The Metallographic Characterization of Metal Artifacts Based on Late Medieval Examples

Garbacz-Klempka A., Kwak Z., Perek-Nowak M., Starski M.

Archives of Foundry Engineering

|

2015

|

Vol. 15, iss. 4 spec.

29--34

EN

This work presents the metallographical observations of the chosen copper objects from the Late Middle Ages. Part of these studies is the analysis of metal relics from the Puck area conducted at the Faculty of Foundry, AGH-UST, in collaboration with the University of Warsaw. Medieval European cities were centers of trade and production of metal artifacts. Also in the Puck area, the manufacturing activities can be confirmed based on the metal findings. The aim of this study was to identify and systematize copper alloys used in the Late Medieval Period, on the basis of historic artifacts from Puck. The chemical composition analysis and microstructure observation were carried out. The research is at the first stage of an experiment of reconstructing the medieval alloys in order to study deeper their properties.

2

Analiza możliwości eliminacji ołowiu w odlewniczych stopach miedzi

Ciura L., Cwolek B., Malec W., Marchewka Ł.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 5

254-262

PL

Opierając się na doniesieniach literaturowych dokonano analizy możliwości eliminacji dodatku ołowiu w odlewniczych stopach miedzi przeznaczonych głównie na elementy armatury. Przedstawiono rolę, jaką pełni dodatek ołowiu w stopach odlewniczych oraz przyczyny konieczności ograniczenia lub eliminacji jego zawartości w tych materiałach. Na podstawie publikowanych wyników badań i patentów zaprezentowano możliwe sposoby rozwiązania tego problemu oraz scharakteryzowano opracowane i wprowadzone do praktyki przemysłowej nowe stopy ekologiczne. Przedstawiono pogląd autorów na stan zagadnienia i scenariusz jego rozwoju oraz określono potrzeby i kierunki prowadzenia prac badawczo-rozwojowych w tym obszarze

EN

Based on literature reports an analysis was made of a possibility of lead elimination from the casting copper alloys designed mainly for fittings. The role played by an addition of lead in the casting alloys and the reasons why its content should be reduced or fully eliminated from these materials have been presented. Based on the published results and patents the alternative methods for solving this problem have been described, and new ecological alloys, which have been developed and implemented into industrial practice, have been characterised. The views of the authors on this question and the possible scenarios of its future development are presented. The needs and directions of further R&D works, which should be conducted in this field, have been outlined.

3

Rola wtrąceń siarczkowych w stymulowaniu korozji mosiądzów jednofazowych

Kucharska B., Bala H.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

814-817

PL

Badano odporność korozyjną trzech gatunków mosiądzów jednofazowych do przeróbki plastycznej: CuZn30, CuZn28Sn1 i CuZn20Al2 pochodzące z rur. Stwierdzono, że wtrącenia niemetaliczne najczęściej występujące w tych gatunkach mosiądzów stanowi siarczek cynku choć w mosiądzach CuZn30 i CuZn28Sn1 identyfikowano również wtrącenia fosforkowe. Zidentyfikowane w mosiądzach wtrącenia nie uległy plastycznej deformacji podczas ciągnienia rur. W specjalnie opracowanej modelowej próbie elektrochemicznej wykazano silny wpływ siarkowodoru na lokalną korozję mosiądzu. Założono, że rozwój procesów korozyjnych mosiądzu jest efektem ich symulacji przez siarkowodór - produkt roztwarzania wtrąceń siarczkowych.

EN

Corrosion resistance of three kind of one-phase brasses CuZn30, CuZn28Sn1 and CuZn20Al2 has been studied. The non-metallic inclusions occured in the brasses were identified. It was found that main inclusions in studied brasses are composed of zinc sulphide. Besides, the cooper phosphide occurred in CuZn30 and CuZn28Sn1 brasses. Identified inclusions did not undergo plastic deformation during the tube drawing. A specially invented model electrochemical test allowed to evidence a strong effect of H2S on local corrosion of brass. It was assumed that development of corrosion phenomena of brass was caused by their stimulation by hydrogen sulphide - a product of sulphide inclusions dissolution.