgCu35Ti2 wykazały rozdrobnienie mikrostruktury występujące wskutek intensywnego odkształcania, w szczególności iglastych cząstek fazy Cu4Ti. Efektem zastosowania tej metody wyciskania jest uzyskanie drutu o bardzo dobrej podatności do przeróbki plastycznej, lepszej od uzyskiwanej dla prasówki wytwarzanej metodą tradycyjną.

EN

The aim of this work was to check possibility of application of wire extrusion method KOBO in reference to AgCuTi brazing alloys and to investigate an effect of this process on cold workability of an extruded wire. Tests were made with extruding wire from the AgCu35Ti2 alloy showing that severe deformation results in the refinement of microstructure, which applies in particular to needlelike particles of the Cu4Ti phase. Application of the KOBO extrusion method enabled fabrication of wire exhibiting excellent workability, better than that characterizing wires produced by traditional method.

5

Badania plastyczności stopu CuZn34P6

Marchewka Ł., Malec W., Stobrawa J., Juszczyk B.

Hutnik, Wiadomości Hutnicze

|

2009

|

Vol. 76, nr 8

628-631

PL

Stop CuZn34P6 cechuje się właściwościami, które dają szansę na jego zastosowanie do lutowania miedzi i jej stopów w miejsce srebrowych spoiw z dodatkiem szkodliwego kadmu. W artykule przedstawiono wyniki badań tego stopu w zakresie właściwości mechanicznych, mikrostruktury oraz podatności do przeróbki plastycznej wlewków w szerokim zakresie temperatury. Przedstawiono także wyniki badań struktury i właściwości mechanicznych stopu po wyciskaniu na gorąco.

EN

The CuZn34P6 alloy presents properties which provide possibilities for using it as a substitute for silver-based brazing alloys with addition of harmful cadmium for brazing copper and its alloys. The paper presents results of testing this alloy with respect to its mechanical properties, microstructure and plastic workability of the ingots in a wide temperature range. Results of structure and mechanical properties examinations of the alloy after hot extrusion are also presented.

6

Wpływ mikrostruktury stopu AgCu35Ti2 na jego plastyczność

Malec W., Stobrawa J., Księżarek S., Marchewka Ł., Ciura L., Cwolek B.

Hutnik, Wiadomości Hutnicze

|

2008

|

Vol. 75, nr 8

435-438

PL

Jednym z problemów związanych z wytwarzaniem spoiw z grupy AgCuTi jest ich ograniczona podatność do przeróbki plastycznej. W pracy przedstawiono wyniki badań mikrostruktury i właściwości mechanicznych stopu AgCu35Ti2 po odlewaniu w różnych warunkach. Stwierdzono, że iglasta struktura wydzieleń fazy Cu4Ti obecna w materiale po odlewaniu ogranicza podatność do odkształcania zarówno na zimno, jak i na gorąco. Duża szybkość krzepnięcia powoduje istotne zmniejszenie wielkości igieł i poprawę plastyczności.

EN

One of the problems in production ofAgCuTi alloys is their limited plastic workability. The study presents results of investigations into microstructure and mechanical properties ofAgCu35Ti2 alloy after casting in various conditions. The acicular structure ofCu4Ti phase particles in the material after casting limits its workability both in hot and cold conditions. High rate of solidification results in significant reduction of needles size and improvedformability.

7

Podatność do przeróbki plastycznej stopów Ag-Cu-Zn-Sn

Stobrawa J., Marchewka Ł., Ciura L., Malec W., Cwolek B., Juszczyk B.

Hutnik, Wiadomości Hutnicze

|

2008

|

Vol. 75, nr 8

442-445

PL

Cel badań jest związany z pracami prowadzonymi w kierunku eliminacji szkodliwego kadmu ze srebrowych spoiw twardych. W niniejszej pracy przedstawiono wyniki badań metalograficznych, własności mechanicznych oraz składu fazowego wybranych stopów Ag-Cu-Zn-Sn. Określono także podatność tych materiałów do przeróbki plastycznej.

EN

The objective of research is related to the works for elimination of harmful cadmium from silver-based brazing alloys. The study presents results ofmetallographical investigations, mechanical properties and phase composition ofselectedAg-Cu-Zn-Sn alloys. Plastic workability of the material was also examined.

8

Badania wpływu temperatury, prędkości i stopnia odkształcenia na strukturę i własności trudnoodkształcalnych stopów CuPAg

Marchewka Ł., Stobrawa J., Cwolek B., Hadasik E., Płachta A.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 6

343-348

PL

Przedstawiono wyniki badań trudnoodkształcalnego stopu CuP5Agl5 w aspekcie analizy wpływu temperatury, prędkości i stopnia odkształcenia na strukturą i własności tego stopu. Zaprezentowano również wstępne wyniki badań plastometrycznych, przeprowadzonych przy zastosowaniu płastometru skręcającego, w postaci wykresów funkcji naprężenie uplastyczniające-odkształcenie rzeczywiste. Na podstawie wyników badań stwierdzono bardzo małą odkształcalność stopu w zakresie temperatur 20^-150 °C. Odkształcalność stopu rośnie natomiast gwałtownie powyżej 300 °C.

EN

Results of tests hardly deformed CuP5Ag15 alloy, aimed to determine an effect of temperature, and rate and degree of deformation on its structure and properties, have been presented. Moreover, preliminary results of plastometric tests performed using bend plastometer have been included in a form of actual stress-strain diagrams. It was found that the alloy examined was characterised by very low workability within the temperature range of 20÷150 °C, whereas at the temperatures over 300 Celsius degrees it is workability increases rapidly.

9

Technologia wytwarzania stopów szybkoschładzanych oraz półwyrobów - nowy kierunek przemysłu metalurgicznego w Polsce

Kolano R., Kolano-Burian A., Szynowski J., Wójcik N., Polak M.

Rudy i Metale Nieżelazne

|

2006

|

R. 51, nr 3

128-136

PL

W artykule omówiono główne kierunki badań z zakresu technologii wytwarzania stopów szybkoschładzanych oraz perspektywę rozwoju w Polsce produkcji tych stopów. Zaprezentowano opracowane i wykonane w IMN urządzenie do odlewania taśm amorficznych, w którym wykorzystuje się sposób ultraszybkiego schładzania strugi stopu na powierzchni wirującego bębna. Urządzenie składa się z trzech głównych podzespołów: podzespołu bębna odlewniczego, podzespołu do grzania wsadu oraz pulpitu do sterowania procesem odlewania. Urządzenie pozwala jednorazowo odlać ok. 2 kg taśm o grubości 18/50 mum i szerokości ok. 20 mm. Na przykładzie beztopnikowych amorficznych taśm lutowniczych na osnowie Cu i Ni oraz magnetycznie miękkich taśm ze stopów amorficznych na osnowie Fe-Ni oraz Co i Fe omówiono zagadnienia wytwarzania tych taśm, badania ich właściwości, oraz podano przykłady zastosowania taśm szybkoschładzanych w praktyce.

EN

New research directions in the field of technology for fabrication of rapidly-quenched alloys and perspectives of their production in Poland have been outlined. Pilot installation for casting amorphous ribbons by melt spinning method, developed and built at the Institute of Non-Ferrous Metals, has been described. The installation consists of three main sub-assemblies: casting wheel, charge heating unit and a casting process control system. It enables casting of 2 kg ribbons per cycle, 18/50 mum in thickness and about 20 mm wide. Taking as an example the Cu-based and Ni-based brazing alloys, as well as soft amorphous ribbons of the FeNiMoB type and Fe-based and Co-based, the issues related to ribbons fabrication, examination of properties and their application in industrial practice have been described.

10

Rozwój technologii wytwarzania spoiw twardych na osnowie srebra i miedzi w Zakładzie Przetwórstwa Metali INMET Instytutu metali Nieżelaznych

Malec W., Ciura L., Księżarek S., Besztak B., Durst K., Marchewka Ł.

Rudy i Metale Nieżelazne

|

2006

|

R. 51, nr 12

725-730

PL

Przedstawiono zarys rozwoju produkcji spoiw twardych na bazie srebra oraz miedzi w ZPM INMET, zwłaszcza w zakresie aktualnie wytwarzanych gatunków. Omówiono ogólnie zmiany wprowadzone w technologiach ich produkcji w powiązaniu z rozwojem możliwości wytwórczych wyposażenia produkcyjnego ZPM INMET. Zaprezentowano stosowane aktualnie ramowe schematy procesowe wytwarzania wyrobów z tych materiałów w postaci drutów i taśm, w zależności od specyfiki poszczególnych grup gatunków spoiw twardych. W podsumowaniu wskazano kierunki dalszego rozwoju tego segmentu produkcji, który zdaniem autorów powinien być konsekwentnie rozwijany w oparciu o opracowania badawczo-rozwojowe.

EN

Development of the production of silver-based and copper-based brazing alloys at the INMET Metals Processing Plant of the Institute of Non-Ferrous Metals in Gliwice has been outlined with particular account of currently produced assortments. Technology modernisation combined with the increased capabilities of the machines and installations have been described. Technological flowcharts used at present in the production of brazing alloys in a form of wires and strips with an account of the specificity of particular groups of brazing alloys are presented. In the conclusion, directions of further development of this production segment have been indicated emphasizing that this development should be based on the results of the research and development works.

11

Nowoczesne technologie przetwórstwa srebra i jego stopów stosowane w procesie wytwarzania spoiw twardych

Księżarek S.

Elektronika : konstrukcje, technologie, zastosowania

|

2005

|

Vol. 46, nr 9

42-45

PL

Przedstawiono charakterystyczne właściwości fizykochemiczne stopów lutowniczych opartych na srebrze, produkowanych w INMET, firmie działającej przy Instytucie Metali Nieżelaznych w Gliwicach. Przedstawiono procesy lutowania, produkcję stopów, a także główne technologiczne operacje, tj. topienie, rozpylanie proszku, obróbkę na gorąco i na zimno, jak również urządzenia użyte w tych procesach. Zamieszczono rezultaty badań metalograticznych oraz charakterystyczne parametry fizyczne dla wybranych gatunków stopów.

EN

The paper presents characteristic physicochemical properties of silver-based brazing alloys, which are manufactured at Metal Processing Plant INMET of Institute of Non-ferrous Metais. The processes of brazing alloys production are described, including the main technological operations: melting, atomizing of powders, hot and cold working, as well as the equipment used during those processes. Results of metallographic examinations, as well as characteristic physical parameters for selected grades of the alloys are presented.